Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 49.0 MPa | 7100 psi | ASTM D638 |
Polymer Resources TP-FV699 PBT, 10% Glass Reinforced Structural Foam Grade, Low Shrinkage Process: Foam MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Foam grades tested with foamed parts with a 10% weight reduction rel.. |
|||
Tensile Strength, Yield | 49.0 MPa @Thickness 3.20 mm |
7110 psi @Thickness 0.126 in |
5mm/min; ASTM D638 |
LG Chemical LUCEL FW720F Modified POM, Friction Resistance, Abrasion Resistance Feature: Injection Molding, Modified POM, Friction Resistance, Abrasion ResistanceApplication: Gears, Printer Roller Pumps, Gear Worm WheelsCAS No. 66455-31-0 and 9002-84-2Information provided by LG.. |
|||
Tensile Strength, Yield | 49.0 MPa @Thickness 3.20 mm |
7110 psi @Thickness 0.126 in |
50 mm/min; ASTM D638 |
LG Chemical RS650 ABS Feature: Extrusion Molding, General PurposeApplication: MiscellaneousCAS No. 9003-56-9Information provided by LG Chemical |
|||
Tensile Strength, Yield | 49.0 MPa | 7100 psi | ASTM D638 |
Kostat ICP-STAT ICD-1005 ABS Sheet KOSTATs ICP-STAT is a thermoplastic sheet coated with an inherently conductive polymer (ICP). ICP-STAT has distinctive advantages in ESD and cleanliness performances compared to other materials bas.. |
|||
Tensile Strength, Yield | 49.0 MPa | 7110 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP DX94375H PC LNP* LUBRICOMP* DX94375H is a compound based on Polycarbonate resin containing Proprietary Fillers. Added features of this material include: Healthcare, Wear Resistant. |
|||
Tensile Strength, Yield | 49.0 MPa | 7110 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP KP002 Acetal Copoly (Asia Pacific) LNP* Lubricomp* KP002 is a compound based on Acetal Copolymer resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength, Yield | 49.0 MPa | 7110 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP KZL16 Acetal Copolymer (Europe-Africa-Middle East) LNP* LUBRICOMP* KZL16 is a compound based on Acetal Copolymer resin containing milled Glass and PTFE. Added features include; Internally Lubricated. |
|||
Tensile Strength, Yield | 49.0 MPa | 7110 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP ZP001XXP PPE+PS LNP* LUBRICOMP* ZP001XXP is a compound based on PPE+PS resin containing 5% PTFE/Silicone. Added features of this material include: Wear Resistant. |
|||
Tensile Strength, Yield | 49.0 MPa | 7110 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRILOY D2000I PC LNP* LUBRILOY* D2000I is a compound based on Polycarbonate resin containing Proprietary Lubricant. Added features of this material include: Wear Resistant, High Impact. |
|||
Tensile Strength, Yield | 49.0 MPa | 7110 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Xenoy® IQ1103R PBT+PC Xenoy* Resin iQ1103R - Environmetally responsible, sustainable, and low carbon footprint resin. Xenoy iQ1103R is an unreinforced, impact modified PC + iQ-PBT alloy with excellent low temperature im.. |
|||
Tensile Strength, Yield | 49.0 MPa | 7110 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics XYLEX X7300 PC+POLYESTER (Europe-Africa-Middle East) PC+POLYESTER unreinforced alloy. High flow, chemically resistant with excellent optical quality. UV-stabilized. |
|||
Tensile Strength, Yield | 49.0 MPa | 7110 psi | ISO 527 |
Styrolution Novodur® 250 ABS Novodur 250 is an injection molding grade of ABS with standard impact strength, high flow and high gloss.Information provided by Styrolution |
|||
Tensile Strength, Yield | 49.0 MPa | 7110 psi | ASTM D638 |
Samyang Tribit® 1503S Polybutylene Terephthalate Characteristics:High impactApplications:AutomotiveConnectorGearOutdoor handleIgnition systemElectronicConnectorGas valveCoil bobbinSwitch caseRelay caseO/A partsAll information provided by Samyang |
|||
Tensile Strength, Yield | 49.0 MPa | 7110 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Xenoy® IQ1103U PBT+PC (Asia Pacific) Xenoy* Resin iQ1103U - Environmetally responsible, sustainable, and low carbon footprint resin. Xenoy iQ1103U is an unreinforced, UV stable, impact modified PC+ iQ-PBT alloy with excellent low temp.. |
