Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

BASF Ultrason E 3010 PES

Category Polymer , Thermoplastic , Polyethersulfone (PES)
Manufacturer BASF
Trade Name Ultrason E
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultrason E 3010 PES.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultrason E 3010 is an unfilled, higher viscosity injection molding and extrusion PES grade, tougher and with improved chemical resistance.
Physical Properties Metric English Comments
Density 1.37 g/cc
0.0495 lb/in³
ISO 1183
Water Absorption 2.2 %
2.2 %
ISO 62
Moisture Absorption at Equilibrium 0.80 %
0.80 %
23°C/50% R.H.; ISO 62
Viscosity Test 66 cm³/g
66 cm³/g
Viscosity number
Linear Mold Shrinkage, Flow 0.0085 cm/cm
0.0085 in/in
ISO Data
Linear Mold Shrinkage, Transverse 0.0090 cm/cm
0.0090 in/in
ISO Data
Melt Flow 35 g/10 min

@Load 10.0 kg,
Temperature 360 °C
 35 g/10 min

@Load 22.0 lb,
Temperature 680 °F
 ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 154 MPa
22300 psi
ISO 2039-1
Tensile Strength at Break 90.0 MPa
13100 psi
5mm/min; ISO 527-2
Tensile Stress 23.0 MPa

@Strain 1.00 %,
Temperature 160 °C
 3340 psi

@Strain 1.00 %,
Temperature 320 °F
 ISO 527
25.0 MPa

@Strain 1.00 %,
Temperature 23.0 °C
 3630 psi

@Strain 1.00 %,
Temperature 73.4 °F
 ISO 527
41.0 MPa

@Strain 2.00 %,
Temperature 160 °C
 5950 psi

@Strain 2.00 %,
Temperature 320 °F
 ISO 527
42.0 MPa

@Strain 2.00 %,
Temperature 23.0 °C
 6090 psi

@Strain 2.00 %,
Temperature 73.4 °F
 ISO 527
50.0 MPa

@Strain 3.00 %,
Temperature 160 °C
 7250 psi

@Strain 3.00 %,
Temperature 320 °F
 ISO 527
73.0 MPa

@Strain 4.00 %,
Temperature 23.0 °C
 10600 psi

@Strain 4.00 %,
Temperature 73.4 °F
 ISO 527
90.0 MPa

@Strain 6.00 %,
Temperature 23.0 °C
 13100 psi

@Strain 6.00 %,
Temperature 73.4 °F
 ISO 527
Tensile Strength, Yield 90.0 MPa
13100 psi
50mm/min; ISO 527-2
50.0 MPa

@Temperature 140 °C
 7250 psi

@Temperature 284 °F
65.0 MPa

@Temperature 100 °C
 9430 psi

@Temperature 212 °F
75.0 MPa

@Temperature 60.0 °C
 10900 psi

@Temperature 140 °F
85.0 MPa

@Temperature 20.0 °C
 12300 psi

@Temperature 68.0 °F
Elongation at Break 6.7 %
6.7 %
5mm/min; ISO 527-2
Elongation at Yield 6.7 %
6.7 %
50mm/min; ISO 527-2
0.40 %

