Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 69.0 MPa | 10000 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® DMX1132 PC Copolymer Lexan* DMX1132 is a high flow polycarbonate copolymer resin with improved ammonia resistance over regular polycarbonate resin. |
|||
Tensile Strength, Yield | 69.0 MPa | 10000 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Lexan® ML7677A PC (Asia Pacific) Commercial grade for Polycarbonate in only nature color. Excellent processability, super high flow, flame retardant, UL rated V-1 at 2.0mm.This data was supplied by SABIC-IP for the Asia Pacific reg.. |
|||
Tensile Strength, Yield | 69.0 MPa | 10000 psi | ASTM Data |
Dow Isoplast® 202 Polyurethane (PUR-RT), Impact Modified
(discontinued **) ISOPLAST® 202 resin is an impact modified amorphous polymer with the chemical resistance of crystalline resins. Its outstanding properties include excellent chemical resistance, high heat, low mois.. |
|||
Tensile Strength, Yield | 69.0 MPa | 10000 psi | ASTM Data |
Dow Isoplast® 2520 Polyurethane (PUR-RT), Impact Modified
(discontinued **) ISOPLAST® 2520 resin is an impact modified amorphous polymer with the chemical resistance of crystalline resins specially designed for medical applications. Its outstanding properties include excel.. |
|||
Tensile Strength, Yield | 69.0 MPa | 10000 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Lexan® DMX1132 PC Copolymer (Europe-Africa-Middle East) Lexan* DMX1132 is a high flow polycarbonate copolymer resin with improved ammonia resistance over regular polycarbonate resin.This data was supplied by SABIC-IP for the Europe-Africa-Middle East reg.. |
|||
Tensile Strength, Yield | 69.0 MPa | 10000 psi | ASTM D638 |
Covestro Apec® DP9-9373 High-Heat Polycarbonate, General Purpose, UV-Stabilized
(discontinued **) Information provided by Bayer Corporation, Plastics DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and has officially adopted its new name – Covestro. This produ.. |
|||
Tensile Strength, Yield | 69.0 MPa | 10000 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL V01525 PPE+HIPS Noryl* V01525 is a 15% milled fiber reinforced, injection moldable grade. Designed for good dimensional stability and low warpage, this resin also uses non-chlorinated, non-brominated FR additives t.. |
|||
Tensile Strength, Yield | 69.0 MPa | 10000 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL V01525 PPE+HIPS (Europe-Africa-Middle East) Noryl* V01525 is a 15% milled fiber reinforced, injection moldable grade. Designed for good dimensional stability and low warpage, this resin also uses non-chlorinated, non-brominated FR additives t.. |
|||
Tensile Strength, Yield | 69.0 MPa | 10000 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP RL004 PA 66 LNP* LUBRICOMP* RL004 is a copmpound based on Nylon 66 resin containing 20% PTFE. Added feature of this grade includes: Wear Resistant. |
|||
Tensile Strength, Yield | 69.0 MPa | 10000 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP RN001S PA 66 LNP* LUBRICOMP* RN001S is a compound based on Nylon 66 resin containing 2% MOS2. Added features of this material include: Wear Resistant, Heat Stabilized. |
|||
Tensile Strength, Yield | 69.0 MPa | 10000 psi | ASTM D 638 |
Shakespeare Isocorâ„¢ TT52SI Nylon 6 Terpolymer Isocorâ„¢ TT52SI multi-polymer is a linear polyamide with unique solubility characteristics and physical properties. Isocorâ„¢ TT52SI is easily processed and has a wide range of application.. |
|||
Tensile Strength, Yield | 69.0 MPa | 10000 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON DD0009XP PC LNP* STAT-KON* D-FR is a compound based on Polycarbonate resin containing Carbon. Added features of this grade include: Flame Retardant, Electrically Conductive. |
|||
Tensile Strength, Yield | 69.0 MPa | 10000 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics LNP Stat-kon RX89129 PA 66 LNP* Stat-Kon RX89129 is a compound based on Nylon 6,6. Fillers are proprietary.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength, Yield | 69.0 MPa | 10000 psi | ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP 9X04488 PPS LNP* THERMOCOMP* 9X04488 is a compound based on PPS resin containing Mineral. |
|||
