- Lanxess Durethan® DP A 32 901510 Nylon 66
Lanxess Durethan® DP A 32 901510 Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® DP A 32 901510 Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 66 standard injection molding grade, non-reinforced, very easy release
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.133 g/cc | 0.04093 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0080 cm/cm | 0.0080 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0016 cm/cm | 0.0016 in/in | ISO 294-4, 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 47.0 MPa | 6820 psi | Conditioned; ISO 527-1/-2 |
| 98.0 MPa | 14200 psi | ISO 527-1/-2 | |
| Elongation at Yield | 3.6 % | 3.6 % | ISO 527-1/-2 |
| Tensile Modulus | 1.40 GPa | 203 ksi | Conditioned; ISO 527-1/-2 |
| 3.80 GPa | 551 ksi | ISO 527-1/-2 | |
| Charpy Impact Unnotched | 5.50 J/cm² @Temperature 23.0 °C |
26.2 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| 21.3 J/cm² @Temperature 23.0 °C |
101 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 50.0 µm/m-°C | 27.8 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 110 µm/m-°C | 61.1 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 261 °C | 502 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 81.0 °C | 178 °F | ISO 75-1/-2 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Lubricants | |
| Form | Pellets | |
| ISO Shortname | ISO 1874-PA 66,MR, 14-030 | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- Flint Hills P6G2Z-090 Impact Copolymer Polypropylene
- Lucite International Diakon® CLG340 Acrylic Polymer
- Total PPC 3666 Polypropylene, Heterophasic Copolymer, Extrusion
- ExxonMobil 21 Mobil DTE 20 Series
- ExxonMobil Light Mobil DTE Oil Named Series
- CLAL-MSX NICLAFOR® 1000 TD1 Quenched/Cold Rolled, Drawn Copper Alloy
- Azdel SuperLite® SL550700-100 PP Resin Matrix / 55% Glass Fiber (1 mm Molded Thickness)
- Ascend Performance Materials Vydyne® 41H BK03 Nylon 66, Impact Modified, Conditioned
Copyright © lookpolymers.com All Rights Reserved