SABIC Innovative Plastics LNP STAT-KON DX98477 PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON DX98477 PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-KON* DX98477 is a compound based on Polycarbonate containing Proprietary Filler(s). Added feature of this grade is: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | ASTM D792 |
| Density | 1.25 g/cc | 0.0452 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.160 % | 0.160 % | 50% RH, 24 hrs; ASTM D570 |
| 0.240 % | 0.240 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0080 - 0.010 cm/cm @Time 86400 sec |
0.0080 - 0.010 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0080 - 0.010 cm/cm @Time 86400 sec |
0.0080 - 0.010 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 46.0 MPa | 6670 psi | 5 mm/min; ISO 527 |
| 49.0 MPa | 7110 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 58.0 MPa | 8410 psi | 5 mm/min; ISO 527 |
| 59.0 MPa | 8560 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 21.2 % | 21.2 % | Type I, 5 mm/min; ASTM D638 |
| 21.4 % | 21.4 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 4.7 % | 4.7 % | 5 mm/min; ISO 527 |
| 4.8 % | 4.8 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 2.70 GPa | 392 ksi | 1 mm/min; ISO 527 |
| 2.79 GPa | 405 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 89.0 MPa | 12900 psi | ISO 178 |
| Flexural Modulus | 2.72 GPa | 395 ksi | 2 mm/min; ISO 178 |
| 2.89 GPa | 419 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.870 J/cm | 1.63 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 23.3 J/cm | 43.7 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 234 kJ/m² | 111 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 45.0 J @Temperature 23.0 °C |
33.2 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 34.0 J | 25.1 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 67.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
37.2 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 66.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
36.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C | 288 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 142 °C @Thickness 3.20 mm |
288 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 132 °C | 270 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 133 °C @Thickness 3.20 mm |
271 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 2.0 - 6.0 ohm | 2.0 - 6.0 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Pacific Sintered Materials FP-1650-S Phosphorous Iron Soft Magnetic Powdered Metal
- Idemitsu Kosan Xarec® EA 533 SPS, 30% Glass Filled
- Hexcel® Redux® 330 MSS Epoxy film adhesives for the bonding and finishing of composites
- A. Schulman POLYFLAM™ RPP 1133 Flame Retardant, Copolymer Polypropylene
- Akzo Nobel Expancel® 091 WUF 40 Wet unexpanded microspheres
- DuPont Performance Polymers Zytel® 101 NC010 Nylon 66 (Unverified Data**)
- Axiall 5006 Rigid PVC, Extrusion, White
- PolyOne Synprene® ST-6105 Thermoplastic Elastomer - SBC (discontinued **)
Copyright © lookpolymers.com All Rights Reserved