|||
Tensile Strength, Yield | 49.0 MPa | 7110 psi | ISO 527 |
Styrolution Novodur® 240 ABS Novodur 240 is an injection molding grade of ABS with standard impact strength and high gloss.Information provided by Styrolution |
|||
Tensile Strength, Yield | 49.0 MPa | 7110 psi | ISO 527 |
Styrolution Novodur® 5300 ABS Novodur 5300 is a high heat injection molding grade with high impact strength, good chemical resistance and reduced emission (PC modified)Information provided by Styrolution |
|||
Tensile Strength, Yield | 49.0 MPa | 7110 psi | ISO 527 |
Styrolution Novodur® H801 ABS / PC Novodur H801 is a high heat injection molding grade with high impact strength and reduced emission.Information provided by Styrolution |
|||
Tensile Strength, Yield | 49.0 MPa | 7110 psi | 9.8 in/min; ASTM D638 |
Teknor Apex Sinvicomp SRF 1703 Polyvinyl Chloride, Rigid Availability: Asia Pacific Features: Good Impact Resistance Uses: Fittings Forms: Pellets Processing Method: Injection MoldingInformation Provided by Teknor Apex |
|||
Tensile Strength, Yield | 49.0 MPa | 7110 psi | ASTM D638 |
A. Schulman POLYFORT™ FPP 3715 Glass Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 3715 is a 15% glass filled homopolymer polypropylene product. Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 49.0 MPa | 7110 psi | 50 mm/min; ISO 527 |
Chi Mei Polylac® PA-717C ABS Medium impact |
|||
Tensile Strength, Yield | 49.0 MPa | 7110 psi | chs 2 in/min; ASTM D638 |
Diamond Polymers ABS 2100 P Compounding Grade Powder Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc. |
|||
Tensile Strength, Yield | 49.0 MPa | 7100 psi | chs 2 in/min; ASTM D638 |
Diamond Polymers ABS TM 40 Description: Heat Resistant Grade, Ultra High HeatInformation provided by Diamond Polymers, Inc. |
|||
Tensile Strength, Yield | 49.0 MPa | 7110 psi | 50 mm/min; ISO 527 |
Chi Mei Polylac® PA-756 ABS - High Flow High rigid, high flow |
|||
Tensile Strength, Yield | 49.0 MPa | 7100 psi | ASTM D-638 |
Axiall 3152 Rigid PVC, Extrusion Georgia Gulf 3152 is a twin screw powder blend NSF approved for the extrusion of potable water and drain waste and vent pipe application.Information provided by Georgia GulfGeorgia Gulf became Axial.. |
|||
Tensile Strength, Yield | 49.0 MPa | 7110 psi | ASTM D638 |
Ashley Polymers Ashlene® L925 Nylon 12 A flexible Nylon 12 with exceptional toughness, excellent abrasion and chemical resistance, outstanding low temperature performance, dimensional stability and low moisture absorption. The natural c.. |
|||
Tensile Strength, Yield | 49.0 MPa | 7110 psi | ISO value at 50 mm/min. |
BASF Capron® 1202CQ Nylon 6 (Conditioned)
(discontinued **) Capron 1202CQ is a blended low viscosity, polyamide 6 injection molding homopolymer, possessing a modified crystalline structure for increased property performance and faster cycles. It is also ava.. |
|||
Tensile Strength, Yield | 49.0 - 227 MPa | 7100 - 32900 psi | Average value: 137 MPa Grade Count:11 |
Overview of materials for Thermoplastic Polyurethane (TPUR), Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Thermoplastic Polyurethane (TPUR), Glass Fiber Reinforced". Each property range of values reported is mi.. |
|||
Tensile Strength, Yield | 49.0 MPa @Thickness 3.20 mm |
7110 psi @Thickness 0.126 in |
50 mm/min; ASTM D638 |
LG Chemical XG570 MABS, Anti-Scratch, High Impact, High Flow Feature: Injection Molding, Anti-Scratch, High Impact, High FlowApplication: LCD TV Stand Base, Audio/Video HousingCAS No. 9010-94-0Information provided by LG Chemical |
|||
Tensile Strength, Yield | 49.0 MPa | 7100 psi | chs 2 in/min; ASTM D638 |
Diamond Polymers ABS/PC 9801 Description: Injection Molding Grade, High Impact, High HeatInformation provided by Diamond Polymers, Inc. |
|||
Tensile Strength, Yield | 49.0 - 142 MPa | 7110 - 20600 psi | Average value: 104 MPa Grade Count:6 |
Overview of materials for Polybutylene Terephthalate (PBT), Carbon Black Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Carbon Black Filled". Each property range of values reported is minimu.. |