Polymer Property : Tensile Strength, Yield = 17.2 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	17.2 MPa	2490 psi	Type IV, 510 mm/min; ASTM D638
PolyOne Geon™ Vinyl Wire & Cable W1200 Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne
Tensile Strength, Yield	17.2 MPa	2490 psi	Type IV, 510 mm/min; ASTM D638
PolyOne Geon™ Vinyl Wire & Cable W1802-xx06FRA Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne
Tensile Strength, Yield	17.2 MPa	2490 psi	Type IV, 510 mm/min; ASTM D638
PolyOne Geon™ Vinyl Wire & Cable WJB593KBL Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne
Tensile Strength, Yield	17.2 MPa	2490 psi	Type IV, 510 mm/min; ASTM D638
PolyOne Syncure™ System S110FV Polyethylene, Crosslinked (XLPE) Syncure™ systems are two part moisture crosslinkable compounds, is a UL bulletinized high strength, highly flame retardant insulation compound. Available in a RoHS complaint version.NOTE: The above..
Tensile Strength, Yield	17.2 MPa	2500 psi	TM R050-36
Resinlab® EP950NMF Gray Non-Metallic Filled Rubber Modified Epoxy Resinlab™ EP950NMF Gray is a non-metallic filled version of EP950G. It is a one-part rubber modified epoxy designed for bonding metal and other structural material subject to stress at elevated tem..
Tensile Strength, Yield	17.2 MPa	2490 psi	Type IV, 510 mm/min; ASTM D638
PolyOne Geon™ Vinyl Flexible R3792E Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne
Tensile Strength, Yield	17.2 MPa	2500 psi	ASTM D638
NOVA Chemicals Sclair® 94E Butene LMDPE Film and Extrusion Resin Features: Excellent processabilityGood stiffness and strengthHigh stretchability Applications: Overwrap filmNettingBlend resinInformation provided by Nova Chemicals
Tensile Strength, Yield	17.2 MPa	2500 psi	ASTM D638
Global TPO-28T Talc Filled TPO Grade Data provided by Global Polymers Corporation.
Tensile Strength, Yield	17.2 MPa	2490 psi	ISO 1184-1983E
LyondellBasell DP 0110M Polybutene Key Features: highly isotactic, semi-crystalline nucleated homopolymer, good creep resistance, good environmental stress crack resistance, FDA acceptable, easily dispersibleApplications: packaging i..
Tensile Strength, Yield	17.2 MPa	2500 psi	ASTM D412
Teknor Apex APEXÂ® 3310-85 Polyvinyl Chloride, Flexible Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTMFeatures-Sterilizable, RadiationUses-Automotive Applications, Food Service Applications, General Purpose, Med..
Tensile Strength, Yield	17.2 MPa	2490 psi	41% Ret.
UBE UBESTA® 3030U Nylon 12 (After Ethanol for 500 hours) Description: UBESTA has a strong resistance to chemicals. Under normal conditions, it is not significantly affected by alkalis, alcohols, ethers, ketones, hydrocarbons, lubricating oils, gasoline, c..
Tensile Strength, Yield	17.2 MPa	2500 psi	ASTM D1238
Borealis Superclean™ LE4244 Natural Crosslinkable Polyethylene for HIV Power Cable Insulation Superclean LE4244 is a natural crosslinkable polyethylene compound developed especially for the insulation of medium and high voltage cables. It provides an excellent balance of anon-staining antio..
Tensile Strength, Yield	17.2 MPa	2500 psi	ASTM D638
A. Schulman POLYTROPE™ TPP 620 Olefinic Elastomer DescriptionPolytrope TPP 620is an olefinic elastomer developed to exhibit very low thermal expansion, high DOI on painted parts with good low temperature impact properties. ApplicationTPP 620 is des..
Tensile Strength, Yield	17.2 MPa	2500 psi	ASTM D638
A. Schulman POLYTROPE™ TPP 1008-01 Injection Molding Reactor Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 1008-01 is an injection molding reactor grade olefinic thermoplastic elastomer (TPO). This product has excellent low temperature impact properties and flow characteristics ..
Tensile Strength, Yield	17.2 MPa	2500 psi	ASTM D638
A. Schulman POLYTROPE™ TPP 503 Injection Molding Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 503 is an injection molding grade olefinic thermoplastic elastomer. This product is recommended for parts requiring flexibility and high impact strength at sub-ambient temp..
