- Polymer Property : Tensile Strength, Yield = 10900 psi
Polymer Property : Tensile Strength, Yield = 10900 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 75.0 MPa | 10900 psi | ISO METHOD 527 |
| NYCOA 2237 Copolymer Nylon 6/66 Alloy transparent molding and extrusion gradeInformation provided by NYCOA, Inc. |
|||
| Tensile Strength, Yield | 75.0 MPa | 10900 psi | 50 mm/min; ASTM D638 |
| Ovation Polymers Nemcon™ H PK DP110/X5 Polyetheretherketone Thermally Conductive Polyetheretherketone, excellent chemical, high stiffness, modulus and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All sa.. |
|||
| Tensile Strength, Yield | 75.0 MPa | 10900 psi | 50 mm/min; ISO 527-1,2 |
| Qualchem Danamid FEH Polyamide 6 Heat stabilized type polyamide, for long-lasting use at 120-130°CInformation provided by Qualchem Zrt. |
|||
| Tensile Strength, Yield | 75.0 MPa | 10900 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® ML7686 PC (Europe-Africa-Middle East) Transparent Polycarbonate in limited colors. Excellent processability, super high flow. UL rated V-2 at 1.5mm. |
|||
| Tensile Strength, Yield | 75.0 MPa @Strain 0.200 %, Temperature 1090 °C |
10900 psi @Strain 0.200 %, Temperature 2000 °F |
|
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, 1.6 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| Tensile Strength, Yield | 75.0 MPa | 10900 psi | ISO 527-1/-2 |
| Lanxess Durethan® B 35 FA 000000 Nylon 6, Film Grade PA 6, film , medium viscosity, lubricated, not nucleated, in compliance with FDA for food contact and acc. the German BgVV Recommendation XLIV, Section VI.A" Synthetic casings in polyamide"Applicati.. |
|||
| Tensile Strength, Yield | 75.0 MPa | 10900 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics NORYL V02570 PPE+HIPS Noryl* V02570 is a 25% milled fiber reinforced, injection moldable grade. Designed for good dimensional stability and low warpage, this resin also uses non-chlorinated, non-brominated FR additives t.. |
|||
| Tensile Strength, Yield | 75.0 MPa | 10900 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics NORYL V02570 PPE+HIPS (Asia Pacific) Noryl* V02570 is a 25% milled fiber reinforced, injection moldable grade. Designed for good dimensional stability and low warpage, this resin also uses non-chlorinated, non-brominated FR additives t.. |
|||
| Tensile Strength, Yield | 75.0 MPa | 10900 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics NORYL HH180 PPE+PS (Europe-Africa-Middle East) Noryl* HH180 is a high heat, unfilled modified polyphenylene ether resin with a Vicat B/120 temperature of 185 deg C. Noryl HH180 is only available in color 80365. |
|||
| Tensile Strength, Yield | 75.0 MPa | 10900 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP Thermocomp RB003 PA 66 (Europe-Africa-Middle East) 15% glass beads filled polyamide 66 injection moulding resinThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
| Tensile Strength, Yield | 75.0 MPa | 10900 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics NORYL N1250 PPE+HIPS (Asia Pacific) Noryl* N1250 is an unfilled, injection moldable modified polyphenylene ether resin. Designed for good dimensional stability and good flow , this resin also uses non-chlorinated, non-brominated FR ad.. |
|||
| Tensile Strength, Yield | 75.2 MPa | 10900 psi | ASTM D638 |
| PlastxWorld Veroplas PA5300 Nylon 6 general purpose, 30% mineral filled injection molding gradeInformation provided by PlastxWorld Inc. |
|||
| Tensile Strength, Yield | 75.0 MPa | 10900 psi | ISO 527 |
| Polyram RamTal PMH2022 Polyacetal Homopolymer for Injection Molding General purpose polyacetal homopolymer for injection molding applications, MFI 22.Information provided by Polyram. |
|||
| Tensile Strength, Yield | 75.0 MPa | 10900 psi | ASTM D638 |
| Covestro Bayblend® T 88-4N Polycarbonate/ABS Blend, 20% Glass Fiber Contains 20% glass fiber reinforcement, high stiffness.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – .. |
|||
| Tensile Strength, Yield | 75.0 MPa | 10900 psi | 50 mm/min; ISO 527-1,-2 |
| Covestro Makrolon® FR 7087 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Flame retardant• Med.. |
|||
| Tensile Strength, Yield | 75.0 MPa | 10900 psi | conditioned; ISO 527-1/-2 |
