Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 116 MPa | 16800 psi | ISO 527-2 |
PolyOne Nymax™ GMF 604 40 UV Black 28 Polyamide 6 (Nylon 6) The Nymax® GMF 600 Series of compounds are based upon nylon 6 resins and select combinations of glass fiber and mineral reinforcements offering a unique balance of physical property and part perfor.. |
|||
Tensile Strength, Yield | 116 MPa | 16800 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP DFL369XF PC LNP* LUBRICOMP* DFL369XF is a compound based on Polycarbonate resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Internally Lubricated, Flame Retardant. |
|||
Tensile Strength, Yield | 116 MPa @Temperature 22.8 °C |
16800 psi @Temperature 73.0 °F |
ASTM D638 |
Ensinger Sintimid™ V-HPHT high purity high temp Polyimide (PI)
(discontinued **) SINTIMID™ V polyimide stock shapes provide a superior combination of high temperature and bearing and wear, properties that make it an idea choice for the most demanding applications. SINTIMID™ V.. |
|||
Tensile Strength, Yield | 116 MPa | 16800 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Lubricomp LFL36 PEEK LNP* Lubricomp* LFL36 is a compound based on PEEK containing Glass Fiber and PTFE.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength, Yield | 116 MPa | 16800 psi | SABIC - Japan Method |
SABIC Innovative Plastics Valox® PDR4911 PBT (Asia Pacific) This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Tensile Strength, Yield | 116 MPa | 16800 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® V4860HR PBT 30% glass reinforced PBT, UL94 V-0 rated, Hydrolytically stable, Impact Modified. |
|||
Tensile Strength, Yield | 116 MPa | 16800 psi | ASTM D638 |
Techmer ES HiFill® PA6/6 GF/M40 HS L NAT 40% Glass/Mineral Fiber Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 40% Filler by Weight and Mineral Filler, 40% Filler by WeightAdditive: Lubricant and Heat StabilizerFeatures.. |
|||
Tensile Strength, Yield | 116 MPa | 16800 psi | ASTM D638 |
Techmer ES HiFill® PA6/6 GF/M40 HS Up BK 40% Glass/Mineral Fiber Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 40% Filler by Weight and Mineral Filler, 40% Filler by WeightAdditive: Lubricant, UV Stabilizer and Heat Sta.. |
|||
Tensile Strength, Yield | 116 MPa | 16800 psi | ASTM D638 |
Techmer ES HiFill® PA6/6 GF/M40 IG BK 40% Glass/Mineral Fiber Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 40% Filler by Weight and Mineral Filler, 40% Filler by WeightAdditive: Lubricant and Heat StabilizerFeatures.. |
|||
Tensile Strength, Yield | 116 MPa | 16800 psi | ASTM D638 |
Techmer ES HiFill® PA6/6 GF/M40 L BK 40% Glass/Mineral Fiber Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 40% Filler by Weight and Mineral Filler, 40% Filler by WeightAdditive: Lubricant and Heat StabilizerFeatures.. |
|||
Tensile Strength, Yield | 116 MPa | 16800 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP DE004ERP PC LNP* Thermocomp* DE004ERP is a compound based on Polycarbonate resin containing 20% Carbon Fiber. Added features include: Electrically Conductive, Easy Molding, Mold Release. |
|||
Tensile Strength, Yield | 116 MPa | 16800 psi | ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP DE004ERP PC LNP* Thermocomp* DE004ERP is a compound based on Polycarbonate resin containing 20% Carbon Fiber. Added features include: Electrically Conductive, Easy Molding, Mold Release. |
|||
Tensile Strength, Yield | 116 MPa | 16800 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP DE004ERP PC (Asia Pacific) LNP* Thermocomp* DE004ERP is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this material include: Electrically Conductive, Easy Molding, Mold Release. |
|||
Tensile Strength, Yield | 116 MPa | 16800 psi | ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP DE004ERP PC (Asia Pacific) LNP* Thermocomp* DE004ERP is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this material include: Electrically Conductive, Easy Molding, Mold Release. |
