SABIC Innovative Plastics LNP THERMOCOMP DE004ERP PC (Asia Pacific)

Category	Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP THERMOCOMP
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP THERMOCOMP DE004ERP PC (Asia Pacific).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP* Thermocomp* DE004ERP is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this material include: Electrically Conductive, Easy Molding, Mold Release.

Physical Properties	Metric	English	Comments
Density	1.26 g/cc	0.0455 lb/inÂ³	ISO 1183
	1.27 g/cc	0.0459 lb/inÂ³	ASTM D792
Moisture Absorption	0.100 %	0.100 %	50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow	0.0019 cm/cm @Time 86400 sec	0.0019 in/in @Time 24.0 hour	ISO 294
	0.0010 - 0.0030 cm/cm @Time 86400 sec	0.0010 - 0.0030 in/in @Time 24.0 hour	ASTM D955
Linear Mold Shrinkage, Transverse	0.0059 cm/cm @Time 86400 sec	0.0059 in/in @Time 24.0 hour	ISO 294
	0.0050 - 0.0070 cm/cm @Time 86400 sec	0.0050 - 0.0070 in/in @Time 24.0 hour	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	116 MPa	16800 psi	ASTM D638
	116 MPa	16800 psi	ISO 527
Tensile Strength, Yield	116 MPa	16800 psi	ASTM D638
	116 MPa	16800 psi	ISO 527
Elongation at Break	1.9 %	1.9 %	ASTM D638
	2.0 %	2.0 %	ISO 527
Elongation at Yield	1.9 %	1.9 %	ASTM D638
	2.0 %	2.0 %	ISO 527
Tensile Modulus	11.1 GPa	1610 ksi	1 mm/min; ISO 527
	11.72 GPa	1700 ksi	50 mm/min; ASTM D638
Flexural Strength	151 MPa	21900 psi	ASTM D790
	172 MPa	24900 psi	ISO 178
Flexural Modulus	8.96 GPa	1300 ksi	ASTM D790
	9.70 GPa	1410 ksi	ISO 178
Izod Impact, Notched	0.740 J/cm	1.39 ft-lb/in	ASTM D256
Izod Impact, Unnotched	4.53 J/cm	8.49 ft-lb/in	ASTM D4812
Izod Impact, Notched (ISO)	7.00 kJ/mÂ²	3.33 ft-lb/inÂ²	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	28.0 kJ/mÂ²	13.3 ft-lb/inÂ²	80104; ISO 180/1U
Dart Drop, Total Energy	14.0 J	10.3 ft-lb	Instrumented Impact Energy @ peak; ASTM D3763
Impact Test	3.00 J	2.21 ft-lb	Multiaxial Impact; ISO 6603

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	61.0 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	33.9 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ISO 11359-2
	61.2 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	34.0 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
CTE, linear, Transverse to Flow	10.8 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	6.00 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
	11.0 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	6.11 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi)	148 Â°C	298 Â°F	Flatw 80104 sp=64mm; ISO 75/Bf
	147 Â°C @Thickness 3.20 mm	297 Â°F @Thickness 0.126 in	unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	144 Â°C	291 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
	143 Â°C @Thickness 3.20 mm	289 Â°F @Thickness 0.126 in	unannealed; ASTM D648