Polymer Property : Tensile Strength, Yield = 59.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	59.0 MPa	8560 psi	Type I, 50 mm/min; ASTM D 638
SABIC Innovative Plastics Cycoloy® MC9000 PC+ABS AUTOMOTIVE. PC+ABS; high heat resistant. Ductile at room temperature. Excellent flow.This data was supplied by SABIC-IP for the Americas region.
Tensile Strength, Yield	59.0 MPa	8560 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® EXL1810T PC Copolymer Lexan* EXL1810T polycarbonate (PC) siloxane copolymer resin is a transparent injection molding grade. This resin offers cold temperature (0 °C) ductility in combination with very high flow char..
Tensile Strength, Yield	59.0 MPa	8560 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® EXL1890T PC Copolymer (Asia Pacific) Lexan* EXL1890T polycarbonate (PC) siloxane copolymer resin is a transparent injection molding grade for food contact applications. This resin offers cold temperature (0 °C) ductility in combin..
Tensile Strength, Yield	59.0 MPa	8560 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® EXL9112 PC Copolymer (Asia Pacific) Opaque PC-Siloxane copolymer with excellent processability. Improved flow, low temp. ductility. Non-chlorinated, non-brominated flame retardant product. UL rated V-0/5VA.
Tensile Strength, Yield	59.0 MPa	8560 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® EXL9112 PC Copolymer (Europe-Africa-Middle East) Opaque PC-Siloxane copolymer with excellent processability. Improved flow, low temp. ductility. Non-chlorinated, non-brominated flame retardant product. UL rated V-0/5VA.
Tensile Strength, Yield	59.0 MPa	8560 psi	Type I, 50 mm/min; ASTM D 638
SABIC Innovative Plastics Lexan® FXG1413T PC Copolymer PC-siloxane copolymer in special "Diamond Sparkle" colors. Medium flow. Improved toughness compared to medium flow standard PC in same color. Color package may affect performance.This data was supp..
Tensile Strength, Yield	59.0 MPa	8560 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® HPX8R PC Copolymer (Asia Pacific) Very high flow specialty polycarbonate with outstanding processability and ductility. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 o..
Tensile Strength, Yield	59.0 MPa	8560 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® ML7691 PC UV stabilized clear polycarbonate formula for internal uses only.
Tensile Strength, Yield	59.0 MPa	8560 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP FARADEX NS0031 PC+ABS (Asia Pacific) Faradex NS0031 is a compound based on PC+ABS blend resin containing non-brominated and non-chlorinated flame retardant system, Stainless Steel. Added features of this material include: EMI/RFI Shiel..
Tensile Strength, Yield	59.0 MPa	8560 psi	ASTM D638
LG Chemical LUMAX GP-5106F General Purpose PBT, 10% Polymer Alloy, Weather Resistant, Flame Retardant LUMAX resins are a family of thermoplastic blends of polybutyleneterephthalate(PBT) and styrenic resins that combine the most desirable properties of both resins and fillers. They offer high heat r..
Tensile Strength, Yield	59.0 MPa	8560 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP Lexan_WR2210 PC LNP* Lubricomp* Lexan_WR2210 compound is an alternative polymeric wear additive technology. No silicones, superior processability/part appearance. Flow similar to LEXAN 121.
Tensile Strength, Yield	59.0 MPa	8560 psi	ASTM D638
SABIC Innovative Plastics LNP LUBRILOY RX99650 PA 66 (Europe-Africa-Middle East) LNP LUBRILOY* RX99650 is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated.
Tensile Strength, Yield	59.0 MPa	8560 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP STAT-KON DX98477 PC LNP* STAT-KON* DX98477 is a compound based on Polycarbonate containing Proprietary Filler(s). Added feature of this grade is: Electrically Conductive.
Tensile Strength, Yield	59.0 MPa	8560 psi	50 mm/min; ISO 527
SABIC Innovative Plastics ValoxÂ® V2000DM PBT (Asia Pacific) Unreinforced, directly metallizable PBT injection molding resin with high flow better release characteristics.
Tensile Strength, Yield	59.0 MPa	8560 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics ValoxÂ® V2000DM PBT (Europe-Africa-Middle East) Unreinforced, directly metallizable PBT injection molding resin with high flow better release characteristics.
