SABIC Innovative Plastics LNP STAT-KON DD0009XP PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON DD0009XP PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-KON* D-FR is a compound based on Polycarbonate resin containing Carbon. Added features of this grade include: Flame Retardant, Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.130 % | 0.130 % | 50% RH, 24 hrs; ASTM D570 |
| 0.210 % | 0.210 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Time 86400 sec |
0.0050 - 0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 46.0 MPa | 6670 psi | Type I, 5 mm/min; ASTM D638 |
| 50.0 MPa | 7250 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 58.0 MPa | 8410 psi | 5 mm/min; ISO 527 |
| 69.0 MPa | 10000 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 11 % | 11 % | 5 mm/min; ISO 527 |
| 13 % | 13 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 4.7 % | 4.7 % | Type I, 5 mm/min; ASTM D638 |
| 4.7 % | 4.7 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 2.50 GPa | 363 ksi | 1 mm/min; ISO 527 |
| Flexural Modulus | 2.52 GPa | 365 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched | 1.36 J/cm | 2.55 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 17.0 J/cm | 31.8 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 152 kJ/m² | 72.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Impact Test | 33.0 J | 24.3 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 138 °C | 280 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 139 °C @Thickness 3.20 mm |
282 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 126 °C | 259 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 130 °C @Thickness 3.20 mm |
266 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 5.0 - 8.0 ohm | 5.0 - 8.0 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Nye Lubricants 570M (NT) Synthetic Oil
- PolyOne Geon™ Vinyl Flexible XV3863 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Indium Corp. Indalloy® 174 Bi-In-Sn Fusible Alloy
- Sylvin Technologies 8925-80 Natural PVC Extrusion Compound
- Techmer ES Plastiblend® PA6 GF30 RM BK Nylon 6
- A. Schulman POLYBATCH™ Tan LL60139/2 Concentrate Based In LLDPE
- Eastman Eastar EN076 Copolyester
- Epoxy Technology EPO-TEK® E2036 Epoxy
- 3M Scotch-Weld™ MG250-55 UV Medical Grade Light Cure Adhesive
- Zircar Zirconia ZYW-30A Zirconia Cloth Insulation
Copyright © lookpolymers.com All Rights Reserved