| EMS-Grivory Grivory® XE 4028 nat PA12/MACMI Product description: Grilamid XE 4028 natural is a transparent thermoplastic polyamides based on aliphatic, cycloaliphatic and aromatic blocks. Grilamid XE 4028 natural offers a variety of interesti.. |
|||
| Tensile Strength, Yield | 75.0 MPa | 10900 psi | ISO 527-1/-2 |
| DuPont Performance Polymers Delrin® PC691 NC010 Acetal (POM)
(Unverified Data**) Nucleated Low Viscosity Acetal Homopolymer Developed for the Healthcare Industry Delrin SC690 is a low viscosity acetal homopolymer developed for parts requiring high precision molding in the health.. |
|||
| Tensile Strength, Yield | 75.0 MPa | 10900 psi | dry; ISO 527-1/-2 |
| EMS-Grivory Grivory® TR 55 PA12/MACMI Product description: Grilamid TR 55 natural is a high purity transparent thermoplastic polyamide, based on aliphatic and cycloaliphatic monomers. Grilamid TR 55 natural offers outstanding properties.. |
|||
| Tensile Strength, Yield | 75.0 MPa | 10900 psi | ASTM D638 |
| E-Polymers TEKAMID® TB120L Lubricated PA6, DAM LubricatedInformation provided by E-Polymers Co. Ltd. |
|||
| Tensile Strength, Yield | 75.0 MPa | 10900 psi | 50 mm/min; ISO 527-2 |
| BASF Ultradur® S 4090 G2 10% Glass Filled PBT Description: Is a PBT + ASA, easy-flowing injection-molding grades with 10% glass fibers; for rigid, tough and dimensionally stable technical parts e. g. housings, consoles, contact carriers, covers.. |
|||
| Tensile Strength, Yield | 75.0 MPa | 10900 psi | ISO 527-2 |
| Ascend Performance Materials Vydyne® ECO315 BK06 Nylon 66/6, Flame Retardant, DAM Vydyne® ECO315 BK06 is a non-halogenated, unfilled, flame-retardant PA66/6 copolymer with excellent toughness and ductility. It is lubricated for machine feed and easy mold release and has Underwri.. |
|||
| Tensile Strength, Yield | 75.0 MPa | 10900 psi | |
| BASF Luranyl® KR 2460/3 Polyphenylene Ether + Styrene-Butadiene Blend Flame retardant grade with very high heat resistance; used for precision parts and where the material must withstand high injection temperatures (e.g. heater-fan impellers).Data was collected by ISO.. |
|||
| Tensile Strength, Yield | 75.0 MPa | 10900 psi | 50mm/min; ISO 527 |
| BASF Ultramid® C3U PA66/6 (Dry) Ultramid C3U is an injection molding, general purpose PA66/6 grade with improved flame retardance. |
|||
| Tensile Strength, Yield | 75.0 MPa @Temperature 60.0 °C |
10900 psi @Temperature 140 °F |
|
| BASF Ultrason E 3010 PES Ultrason E 3010 is an unfilled, higher viscosity injection molding and extrusion PES grade, tougher and with improved chemical resistance. |
|||
| Tensile Strength, Yield | 75.0 MPa @Temperature 20.0 °C |
10900 psi @Temperature 68.0 °F |
|
| BASF Ultrason S 3010 PSU Ultrason S 3010 is an unreinforced, higher viscosity injection molding and extrusion PSU grade, tougher and with improved chemical resistance. It conforms to FDA requirements of 21 CFR 177.1655. |
|||
| Tensile Strength, Yield | 75.0 MPa | 10900 psi | |
| Radici Radilon® A 35E 990 (dry) Nylon 66 Radilon® A is a range of polyamide 66 (PA66) products obtained through the polymerization of hexamethylendiamine and adipic acid, and used for injection, extrusion and blow-molding.Information prov.. |
|||
| Tensile Strength, Yield | 75.0 MPa | 10900 psi | |
| Radici Radilon® S 38F (dry) Nylon 6 Radilon® S is a range of polyamide 6 (PA6) products obtained through the polymerization of caprolactam and used for injection, extrusion and blow-molding.Information provided by Radici group. |
|||
| Tensile Strength, Yield | 75.0 - 175 MPa | 10900 - 25400 psi | Average value: 117 MPa Grade Count:25 |
| Overview of materials for PBT + PET Blend, Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "PBT + PET Blend, Glass Filled". Each property range of values reported is minimum and maximum values of .. |
|||
| Tensile Strength, Yield | 75.0 MPa | 10900 psi | ISO 527-2 |
| Tisan TISAKRIL® 30% Glass Fiber Reinforced ABS TISAKRIL has a wide area of application in automotive, electronics, computer, construction, and furniture industries. General Specifications include: High surface luminosityEasy processabilityDimens.. |
|||
| Tensile Strength, Yield | 75.0 MPa | 10900 psi | ISO 527 |
| Polyram RamTough PZ304G2 Polycarbonate, 10% Glass Fiber 10% glass fiber reinforced polycarbonate for injection molding applications.Information provided by Polyram. |
|||