|||
Tensile Strength, Yield | 116 MPa | 16800 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP DF006RXQ PC LNP* THERMOCOMP* DF006RXQ is a compound based on Polycarbonate resin containing 30% Glass Fiber. |
|||
Tensile Strength, Yield | 116 MPa | 16800 psi | SABIC - Japan Method |
SABIC Innovative Plastics NORYL HM4025H PPE+PS (Asia Pacific) 40% GF/MF filled FR PPE/PS blend, high flow |
|||
Tensile Strength, Yield | 116 MPa | 16800 psi | Type I, 10 mm/min; SABIC - Japan Method |
SABIC Innovative Plastics NORYL PCN2615 PPE+PS (Asia Pacific) |
|||
Tensile Strength, Yield | 116 MPa | 16800 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® V4860HR PBT (Asia Pacific) 30% glass reinforced PBT, UL94 V-0 rated, Hydrolytically stable, Impact Modified. |
|||
Tensile Strength, Yield | 116 MPa | 16800 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® V4860HR PBT (Europe-Africa-Middle East) 30% glass reinforced PBT, UL94 V-0 rated, Hydrolytically stable, Impact Modified. |
|||
Tensile Strength, Yield | 116 MPa | 16800 psi | ISO 527 |
Polyram PlusTek PA840G13 Nylon 66 for Injection Molding, 13% Glass Fiber Reinforced, Impact Modified, Heat Resistant Impact modified, 13% glass fiber reinforced, heat resistant Nylon 66 for injection molding applications.Information provided by Polyram. |
|||
Tensile Strength, Yield | 116 MPa @Temperature 23.0 °C |
16800 psi @Temperature 73.4 °F |
EN ISO 527 |
Ensinger TECASINT 1011 Polyimide (PI) TECASINT is a range of non-melting high temperature polyimides characterized by high strength over a wide range of temperatures, good long term thermal stability, minimal thermal expansion and excel.. |
|||
Tensile Strength, Yield | 116 MPa @Temperature -40.0 °C |
16800 psi @Temperature -40.0 °F |
ASTM Test |
BASF Ultramid® 8253 HS PA6 (Conditioned) Ultramid 8253 HS is a heat stabilized, impact modified type 6 graft copolymer developed for both injection molding and extrusion applications requiring improved dry as molded toughness and increased.. |
|||
Tensile Strength, Yield | 116 MPa @Temperature -40.0 °C |
16800 psi @Temperature -40.0 °F |
ISO Data |
BASF Ultramid® 8253 HS PA6 (Conditioned) Ultramid 8253 HS is a heat stabilized, impact modified type 6 graft copolymer developed for both injection molding and extrusion applications requiring improved dry as molded toughness and increased.. |
|||
Tensile Strength, Yield | 116 MPa @Temperature -40.0 °C |
16800 psi @Temperature -40.0 °F |
ASTM Test |
BASF Ultramid® 8253 PA6 (Conditioned) Ultramid 8253 is an unfilled, impact modified type 6 graft copolymer developed for both injection molding and extrusion applications. It is also available in heat stabilized (Ultramid 8253 HS) and/o.. |
|||
Tensile Strength, Yield | 116 MPa @Temperature -40.0 °C |
16800 psi @Temperature -40.0 °F |
ISO Data |
BASF Ultramid® 8253 PA6 (Conditioned) Ultramid 8253 is an unfilled, impact modified type 6 graft copolymer developed for both injection molding and extrusion applications. It is also available in heat stabilized (Ultramid 8253 HS) and/o.. |
|||
Tensile Strength, Yield | 116 MPa | 16800 psi | ASTM D638 |
Ashley Polymers Ashlene® P126 PBT Polyester, 30% Glass Reinforced PBT polyester with 30% glass reinforcement.Data provided by the manufacturer |
|||
Tensile Strength, Yield | 116 MPa | 16800 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP DFL28EG PC LNP* Lubricomp* DFL28EG is a compound based on Polycarbonate resin containing 40% Glass Fiber and 10% PTFE. Added features include: Internally Lubricated, Easy Molding. |
|||
Tensile Strength, Yield | 116 MPa | 16800 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP DFL369XF PC (Asia Pacific) LNP* Lubricomp* DFL369XF is a compound based on Polycarbonate resin containing Glass Fiber, PTFE, Flame Retardant. Added features of this material include: Internally Lubricated, Flame Retardant. |