SABIC Innovative Plastics LNP LUBRICOMP DFL369XF PC

Category	Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP LUBRICOMP
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP LUBRICOMP DFL369XF PC.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP* LUBRICOMP* DFL369XF is a compound based on Polycarbonate resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Internally Lubricated, Flame Retardant.

Physical Properties	Metric	English	Comments
Density	1.60 g/cc	0.0578 lb/in³	ASTM D792
	1.60 g/cc	0.0578 lb/in³	ISO 1183
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm @Time 86400 sec	0.0010 - 0.0030 in/in @Time 24.0 hour	ASTM D955
	0.0021 cm/cm @Time 86400 sec	0.0021 in/in @Time 24.0 hour	ISO 294
Linear Mold Shrinkage, Transverse	0.0030 - 0.0050 cm/cm @Time 86400 sec	0.0030 - 0.0050 in/in @Time 24.0 hour	ASTM D955
	0.0040 cm/cm @Time 86400 sec	0.0040 in/in @Time 24.0 hour	ISO 294

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	112 MPa	16200 psi	ASTM D638
	115 MPa	16700 psi	ISO 527
Tensile Strength, Yield	115 MPa	16700 psi	ISO 527
	116 MPa	16800 psi	ASTM D638
Elongation at Break	2.1 %	2.1 %	ISO 527
	2.3 %	2.3 %	ASTM D638
Elongation at Yield	2.1 %	2.1 %	ISO 527
	2.2 %	2.2 %	ASTM D638
Tensile Modulus	9.93 GPa	1440 ksi	1 mm/min; ISO 527
	10.34 GPa	1500 ksi	50 mm/min; ASTM D638
Flexural Strength	173 MPa	25100 psi	ISO 178
	179 MPa	26000 psi	ASTM D790
Flexural Modulus	8.96 GPa	1300 ksi	ASTM D790
	9.20 GPa	1330 ksi	ISO 178
Izod Impact, Notched	6.62 J/cm	12.4 ft-lb/in	ASTM D256
Izod Impact, Unnotched	1.22 J/cm	2.29 ft-lb/in	ASTM D4812
Izod Impact, Notched (ISO)	11.0 kJ/m²	5.23 ft-lb/in²	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	39.0 kJ/m²	18.6 ft-lb/in²	80104; ISO 180/1U
Dart Drop, Total Energy	19.0 J	14.0 ft-lb	Instrumented Impact Energy @ peak; ASTM D3763
Impact Test	4.00 J	2.95 ft-lb	Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic	0.51	0.51	ASTM D3702 Modified
Coefficient of Friction, Static	0.52	0.52	ASTM D3702 Modified
K (wear) Factor	56.4 x 10^-8 mm³/N-M	28.0 x 10^-10 in³-min/ft-lb-hr	Washer; ASTM D3702 Modified

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	54.0 µm/m-°C @Temperature -40.0 - 40.0 °C	30.0 µin/in-°F @Temperature -40.0 - 104 °F	ASTM E 831
	54.0 µm/m-°C @Temperature -40.0 - 40.0 °C	30.0 µin/in-°F @Temperature -40.0 - 104 °F	ISO 11359-2
CTE, linear, Transverse to Flow	21.6 µm/m-°C @Temperature -40.0 - 40.0 °C	12.0 µin/in-°F @Temperature -40.0 - 104 °F	ASTM E 831
	22.0 µm/m-°C @Temperature -40.0 - 40.0 °C	12.2 µin/in-°F @Temperature -40.0 - 104 °F	ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi)	140 °C	284 °F	Flatw 80104 sp=64mm; ISO 75/Bf
	138 °C @Thickness 3.20 mm	280 °F @Thickness 0.126 in	unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	135 °C	275 °F	Flatw 80104 sp=64mm; ISO 75/Af
	135 °C @Thickness 3.20 mm	275 °F @Thickness 0.126 in	unannealed; ASTM D648

Users viewing this material also viewed the following: