SABIC Innovative Plastics Valox® V4860HR PBT

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Valox®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Valox® V4860HR PBT.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
30% glass reinforced PBT, UL94 V-0 rated, Hydrolytically stable, Impact Modified.
Physical Properties Metric English Comments
Specific Gravity 1.64 g/cc
1.64 g/cc
ASTM D792
Density 1.64 g/cc
0.0592 lb/in³
ISO 1183
Moisture Absorption 0.0600 %
0.0600 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.19 %
0.19 %
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0070 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.0050 - 0.010 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.010 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 17.8 g/10 min

@Load 5.00 kg,
Temperature 250 °C
 17.8 g/10 min

@Load 11.0 lb,
Temperature 482 °F
 ASTM D1238
Melt Index of Compound 12 g/10 min

@Load 5.00 kg,
Temperature 250 °C
 12 g/10 min

@Load 11.0 lb,
Temperature 482 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 110 MPa
16000 psi
5 mm/min; ISO 527
114 MPa
16500 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 111 MPa
16100 psi
5 mm/min; ISO 527
116 MPa
16800 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 2.2 %
2.2 %
5 mm/min; ISO 527
2.3 %
2.3 %
Type I, 5 mm/min; ASTM D638
2.9 %
2.9 %
Flexural Strain, break, 2 mm/min; ISO 178
Elongation at Yield 2.1 %
2.1 %
5 mm/min; ISO 527
2.3 %
2.3 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 9.44 GPa
1370 ksi
1 mm/min; ISO 527
9.75 GPa
1410 ksi
5 mm/min; ASTM D638
Flexural Strength 182 MPa
26400 psi
2 mm/min; ISO 178
Flexural Yield Strength 174 MPa
25200 psi
1.3 mm/min, 50 mm span; ASTM D790
183 MPa
26500 psi
2 mm/min; ISO 178
Flexural Modulus 6.74 GPa
978 ksi
1.3 mm/min, 50 mm span; ASTM D790
7.87 GPa
1140 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.900 J/cm
1.69 ft-lb/in
ASTM D256
0.740 J/cm

@Temperature -30.0 °C
 1.39 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
Izod Impact, Notched (ISO) 10.0 kJ/m²
4.76 ft-lb/in²
80*10*4; ISO 180/1A
8.00 kJ/m²

@Temperature -30.0 °C
 3.81 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
Charpy Impact, Notched 1.00 J/cm²
4.76 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 13.0 J

@Temperature 23.0 °C
 9.59 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 22.8 µm/m-°C

@Temperature 23.0 - 80.0 °C
 12.7 µin/in-°F

@Temperature 73.4 - 176 °F
 ISO 11359-2
23.5 µm/m-°C

@Temperature -40.0 - 95.0 °C
 13.1 µin/in-°F

@Temperature -40.0 - 203 °F
 ASTM E 831
CTE, linear, Transverse to Flow 114 µm/m-°C

@Temperature -40.0 - 95.0 °C
 63.3 µin/in-°F

@Temperature -40.0 - 203 °F
 ASTM E 831
119 µm/m-°C

@Temperature 23.0 - 80.0 °C
 66.1 µin/in-°F

@Temperature 73.4 - 176 °F
 ISO 11359-2
Hot Ball Pressure Test <= 75.0 °C
<= 167 °F
IEC 60695-10-2
Deflection Temperature at 0.46 MPa (66 psi) 221 °C

@Thickness 6.40 mm
 430 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 188 °C
370 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
197 °C

@Thickness 3.20 mm
 387 °F

@Thickness 0.126 in
 unannealed; ASTM D648
205 °C

@Thickness 6.40 mm
 401 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Vicat Softening Point 175 °C
347 °F
Rate B/120; ISO 306
176 °C
349 °F
Rate B/50; ASTM D1525
176 °C
349 °F
Rate B/50; ISO 306
Flammability, UL94 V-0

@Thickness 0.800 mm
 V-0

@Thickness 0.0315 in
 UL 94 by SABIC-IP