SABIC Innovative Plastics LNP Lubricomp LFL36 PEEK
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Lubricomp LFL36 PEEK.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubricomp* LFL36 is a compound based on PEEK containing Glass Fiber and PTFE.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.63 g/cc | 0.0589 lb/in³ | ASTM D 792 |
| 1.63 g/cc | 0.0589 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 116 MPa | 16800 psi | 5 mm/min; ISO 527 |
| 144 MPa | 20900 psi | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Strength, Yield | 116 MPa | 16800 psi | 5 mm/min; ISO 527 |
| 144 MPa | 20900 psi | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Break | 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D 638 |
| 2.0 % | 2.0 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D 638 |
| 2.0 % | 2.0 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 11.43 GPa | 1658 ksi | 1 mm/min; ISO 527 |
| 12.96 GPa | 1880 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 187 MPa | 27100 psi | ISO 178 |
| 191 MPa | 27700 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Flexural Yield Strength | 193 MPa | 28000 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 9.97 GPa | 1450 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 10.35 GPa | 1501 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.05 J/cm @Temperature 23.0 °C |
1.97 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 6.66 J/cm @Temperature 23.0 °C |
12.5 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Impact Test | 15.0 J @Temperature 23.0 °C |
11.1 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Coefficient of Friction, Dynamic | 0.46 | 0.46 | ASTM D 3702 Modified |
| Coefficient of Friction, Static | 0.59 | 0.59 | ASTM D 3702 Modified |
| K (wear) Factor | 12.1 x 10-8 mm³/N-M | 6.00 x 10-10 in³-min/ft-lb-hr | Ring; ASTM D 3702 Modified |
| 88.6 x 10-8 mm³/N-M | 44.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D 3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 37.8 µm/m-°C @Temperature -30.0 - 30.0 °C |
21.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| CTE, linear, Transverse to Flow | 31.8 µm/m-°C @Temperature -30.0 - 30.0 °C |
17.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 331 °C | 628 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 329 °C @Thickness 3.20 mm |
624 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 296 °C | 565 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 300 °C @Thickness 3.20 mm |
572 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- NanoAmor 95%, OD/ID/L: 20-40/5-10 nm/1-2 um Short Multi-Walled Carbon Nanotubes
- ICO Polymers ICOFLOâ„¢ 510-5055 1200 Micron LDPE Powder
- Lubrizol Advanced Materials PEARLTHANE® 11H94 Thermoplastic Polyurethane Elastomer
- SABIC Innovative Plastics NORYL SE1GFN2 PPE+PS (Asia Pacific)
- Plenco 08235 Polyester BMC, Compression Molded
- A. Schulman SCHULAMID® 66 GF15H 15% Glass Fiber Reinforced, Heat Stabilized Nylon 66
- Hexcel® HexWeb® HDC - 3/16 - 16.0 (R2) Heavy Density Core
- SMAC CABLE® 2519S-20-08 Damping Material
Copyright © lookpolymers.com All Rights Reserved