Tensile Strength, Yield	17.2 MPa	2490 psi	ASTM D638
Eastman Tenite 485E3720023 Butyrate Clear, Trsp Tenite cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gloss, clarity, and a warm feel. The mechanical properties of Tenite cellulosi..
Tensile Strength, Yield	17.2 MPa	2500 psi	ISO 527-1/2
CTC X-PRO CTC PP 4025 Polypropylene Copolymer X-PRO PP 4025 is a high value polypropylene copolymer. It has applications in general purpose industrial, housewares, and construction.Data provided by Composite Technologies (CTC).
Tensile Strength, Yield	17.2 MPa	2500 psi	ASTM D638
ExxonMobil LL 8555.25 Rotational Molding Resin Product Description: LL 8555 is a linear low density hexene copolymer designed to offer superior processability, excellent dimensional control, whiteness and low warpage. This resin is ideally suite..
Tensile Strength, Yield	17.2 MPa	2500 psi	2.0 in/min; ASTM D638
ExxonMobil LLP8555.24 Rotational Molding Resin Product Description: LL 8555 is a linear low density hexene copolymer designed to offer superior processability, excellent dimensional control, whiteness and low warpage. This resin is ideally suite..
Tensile Strength, Yield	17.2 MPa	2500 psi	2.0 in/min; ASTM D638
ExxonMobil LLP8555.25 Rotational Molding Resin Product Description: LL 8555 is a linear low density hexene copolymer designed to offer superior processability, excellent dimensional control, whiteness and low warpage. This resin is ideally suite..
Tensile Strength, Yield	17.2 MPa	2500 psi	ASTM D-638
Axiall 8805 Moldings & Extrusions Flexible PVC General purpose clear extrusion compound with good low temperature properties.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013.
Tensile Strength, Yield	17.2 MPa	2500 psi	ASTM D-638
Axiall 02540 Plenum Flexible PVC Non-lead stabilized Category 3 plenum jacket.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013.
Tensile Strength, Yield	17.2 MPa	2500 psi	ASTM D-638
Axiall 1131-57D Wire & Cable Flexible PVC Non-lead stabilized 105°C rated jacket compound.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013.
Tensile Strength, Yield	17.2 MPa	2500 psi	ASTM D-638
Axiall 22830 Coax & Telecom/Moldings & Extrusions Flexible PVC Non-lead stabilized, 75C rated jacketing compound suitable for CATV, CM, CL2 type applications. UL recognized for 94 V-0 in all colors at 1.5 mm. QMFZ2 recognized component.Information provided by..
Tensile Strength, Yield	17.2 MPa	2500 psi	ASTM D-638
Axiall 8881 Moldings & Extrusions Flexible PVC Profile extrusion compound especially formulated to impart a matte surface appearance to the finished article.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013.
Tensile Strength, Yield	17.2 MPa	2500 psi	ASTM D638
Asahi Kasei Thermofil P-9900-0576 Unreinforced, Flame Retardant, Heat Stabilized Information provided by Asahi Thermofil
Tensile Strength, Yield	17.2 MPa	2500 psi	ASTM D-638
Axiall 18860 Wire & Cable Flexible PVC Flame retardant jacketing compound recommended for a maximum service temperature rating of 105°C.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013.
Tensile Strength, Yield	17.2 MPa	2490 psi	Type IV, 510 mm/min; ASTM D638
PolyOne Geon™ Vinyl Wire & Cable W1100 Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne
Tensile Strength, Yield	17.2 MPa	2490 psi	Type IV, 510 mm/min; ASTM D638
PolyOne Syncure™ System S110FV-UV Polyethylene, Crosslinked (XLPE) Syncure™ systems are two part moisture crosslinkable insulation compounds. S110FV-UV is a UL bulletinized, RoHS compliant, high strength, highly flame retardant insulation compound. Available in bl..
Tensile Strength, Yield	17.2 MPa	2500 psi	Longitudinal
Saint-Gobain Norton® Fluorglas® Chemfilm® R128/R129 Premium Grade Extruded Full Density PTFE Film (0.002" thick) Description: Full Density Unsintered Tape is used as primary insulation for high-temperature wires, jackets and cables and wall for convoluted hose. It meets the requirements of component insulation..