Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 39.0 MPa | 5660 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Cycolac® MG37EPX ABS (Europe-Africa-Middle East) ABS plating grade optimized for a broad processing window for both painted and plated applications. |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Cycolac® MG8000SR ABS This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Cycolac® MG8000SR ABS (Asia Pacific) This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | ASTM D638 |
SABIC Innovative Plastics LNP FARADEX AS002 ABS LNP* Faradex* AS002 is a compound based on Acrylonitrile Butadiene Styrene resin containing 10% Stainless Steel. Added features of this material include: Electrically Conductive, EMI/RFI Shielding... |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics Geloy FXTW30CP ASA Pearlescent GELOY ASA resin with copper-look for capstock extrusion. Outstanding weatherability.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® HFD4271 PC (Asia Pacific) Lexan* HFD4271 is a 10% glass filled, high flow, impact modified, injection moldable grade designed for high flow and superior surface appearance. HFD4271 has enhanced mold release, impact ductility.. |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP AL001 ABS LNP LUBRICOMP* AL-4010 HP is a compound based on Acrylonitrile Butadiene Styrene resin containing 5% PTFE. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | ASTM D638 |
LG Chemical HI855H PMMA, Impact Resistant Grade Molding granule designed for greater impact strength combined with the outstanding properties of conventional acrylic materialsFeatures: Excellent transparency and eleganceWeather resistance and che.. |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL PX6120 PPE+PS (Asia Pacific) Noryl PX6120 is an unfilled material with good flow, high Impact and chemical resistance against cleaners. Noryl PX6120 is developed for personal care appplications. |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP DL004 PC LNP* Lubricomp* DL004 is a compound based on Polycarbonate resin containing 20% PTFE. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP KP004 Acetal LNP LUBRICOMP* KP004 is a compound based on Acetal Copolymer resin containing 20% PTFE/Silicone. Added feature of this material is: Wear Resistant. |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP KP004 Acetal Copolymer (Europe-Africa-Middle East) LNP* Lubricomp* KP004 is a compound based on Acetal Copolymer resin containing PTFE, Silicone. |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP KX06415 Acetal Copolymer LNP LUBRICOMP* KX06415 is a compound based on Acetal Copolymer resin containing 10% PTFE, 10% Aramid Powder. Added features of this material include: Easy Molding, Heat Stabilized, Wear Resistant. |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® 364 PBT+PC Designed for outdoor telecommunications enclosure applications. |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP 4X08423 FP-P (PFA) LNP* THERMOCOMP* 4X08423 is a compound based on PFA resin containing Glass Fiber. |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | 0.2 in/min; ASTM Test |
Styrolution Terblend® N NM-12 ABS/PA6 (Dry) Terblend N NM-12 is an ABS/PA6 blend combining high impact strength and rigidity with an excellent processability and surface appearance.Information provided by STYROLUTION, which is a joint venture.. |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL PX1007 PPE+PS Noryl* PX1007 is an unfilled non-chlorinated, non-brominated flame retardant PPE/HIPS grade. |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP MF001AS PP LNP* THERMOCOMP* MF001AS is a compound based on Polypropylene resin containing 5% Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOTUF MF004AI PP (Asia Pacific) LNP* Thermotuf* MF004AI is a compound based on Polypropylene resin containing Glass Fiber. Added features of this material include: High Impact. |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | 50mm/min; ASTM D638 |
Denka TH-23 Transparent Resin Polymer (MBS resin) Polymethacrylate Butadiene Styrene "TX Polymer" (methyl methacrylate styrene), MS resins as an alternative to acrylic resins, with low density, low moisture absorption, and good moldability, "TH Polymer/TP Polymer," MBS resins with a.. |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | 50 mm/min; ISO 527 |
Chi Mei Wonderloy® PC-345 PC/ABS Alloy High Flow |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | ISO R 527 |
Fainplast Compounds ARC 20 Rigid PVC, Atoxic for General Purpose Bottles medium/high antishock |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | ASTM D638 |
Arkema Group OREVAC® 18707 Grafted Maleic Anhydride Polypropylene OREVAC 18707 is a maleïc anhydride modified PP based resin. It is available in pellet form for use in conventional extrusion and coextrusion equipment designed to process polyolefins. OREVAC 18707 .. |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | ISO 527-1 |
Barlog Plastics KEBAFLEX P D72.1 Polyester-Elastomer, Shore D75 TPC-ETInformation provided by BARLOG plastics GmbH. |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | ASTM D638 |
Asahi Glass Fluon® P-802UP PFA Perfluoropolymer Fluon® PFA is a copolymer of tetrafluoroethylene (C2F4) and perfluoroalkoxyethylene, which has excellent chemical, electrical, mechanical and surface properties. PFA retains many inherent character.. |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | ISO 527-2 |
Ascend Performance Materials Vydyne® 41 Nylon 66, Conditioned Vydyne® 41 is a general-purpose, impact-modified PA66 resin. Available in natural, it is recognized for all the processing and property advantages inherent to PA66 with the addition of improved imp.. |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | ISO 527-2 |
Ascend Performance Materials Vydyne® 41H BK03 Nylon 66, Impact Modified, Conditioned Vydyne® 41H BK03 is a general-purpose, impact-modified PA66 resin. Available in black, it is heat-stabilized for improved resistance to elevated temperatures. The heat stabilization package for Vyd.. |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | JIS K6891 |
Asahi Glass Fluon® G350 PTFE Granular Powder Fluon®PTFE granular powders (molding powders) are used for the production of sheets, rods, billets and other general moldings.Information provided by Asahi Glass Company, Inc. |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Cycolac® DL100LG ABS (Europe-Africa-Middle East) Cycolac DL100LG is a low gloss, high heat, high impact ABS/PC blend with low emission |
|||
Tensile Strength at Break | 39.0 MPa | 5660 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® HFD4271 PC (Europe-Africa-Middle East) Lexan* HFD4271 is a 10% glass filled, high flow, impact modified, injection moldable grade designed for high flow and superior surface appearance. HFD4271 has enhanced mold release, impact ductility.. |