Tensile Strength, Yield	59.0 MPa	8560 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP DX11354 PC (Asia Pacific) This is a PC compound with good plating, surface and mechanical performance, a good candidate for Laser Direct Structuring applications.
Tensile Strength, Yield	59.0 MPa	8560 psi	ISO 527
SABIC Innovative Plastics LNP THERMOCOMP KZ001L Acetal Copoly LNP* THERMOCOMP* KZ001L is a compound based on Acetal Copolymer resin containing 5% Milled Glass. Added features of this material include: Low Extractible.
Tensile Strength, Yield	59.0 MPa	8560 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP PH0460A PA 6 LNP* THERMOCOMP* PH0460A is a compound based on Nylon 6. Added feature of this material is: High Specific Gravity.
Tensile Strength, Yield	59.0 MPa	8560 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics ValoxÂ® V2000DM PBT Unreinforced, directly metallizable PBT injection molding resin with high flow better release characteristics.
Tensile Strength, Yield	59.0 MPa	8560 psi	50 mm/min; ISO 527
SABIC Innovative Plastics ValoxÂ® V2000DM PBT Unreinforced, directly metallizable PBT injection molding resin with high flow better release characteristics.
Tensile Strength, Yield	59.0 MPa	8560 psi	ASTM D638
A. Schulman POLYFORT™ FPP 3459 Glass Filled Impact Copolymer DescriptionPolyfort® FPP 3459 is a 30% glass filled copolymerInformation provided by A. Schulman.
Tensile Strength, Yield	59.0 MPa	8560 psi	ASTM D638
A. Schulman POLYFORT™ FPP 3459 Glass Filled Impact Copolymer DescriptionPolyfort® FPP 3459 is a 30% glass filled copolymerInformation provided by A. Schulman.
Tensile Strength, Yield	59.0 MPa	8560 psi	ASTM D638
Eastman TiGlaze SV Copolyester TiGLAZE SV copolyester is a specialty copolyester for the architectural glazing industry, designed to provide a unique balance of toughness, stiffness and material value. The material has a CC1 Ligh..
Tensile Strength, Yield	59.0 MPa	8560 psi	ISO 527-1/-2
DuPont Performance Polymers Crastin® 6130 NC010 Polybutylene Terephthalate (PBT) (Unverified Data**) Unreinforced High Viscosity Polybutylene Terephthalate Developed for Extrusion and Injection Molding Crastin 6130 NC010 is an unreinforced medium high viscosity polybutylene terephthalate resin for ..
Tensile Strength, Yield	59.0 MPa	8560 psi	ASTM D638
Diamond Polymers NYLON 6630 L Black Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
Tensile Strength, Yield	59.0 MPa	8560 psi	DAM; ISO 527-1/-2
DuPont Performance Polymers Zytel® FE3734 NC010 Nylon 612 (Unverified Data**) Unreinforced Polyamide 612 Zytel FE3734 NC010 is an unreinforced lubricated polyamide 612 resin suitable for injection molding.Information provided by DuPont Performance Polymers
Tensile Strength, Yield	59.0 MPa	8560 psi	ASTM D638
E-Polymers Tekaloy® G70A3 , Heat Resistance, Easy Molding PC/ABS Alloy Heat Resistance, Easy MoldingInformation provided by E-Polymers Co. Ltd.
Tensile Strength, Yield	59.0 MPa	8560 psi	ASTM D638
E-Polymers Tekaloy® G70NH Non-Halogen Flame Retardant, Un-Reinforced PC/ABS Alloy Non Halogen Flame Retardant, High FlowInformation provided by E-Polymers Co. Ltd.
Tensile Strength, Yield	59.0 MPa	8560 psi	23°C, 50% RH; ASTM D638
Asahi Kasei Xyron® 340V Modified Polyphenylene Ether Flame RetardantInformation provided by Asahi Kasei
Tensile Strength, Yield	59.0 MPa	8560 psi	ASTM D638
LG Chemical LUPOY SR-3108F High Flow Modified PC, 10% Mineral Fillers, High Reflectivity, Flame Retardant Among the characteristics of LUPOY polycarbonate resins are excellent mechanical properties, high heat resistance, high impact strength, and dimensional stability.Applications:Automotive: Automotive..