SABIC Innovative Plastics ULTEM AR9300 PEI (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics ULTEM AR9300 PEI (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% Glass fiber filled, standard flow Polyetherimide (Tg 217C). Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution. ECO Conforming.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.49 g/cc | 1.49 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0040 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 4.2 g/10 min @Load 6.60 kg, Temperature 337 °C |
4.2 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 155 MPa | 22500 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 8.96 GPa | 1300 ksi | 5 mm/min; ASTM D638 |
| Flexural Yield Strength | 241 MPa | 35000 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Modulus | 9.65 GPa | 1400 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Izod Impact, Notched | 1.17 J/cm | 2.19 ft-lb/in | ASTM D256 |
| 5.34 J/cm @Thickness 3.20 mm |
10.0 ft-lb/in @Thickness 0.126 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 212 °C @Thickness 6.40 mm |
414 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Glass Transition Temp, Tg | 217 °C | 423 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| FAA Flammability, FAR 25.853 A/B | NATURAL | FAR 25.853 |
| NBS Smoke Density, Flaming, Dmax | 5 | ASTM E 662 |
| NBS Smoke Density, Flaming, Ds 1.5 min | 0 | ASTM E 662 |
| NBS Smoke Density, Flaming, Ds 4 min | 5 | ASTM E 662 |
| OSU total heat release (2 minute test) | 5kW-min/m^2 | FAR 25.853 |
| OSU peak heat release rate (5 minute test) | 40kW/m^2 | FAR 25.853 |
| Vertical Burn a (60s) passes at | 0sec | FAR 25.853 |
| Vertical Burn b (12s) passes at | 0sec | FAR 25.853 |
Users viewing this material also viewed the following:
- Nye Lubricants 362F (RL) Synthetic Oil
- Universal Wire Works No. 21 Cobalt Alloy Welding Wire
- Zhejiang Juner PA66-301-G20 Flame-Retardant & Glass Reinforced, Environmental PA66
- ConocoPhillips Hydroclear® MV100 AW Hydraulic Fluid
- Addiplast Addilene H 220 T20 Polypropylene Homopolymer
- ATI Allegheny Ludlum Stainless Steel Type 201L, 10% Cold Work (UNS S20103)
- Arlon 51986RA020 0.020" Cured/Uncured Silicone Rubber with Fiberglass Substrate
- Beijing Ranger Chem PBT-201-G25 272 Flame Retarding FR PBT
- Resinlab® UR3005 Clear Two Part Urethane Elastomer
- Sumitomo Bakelite North America FM 4017F Fiberglass and Mineral Reinforced Phenolic
Copyright © lookpolymers.com All Rights Reserved