Total Finathene® SR 572 HDPE blow molding (discontinued **)

Category	Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Blow Molding Grade
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Total Finathene® SR 572 HDPE blow molding (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

FINATHENE® SR 572 is a high density polyethylene produced by the slurry loop low pressure polymerization process. FINATHENE® SR 572 has been developed for the manufacturing of blow molded bottles for aggressive liquids and extrusion of thin sheets (< 5 mm). This new generation resin offers an optimal balance of processing and end-use characteristics in terms of resistance to environmental stress cracking and stiffness. FINATHENE® SR 572 is best processed at temperatures between 180 and 220°C.Information provided provided by Total Petrochemicals.Total Petrochemicals includes former Fina and Atofina plastics product lines.

Physical Properties	Metric	English	Comments
Density	0.957 g/cc	0.0346 lb/in³	ISO 1183
Environmental Stress Crack Resistance	100 hour	100 hour	ASTM D1693-70
Melt Flow	0.20 g/10 min @Load 2.16 kg	0.20 g/10 min @Load 4.76 lb	ISO 1133
High Load Melt Index	17 g/10 min @Load 21.6 kg	17 g/10 min @Load 47.6 lb	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	32.0 MPa	4640 psi	ISO 527
Tensile Strength, Yield	30.0 MPa	4350 psi	ISO 527
Elongation at Break	>= 700 %	>= 700 %	ISO 527
Elongation at Yield	9.0 %	9.0 %	ISO 527
Flexural Modulus	1.50 GPa	218 ksi	ISO 178
Tensile Impact Strength	85.0 kJ/m²	40.4 ft-lb/in²	Notched, -30°C; ISO 8256
	200 kJ/m²	95.2 ft-lb/in²	Notched, 23°C; ISO 8256

Thermal Properties	Metric	English	Comments
Vicat Softening Point	128 °C	262 °F	ISO 306

Descriptive Properties	Value	Comments
Food Approval	This material complies with the main regulations concerning non-toxicity of plastics materials in contact with food stuffs.