PolyOne Syncure™ System S110FV-UV Polyethylene, Crosslinked (XLPE)

Category	Polymer , Thermoplastic , Polyethylene (PE)
Manufacturer	PolyOne Corporation
Trade Name	Syncure™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne Syncure™ System S110FV-UV Polyethylene, Crosslinked (XLPE).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Syncure™ systems are two part moisture crosslinkable insulation compounds. S110FV-UV is a UL bulletinized, RoHS compliant, high strength, highly flame retardant insulation compound. Available in black and natural colorable versions. S110FV-UV is suitable for UL4703 photovoltaic wire insulation not requiring an outer jacket.NOTE: The above represents Typical Properties measured on 14 AWG with 30 mil wall. STORAGE AND HANDLING: Use S-1060A within 48 hours once package is open to avoid self-curing and scrap.Information provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	1.29 g/cc	1.29 g/cc	ASTM D792
Deformation	3.0 % @Temperature 131 °C, Time 3600 sec	3.0 % @Temperature 268 °F, Time 1.00 hour	500 g; UL 1581

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	50	50	10 sec; ASTM D2240
	54	54	ASTM D2240
Tensile Strength, Yield	17.2 MPa	2490 psi	Type IV, 510 mm/min; ASTM D638
Elongation at Break	400 %	400 %	Type IV, 510 mm/min; ASTM D638

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	90.0 °C	194 °F	UL Temperature Rating
Oxygen Index	27 % @Thickness 1.91 mm	27 % @Thickness 0.0752 in	ASTM D2863

Electrical Properties	Metric	English	Comments
Dielectric Constant	2.54 @Frequency 1.00e+6 Hz	2.54 @Frequency 1.00e+6 Hz	ASTM D150
Dielectric Strength	39.0 kV/mm	991 kV/in	ASTM D149
Dissipation Factor	0.0028 @Frequency 1.00e+6 Hz	0.0028 @Frequency 1.00e+6 Hz	ASTM D150

Descriptive Properties	Value	Comments
Agency Ratings	UL 44
	UL 4703
	UL VW-1
	USE 2
Appearance	Black
	Natural Color
Catalyst Masterbatch	50%	V-0044G-UV Natural or Black
Features	Flame Retardant
	Low Temperature Resistant
	Oil Resistant
	Sunlight Resistant (720 hours)
Flame Test	Pass	UL 1581; Vertical
Forms	Pellets
Gel Content	60%	ASTM D2765; Crosslinked PE, Method B (NonReferee Test)
Generic Material	XLPE
Generic Name	Polyethylene, Crosslinked (XLPE)
Grafted Base Resin	50%	S-1060A
Processing Method	Extrusion Coating
Regional Availability	North America
Retention of Tensile Elongation	94%	121°C, 1.91 mm; 336 hr, UL Standard
Retention of Tensile Strength	100%	121°C, 1.91 mm; 336 hr, UL Standard
Uses	Insulation
	Solar Panels
	Wire & Cable Applications
Wire Types	SIS
	XHH
	XHHW
	XHHW-2