@Time 3600 sec,
Pressure 10.0 MPa
 0.40 %

@Time 1.00 hour,
Pressure 1450 psi
 140°C; ISO 899
0.50 %

@Pressure 10.0 MPa,
Time 360000 sec
 0.50 %

@Pressure 1450 psi,
Time 100 hour
 140°C; ISO 899
0.50 %

@Time 3600 sec,
Pressure 10.0 MPa
 0.50 %

@Time 1.00 hour,
Pressure 1450 psi
 ISO 899
0.50 %

@Time 3600 sec,
Pressure 10.0 MPa
 0.50 %

@Time 1.00 hour,
Pressure 1450 psi
 ISO 899
0.55 %

@Pressure 10.0 MPa,
Time 360000 sec
 0.55 %

@Pressure 1450 psi,
Time 100 hour
 ISO 899
0.55 %

@Pressure 10.0 MPa,
Time 360000 sec
 0.55 %

@Pressure 1450 psi,
Time 100 hour
 ISO 899
0.60 %

@Pressure 10.0 MPa,
Time 3.60e+7 sec
 0.60 %

@Pressure 1450 psi,
Time 10000 hour
 ISO 899
0.60 %

@Time 3600 sec,
Pressure 15.0 MPa
 0.60 %

@Time 1.00 hour,
Pressure 2180 psi
 140°C; ISO 899
0.60 %

@Pressure 10.0 MPa,
Time 3.60e+6 sec
 0.60 %

@Pressure 1450 psi,
Time 1000 hour
 140°C; ISO 899
0.60 %

@Pressure 10.0 MPa,
Time 3.60e+7 sec
 0.60 %

@Pressure 1450 psi,
Time 10000 hour
 ISO 899
0.70 %

@Pressure 1.52 MPa,
Time 360000 sec
 0.70 %

@Pressure 220 psi,
Time 100 hour
 140°C; ISO 899
0.80 %

@Time 3600 sec,
Pressure 20.0 MPa
 0.80 %

@Time 1.00 hour,
Pressure 2900 psi
 140°C; ISO 899
0.90 %

@Time 3600 sec,
Pressure 20.0 MPa
 0.90 %

@Time 1.00 hour,
Pressure 2900 psi
 ISO 899
0.90 %

@Time 3600 sec,
Pressure 20.0 MPa
 0.90 %

@Time 1.00 hour,
Pressure 2900 psi
 ISO 899
1.0 %

@Pressure 20.0 MPa,
Time 360000 sec
 1.0 %

@Pressure 2900 psi,
Time 100 hour
 ISO 899
1.0 %

@Pressure 20.0 MPa,
Time 360000 sec
 1.0 %

@Pressure 2900 psi,
Time 100 hour
 ISO 899
1.0 %

@Pressure 15.0 MPa,
Time 360000 sec
 1.0 %

@Pressure 2180 psi,
Time 100 hour
 140°C; ISO 899
1.1 %

@Pressure 20.0 MPa,
Time 360000 sec
 1.1 %

@Pressure 2900 psi,
Time 100 hour
 140°C; ISO 899
1.1 %

@Time 3600 sec,
Pressure 25.0 MPa
 1.1 %

@Time 1.00 hour,
Pressure 3630 psi
 140°C; ISO 899
1.2 %

@Pressure 20.0 MPa,
Time 3.60e+7 sec
 1.2 %

@Pressure 2900 psi,
Time 10000 hour
 ISO 899
1.2 %

@Pressure 20.0 MPa,
Time 3.60e+7 sec
 1.2 %

@Pressure 2900 psi,
Time 10000 hour
 ISO 899
1.4 %

@Time 3600 sec,
Pressure 30.0 MPa
 1.4 %

@Time 1.00 hour,
Pressure 4350 psi
 ISO 899
1.4 %

@Time 3600 sec,
Pressure 30.0 MPa
 1.4 %

@Time 1.00 hour,
Pressure 4350 psi
 ISO 899
1.5 %

@Pressure 30.0 MPa,
Time 360000 sec
 1.5 %

@Pressure 4350 psi,
Time 100 hour
 ISO 899
1.5 %

@Pressure 30.0 MPa,
Time 360000 sec
 1.5 %

@Pressure 4350 psi,
Time 100 hour
 ISO 899
1.5 %

@Time 3600 sec,
Pressure 30.0 MPa
 1.5 %

@Time 1.00 hour,
Pressure 4350 psi
 140°C; ISO 899
1.5 %

@Pressure 20.0 MPa,
Time 3.60e+6 sec
 1.5 %

@Pressure 2900 psi,
Time 1000 hour
 140°C; ISO 899
1.6 %

@Pressure 25.0 MPa,
Time 360000 sec
 1.6 %

@Pressure 3630 psi,
Time 100 hour
 140°C; ISO 899
1.9 %

@Pressure 30.0 MPa,
