SABIC Innovative Plastics Valox® V2000DM PBT

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Valox®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Valox® V2000DM PBT.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Unreinforced, directly metallizable PBT injection molding resin with high flow better release characteristics.
Physical Properties Metric English Comments
Specific Gravity 1.32 g/cc
1.32 g/cc
ASTM D792
Density 1.32 g/cc
0.0477 lb/in³
ISO 1183
Moisture Absorption 0.340 %
0.340 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.080 %
0.080 %
ISO 62
Linear Mold Shrinkage, Flow 0.021 - 0.024 cm/cm

@Thickness 3.20 mm
 0.021 - 0.024 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 35.4 g/10 min

@Load 2.16 kg,
Temperature 250 °C
 35.4 g/10 min

@Load 4.76 lb,
Temperature 482 °F
 ASTM D1238
Melt Index of Compound 34 g/10 min

@Load 2.16 kg,
Temperature 250 °C
 34 g/10 min

@Load 4.76 lb,
Temperature 482 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 40.0 MPa
5800 psi
Type I, 50 mm/min; ASTM D638
55.0 MPa
7980 psi
50 mm/min; ISO 527
Tensile Strength, Yield 59.0 MPa
8560 psi
Type I, 50 mm/min; ASTM D638
59.0 MPa
8560 psi
50 mm/min; ISO 527
Elongation at Break 15 %
15 %
50 mm/min; ISO 527
100 %
100 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 7.0 %
7.0 %
50 mm/min; ISO 527
20 %
20 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.80 GPa
406 ksi
5 mm/min; ASTM D638
3.00 GPa
435 ksi
1 mm/min; ISO 527
Flexural Yield Strength 90.0 MPa
13100 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.50 GPa
363 ksi
2 mm/min; ISO 178
2.57 GPa
373 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.460 J/cm
0.862 ft-lb/in
ASTM D256
Izod Impact, Unnotched NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
 ASTM D4812
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
80*10*4; ISO 180/1A
2.00 kJ/m²

@Temperature -30.0 °C
 0.952 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
Charpy Impact, Notched 0.500 J/cm²
2.38 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 54.0 J

@Temperature 23.0 °C
 39.8 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 84.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 46.7 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
84.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 46.7 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 80.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 44.4 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
80.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 44.4 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 53.0 °C
127 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
54.0 °C

@Thickness 3.20 mm
 129 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Vicat Softening Point 185 °C
365 °F
Rate B/50; ASTM D1525
185 °C
365 °F
Rate B/120; ISO 306
186 °C
367 °F
Rate B/50; ISO 306