Tensile Strength, Yield | 69.0 MPa | 10000 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL GTX GTX975 PPE+PA NORYL GTX975 is a 18% mineral filled material especially designed for in- or on-line painted exterior automotive trim part, e.g. tankflaps and corner panels. This material combines high stiffness an.. |
|||
Tensile Strength, Yield | 69.0 MPa | 10000 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL GTX GTX975 PPE+PA (Asia Pacific) NORYL GTX975 is a 18% mineral filled material especially designed for in- or on-line painted exterior automotive trim part, e.g. tankflaps and corner panels. This material combines high stiffness an.. |
|||
Tensile Strength, Yield | 69.0 MPa | 10000 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Noryl NH3060 PPE+HIPS NH3060 resin is a modified PPE + PS blend with an excellent balance of non-chlorinated non-brominated flame retardance, hydrolytic stability, impact and heat resistance, good flow, and low specific .. |
|||
Tensile Strength, Yield | 69.0 MPa | 10000 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL NH7010 PPE+PS Noryl* NH7010 resin is a modified PPE-PS blend that exhibits an excellent balance of non-halogenated flame retardance, high heat resistance, good flow, and low specifc gravity for light weight parts.. |
|||
Tensile Strength, Yield | 69.0 MPa | 10000 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL NH7111E PPE+HIPS Noryl* EXNL0280 is a glass fiber reinforced, injection moldable modified polyphenylene ether resin. Designed for good dimensional stability and low warpage, this resin also uses non-halogenated FR a.. |
|||
Tensile Strength, Yield | 69.0 MPa | 10000 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL NH7111E PPE+HIPS (Asia Pacific) Noryl* EXNL0280 is a glass fiber reinforced, injection moldable modified polyphenylene ether resin. Designed for good dimensional stability and low warpage, this resin also uses non-halogenated FR a.. |
|||
Tensile Strength, Yield | 69.0 MPa | 10000 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP RI001 PA 66 (Europe-Africa-Middle East) LNP* Lubricomp* RI001 is a compound based on Nylon 66 resin containing Silicone. |
|||
Tensile Strength, Yield | 69.0 MPa | 10000 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL EXNL0353 PPE+HIPS EXNL0353 resin is a modified PPE + PS blend with an excellent balance of non-halogenated flame retardance, hydrolytic stability, impact and heat resistance, good flow, and low specific gravity for l.. |
|||
Tensile Strength, Yield | 69.0 MPa | 10000 psi | ASTM D638 |
Lubrizol Isoplast® 2531 Engineering Thermoplastic Polyurethane Resin for Medical Applications Features: USP Class VIAvailable in Americas, Europe, Middle East, Africa, India and AsiaData provided by LubrizolLubrizol acquired the Isoplast product line from Dow in 2009. |
|||
Tensile Strength, Yield | 69.0 MPa @Temperature 23.0 °C |
10000 psi @Temperature 73.4 °F |
|
Hexcel® HexPly® 954-2A Curing Cyanate Resin HexPly® 954-2A is a 350°F (177°C) curing toughened cyanate resin with low moisture absorption, and excellent microcracking resistance. HexPly® 954-2A is formulated for autoclave or press molding.. |
|||
Tensile Strength, Yield | 69.0 MPa | 10000 psi | ISO 527-1/-2 |
Covestro Bayblend® FR 3030 Polycarbonate + ABS, Flame Retardant Grade Flame retardant extrusion gradeVicat/B 120 temperature = 115 °Cgood extrusion and vacuum-forming behaviourUL-listing 94 V-0 (1.5 mm)halogen-free according to DIN VDE 0472-815glow wire temperature (.. |
|||
Tensile Strength, Yield | 69.0 MPa | 10000 psi | 5 mm/min; ISO 527 |
Eurostar Starflam PX06012 PA6, Flame Retardant, Injection Molded Starflam PX06012 is an Unfilled, Halogen Free and Red Phosphorous Free, Flame Retardant, Polyamide 6 Injection Molding ResinInformation provided by Eurostar. |
|||
Tensile Strength, Yield | 69.0 MPa | 10000 psi | 50mm/min; ISO 527 |
BASF Ultramid® 1310-11 NF2001 PA66 (Conditioned) Ultramid 1310-11 NF2001 is a controlled crystallization, fast cycling PA6/6 which provides extremely fast cycle times and improved productivity over Ultramid 1000. |
|||
Tensile Strength, Yield | 69.0 MPa @Temperature 23.0 °C |
10000 psi @Temperature 73.4 °F |
DAM; ISO 527 |
DuPont Performance Polymers Zytel® HTN FE8200 BK431 Polyphthalamide (PPA)
(Unverified Data**) Zytel® HTNFE8200 BK431 is an unreinforced, toughened, heat stabilized, lubricated high performance polyamide resin for injection molding. It is also a PPA resin.Information provided by DuPont Perfo.. |