Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 98.0 MPa | 14200 psi | 50 mm/min; ASTM D638 |
Ovation Polymers Nima™ HL 30525 GF FR PET, 25% Glass Fiber PET – Flame Retardant 25% Short Glass Fiber Reinforced. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All samples are prepared according to ASTM s.. |
|||
Tensile Strength, Yield | 98.1 MPa | 14200 psi | 23°C; 50% RH; ASTM D638 |
PTS Lucet® GC-225 25% Glass Reinforced Acetal Copolymer Information provided by US distributor Polymer Technology and Services, LLC (PTS). |
|||
Tensile Strength, Yield | 98.1 MPa @Thickness 3.20 mm |
14200 psi @Thickness 0.126 in |
5mm/min; ASTM D638 |
LG Chemical LUPOY GP2200 PC+GF20%, Heat Resistance Description: Injection Molding, PC+GF20%, General Purpose, Heat ResistanceApplication: IT/OA, E&E Housing and Components, Automotive (Interior)CAS: 103598-77-2 and 65997-17-3Information provided by .. |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | ISO 527-1/-2 |
Lanxess Durethan® DP A 32 901510 Nylon 66 PA 66 standard injection molding grade, non-reinforced, very easy release |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL ZX09022 PPE+PP (Europe-Africa-Middle East) Thermocomp ZX09022 Polyphenylene Oxide (PPO*) + Polypropylene (PP) resin is a 30 % Glass Reinforced, injection moldable grade with a HDT /1.8MPa temperature resistance of 153 deg C and a Tensile mod.. |
|||
Tensile Strength, Yield | 97.9 MPa | 14200 psi | ASTM D638 |
Techmer ES Elastoblend® PA6/6 GF17 IM2 L 17% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 17% Filler by WeightAdditive: Lubricant and Impact ModifierFeatures: Lubricant and Impact ModifiedInformatio.. |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Ultem DT1800E PEI Blend (Asia Pacific) Improved ductility, transparent, standard flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming.This data was supplied by SABIC-IP for the Asia Pacifi.. |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Ultem DT1800E PEI Blend (Europe-Africa-Middle East) Improved ductility, transparent, standard flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming.This data was supplied by SABIC-IP for the Europe-Afri.. |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Ultem DT1810E PEI Blend Improved ductility, transparent, enhanced flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming.This data was supplied by SABIC-IP for the Americas re.. |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Ultem DT1810E PEI Blend (Asia Pacific) Improved ductility, transparent, enhanced flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming.This data was supplied by SABIC-IP for the Asia Pacifi.. |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Ultem DT1810E PEI Blend (Europe-Africa-Middle East) Improved ductility, transparent, enhanced flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming.This data was supplied by SABIC-IP for the Europe-Afri.. |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics ULTEM DT1810EV PEI Blend Improved ductility, transparent, enhanced flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming, UL94 V0 listed. |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics ULTEM DT1810EV PEI Blend (Asia Pacific) Improved ductility, transparent, enhanced flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming, UL94 V0 listed. |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Valox® K4530 PBT (Europe-Africa-Middle East) 15% glass reinforced PBT, Hydrolytically stable, High flow, Automotive connectors. |
|||
Tensile Strength, Yield | 97.9 MPa | 14200 psi | ASTM D638 |
Techmer ES Luriblend® PSU GF20 TL5 20% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 20% Filler by WeightAdditive: PTFE LubricantFeatures: LubricatedInformation provided by TP Composites, Inc. |
|||
Tensile Strength, Yield | 98.1 MPa | 14200 psi | 5 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® EM-8240C MPPE, Glass Filled MPPE/GF material that is used in the main frame of banknote sortersInformation provided by Samsung Cheil Industries. |
|||
Tensile Strength, Yield | 98.1 MPa | 14200 psi | 5 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® EM-8250G MPPE, 20% Glass Filled Information provided by Samsung Cheil Industries. |
|||
Tensile Strength, Yield | 98.1 MPa | 14200 psi | 5 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® TK-4046H PPA, Glass Filled Information provided by Samsung Cheil Industries. |
|||
Tensile Strength, Yield | 98.1 MPa | 14200 psi | ASTM D638 |
Samyang Tribit® 1500G15 Polybutylene Terephthalate, 15% Glass Reinforced Characteristics:G/F reinforcedHeat and Impact resistantApplications:AutomotiveConnectorGearOutdoor handleIgnition systemElectronicConnectorGas valveCoil bobbinSwitch caseRelay caseO/A partsAll infor.. |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP ZX09022 PPE+PP (Europe-Africa-Middle East) Thermocomp ZX09022 Polyphenylene Oxide (PPO*) + Polypropylene (PP) resin is a 30 % Glass Reinforced, injection moldable grade with a HDT /1.8MPa temperature resistance of 153 deg C and a Tensile mod.. |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | SABIC - Japan Method |
SABIC Innovative Plastics NORYL NC220 PPE+HIPS (Asia Pacific) |
|||
Tensile Strength, Yield | 98.1 MPa | 14200 psi | 5 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® TK-6036H PPA, Glass Filled Information provided by Samsung Cheil Industries. |
|||
Tensile Strength, Yield | 97.9 MPa | 14200 psi | ASTM 638 |
PlastxWorld CEVIAN® SKG30 30% GF ABS Glass fiber reinforced, heat resistant and flame retarded ABS.These are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by Plast.. |
|||
Tensile Strength, Yield | 97.9 MPa | 14200 psi | ASTM D638 |
A. Schulman ComAlloy® E-14961 30% Glass Fiber Reinforced Polycarbonate Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength, Yield | 98.1 MPa | 14200 psi | ASTM D638 |
Cheng Yu Plastic NG1100S Nylon 66, 10% Glass Fiber Reinforced |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | ASTM D638 |
E-Polymers Tekaster® F615GM , 40% GF/MF Reinforced PET 40% GF/MF Reinforced, Low warpageInformation provided by E-Polymers Co. Ltd. |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | ISO 527-2 |
Ascend Performance Materials Vydyne® 20NSP Nylon 66, DAM Vydyne® 20NSP is a general-purpose, highly nucleated, lubricated PA66 resin available in natural color. It is designed to crystallize rapidly in order to reduce cycle times and increase productivit.. |
|||
Tensile Strength, Yield | 97.9 - 112 MPa | 14200 - 16200 psi | Average value: 107 MPa Grade Count:3 |
Overview of materials for Polysulfone, 20% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polysulfone, 20% Glass Fiber Reinforced". Specific grades with glass content between 15% and 24% are inc.. |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | ISO 527 |
Victrex® PEEK 381G Medium Viscosity Product Description: High performance thermoplastic material, unreinforced PolyEtherEtherKetone (PEEK), semi crystalline, depth filtered granules for specialty extrusion processes, standard flow, FD.. |
|||
Tensile Strength, Yield | 98.0 MPa @Temperature 23.0 °C |
14200 psi @Temperature 73.4 °F |
ISO 527 |
Victrex® PEEK 450G903 Black Polyetheretherketone, Unreinforced Product Description:High performance thermoplastic material, unreinforced Polyetheretherketone (PEEK), semi crystalline, granules for injection moulding and extrusion, standard flow, FDA food contac.. |