Asahi Kasei Xyron® 340V Modified Polyphenylene Ether
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, Heat Resistant |
| Manufacturer | Asahi Kasei |
| Trade Name | Xyron® |
| Port | Shanghai port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | Asahi Kasei Xyron® 340V Modified Polyphenylene Ether.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flame RetardantInformation provided by Asahi Kasei
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | 23°C; ASTM D792 |
| Moisture Absorption | 0.100 % | 0.100 % | 23°C, 50% RH 24 hours; ASTM D570 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 59.0 MPa | 8560 psi | 23°C, 50% RH; ASTM D638 |
| Elongation at Break | 40 % | 40 % | 23°C, 50% RH; ASTM D638 |
| Flexural Strength | 75.0 MPa | 10900 psi | 23°C, 50% RH; ASTM D790 |
| Flexural Modulus | 2.40 GPa | 348 ksi | 23°C, 50% RH; ASTM D790 |
| Izod Impact, Notched | 1.47 J/cm <br>@Thickness 6.40 mm,<br> Temperature 23.0 °C |
2.75 ft-lb/in <br>@Thickness 0.252 in,<br> Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 75.0 µm/m-°C <br>@Temperature -30.0 - 60.0 °C |
41.7 µin/in-°F <br>@Temperature -22.0 - 140 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | ASTM D648 |
| Flammability, UL94 | V-1 <br>@Thickness 1.60 mm |
V-1 <br>@Thickness 0.0630 in |
|
| V-1 <br>@Thickness 3.20 mm |
V-1 <br>@Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | 50% RH; ASTM D257 |
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | 50% RH; ASTM D257 |
| Dielectric Constant | 2.9 <br>@Frequency 1e+6 Hz |
2.9 <br>@Frequency 1e+6 Hz |
50% RH; ASTM D150 |
| 2.9 <br>@Frequency 1e+6 Hz |
2.9 <br>@Frequency 1e+6 Hz |
50% RH; ASTM D150 | |
| Dielectric Strength | 29.0 kV/mm <br>@Thickness 2.00 mm |
737 kV/in <br>@Thickness 0.0787 in |
Short time; ASTM D149 |
| Dissipation Factor | 0.0030 <br>@Frequency 60 Hz |
0.0030 <br>@Frequency 60 Hz |
50% RH; ASTM D150 |
| 0.0040 <br>@Frequency 1e+6 Hz |
0.0040 <br>@Frequency 1e+6 Hz |
50% RH; ASTM D150 | |
| Arc Resistance | 70 sec | 70 sec | Tungsten; ASTM D495 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 240 - 270 °C | 464 - 518 °F | Resin Temperature |
| Mold Temperature | 50.0 - 80.0 °C | 122 - 176 °F | |
| Drying Temperature | 90.0 - 100 °C | 194 - 212 °F | Pre-drying Temperature |
| Dry Time | 2 - 4 hour | 2 - 4 hour |
Users viewing this material also viewed the following:
- PlastiComp Velocity® LCF40-PA6 High Flow Nylon 6, 40% Long Carbon Fiber
- Haynes HR-120® alloy, solution heat-treated aged at 1200°F for 1000 hours
- Borealis Daplen™ EG203AE Polypropylene Compound Elastomer and Mineral Modified
- DuPont Elvanol® T-25 Polyvinyl Alcohol Textile Grade
- Arkema Group Rilsan® 6733 Nylon 11, Flexible Tubing Grade (Conditioned)
- A. Schulman ComAlloy Aqualoy® 145 Polypropylene, Glass Reinforced, Chemically Coupled NSF
- Tipco Tipcolene® HR 7224 - 25% Talc/Mineral Reinforced, Impact Modified Polypropylene Copolymer
- Solvay RHODAPEX® ES STD Surfactant
Copyright © lookpolymers.com All Rights Reserved