Time 3.60e+7 sec
 1.9 %

@Pressure 4350 psi,
Time 10000 hour
 ISO 899
1.9 %

@Pressure 30.0 MPa,
Time 3.60e+7 sec
 1.9 %

@Pressure 4350 psi,
Time 10000 hour
 ISO 899
2.0 %

@Time 3600 sec,
Pressure 40.0 MPa
 2.0 %

@Time 1.00 hour,
Pressure 5800 psi
 ISO 899
2.0 %

@Time 3600 sec,
Pressure 40.0 MPa
 2.0 %

@Time 1.00 hour,
Pressure 5800 psi
 ISO 899
2.1 %

@Pressure 25.0 MPa,
Time 3.60e+6 sec
 2.1 %

@Pressure 3630 psi,
Time 1000 hour
 140°C; ISO 899
2.2 %

@Pressure 30.0 MPa,
Time 360000 sec
 2.2 %

@Pressure 4350 psi,
Time 100 hour
 140°C; ISO 899
2.3 %

@Pressure 40.0 MPa,
Time 360000 sec
 2.3 %

@Pressure 5800 psi,
Time 100 hour
 ISO 899
2.3 %

@Pressure 40.0 MPa,
Time 360000 sec
 2.3 %

@Pressure 5800 psi,
Time 100 hour
 ISO 899
2.7 %

@Pressure 40.0 MPa,
Time 3.60e+7 sec
 2.7 %

@Pressure 5800 psi,
Time 10000 hour
 ISO 899
2.7 %

@Time 3600 sec,
Pressure 50.0 MPa
 2.7 %

@Time 1.00 hour,
Pressure 7250 psi
 ISO 899
2.7 %

@Pressure 40.0 MPa,
Time 3.60e+7 sec
 2.7 %

@Pressure 5800 psi,
Time 10000 hour
 ISO 899
2.7 %

@Time 3600 sec,
Pressure 50.0 MPa
 2.7 %

@Time 1.00 hour,
Pressure 7250 psi
 ISO 899
3.0 %

@Pressure 30.0 MPa,
Time 3.60e+6 sec
 3.0 %

@Pressure 4350 psi,
Time 1000 hour
 140°C; ISO 899
3.1 %

@Pressure 50.0 MPa,
Time 360000 sec
 3.1 %

@Pressure 7250 psi,
Time 100 hour
 ISO 899
3.1 %

@Pressure 50.0 MPa,
Time 360000 sec
 3.1 %

@Pressure 7250 psi,
Time 100 hour
 ISO 899
3.6 %

@Pressure 50.0 MPa,
Time 3.60e+7 sec
 3.6 %

@Pressure 7250 psi,
Time 10000 hour
 ISO 899
3.6 %

@Pressure 50.0 MPa,
Time 3.60e+7 sec
 3.6 %

@Pressure 7250 psi,
Time 10000 hour
 ISO 899
Creep Strength 5.00 MPa

@Time 3.60e+7 sec
 725 psi

@Time 10000 hour
 in water at 95°C
8.00 MPa

@Time 3.60e+6 sec
 1160 psi

@Time 1000 hour
 in water at 95°C
16.0 MPa

@Time 360000 sec
 2320 psi

@Time 100 hour
 in water at 95°C
30.0 MPa

@Time 36000 sec
 4350 psi

@Time 10.0 hour
 in water at 95°C
Modulus of Elasticity 2.25 GPa

@Temperature 140 °C
 326 ksi

@Temperature 284 °F
 ISO 527
2.40 GPa

@Temperature 100 °C
 348 ksi

@Temperature 212 °F
 ISO 527
2.50 GPa

@Temperature 60.0 °C
 363 ksi

@Temperature 140 °F
 ISO 527
2.55 GPa

@Temperature 20.0 °C
 370 ksi

@Temperature 68.0 °F
 ISO 527
Tensile Modulus 2.70 GPa
392 ksi
ISO 527-2
Flexural Modulus 2.70 GPa
392 ksi
ISO 178
Shear Modulus 0.200 GPa

@Temperature 225 °C
 29.0 ksi

@Temperature 437 °F
 ISO 6721
0.900 GPa

@Temperature 200 °C
 131 ksi

@Temperature 392 °F
 ISO 6721
0.950 GPa

@Temperature 100 °C
 138 ksi

@Temperature 212 °F
 ISO 6721
1.00 GPa

@Temperature 50.0 °C
 145 ksi

@Temperature 122 °F
 ISO 6721
Izod Impact, Notched (ISO) 15.7 kJ/m²
7.50 ft-lb/in²
ISO 180/A
Users viewing this material also viewed the following:
Copyright © lookpolymers.com All Rights Reserved