SABIC Innovative Plastics Cycolac® MG8000SR ABS (Asia Pacific)

Category	Polymer , Thermoplastic , ABS Polymer
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	Cycolac®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics Cycolac® MG8000SR ABS (Asia Pacific).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

This data was supplied by SABIC-IP for the Asia Pacific region.

Physical Properties	Metric	English	Comments
Specific Gravity	1.06 g/cc	1.06 g/cc	ASTM D 792
Density	1.07 g/cc	0.0387 lb/in³	ISO 1183
Linear Mold Shrinkage, Flow	0.0040 - 0.0070 cm/cm @Thickness 3.20 mm	0.0040 - 0.0070 in/in @Thickness 0.126 in	SABIC Method
Melt Flow	25 g/10 min @Load 10.0 kg, Temperature 220 °C	25 g/10 min @Load 22.0 lb, Temperature 428 °F	ASTM D 1238
	25 g/10 min @Load 10.0 kg, Temperature 220 °C	25 g/10 min @Load 22.0 lb, Temperature 428 °F	[cm^3/10 min] Melt Volume Rate; ISO 1133
	33 g/10 min @Load 5.00 kg, Temperature 260 °C	33 g/10 min @Load 11.0 lb, Temperature 500 °F	[cm^3/10 min] Melt Volume Rate; ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell L	87	87	ISO 2039-2
Hardness, H358/30	100 MPa	14500 psi	ISO 2039-1
Hardness, Shore D	78	78	ASTM D 2240
Tensile Strength at Break	34.0 MPa	4930 psi	Type I, 5 mm/min; ASTM D 638
	35.0 MPa	5080 psi	5 mm/min; ISO 527
	37.0 MPa	5370 psi	Type I, 50 mm/min; ASTM D 638
	39.0 MPa	5660 psi	50 mm/min; ISO 527
Tensile Strength, Yield	50.0 MPa	7250 psi	5 mm/min; ISO 527
	51.0 MPa	7400 psi	Type I, 5 mm/min; ASTM D 638
	56.0 MPa	8120 psi	50 mm/min; ISO 527
	56.0 MPa	8120 psi	Type I, 50 mm/min; ASTM D 638
Elongation at Break	8.0 %	8.0 %	50 mm/min; ISO 527
	9.0 %	9.0 %	Type I, 50 mm/min; ASTM D 638
	10 %	10 %	Type I, 5 mm/min; ASTM D 638
	10 %	10 %	5 mm/min; ISO 527
Elongation at Yield	2.8 %	2.8 %	Type I, 5 mm/min; ASTM D 638
	2.8 %	2.8 %	5 mm/min; ISO 527
	3.0 %	3.0 %	50 mm/min; ISO 527
	3.0 %	3.0 %	Type I, 50 mm/min; ASTM D 638
Tensile Modulus	2.60 GPa	377 ksi	1 mm/min; ISO 527
	2.65 GPa	384 ksi	5 mm/min; ASTM D 638
	2.67 GPa	387 ksi	50 mm/min; ASTM D 638
Flexural Yield Strength	77.0 MPa	11200 psi	1.3 mm/min, 50 mm span; ASTM D 790
	80.0 MPa	11600 psi	2 mm/min; ISO 178
Flexural Modulus	2.60 GPa	377 ksi	1.3 mm/min, 50 mm span; ASTM D 790
	2.70 GPa	392 ksi	2 mm/min; ISO 178
Izod Impact, Notched	0.600 J/cm @Temperature -30.0 °C	1.12 ft-lb/in @Temperature -22.0 °F	ASTM D 256
	0.800 J/cm @Temperature 23.0 °C	1.50 ft-lb/in @Temperature 73.4 °F	ASTM D 256
Izod Impact, Notched (ISO)	7.00 kJ/m² @Temperature -30.0 °C	3.33 ft-lb/in² @Temperature -22.0 °F	80104; ISO 180/1A
	12.0 kJ/m² @Temperature 23.0 °C	5.71 ft-lb/in² @Temperature 73.4 °F	80104; ISO 180/1A
Charpy Impact, Notched	0.800 J/cm² @Temperature -30.0 °C	3.81 ft-lb/in² @Temperature -22.0 °F	V-notch Edgew 80104 sp=62mm; ISO 179/1eA
	1.30 J/cm² @Temperature 23.0 °C	6.19 ft-lb/in² @Temperature 73.4 °F	V-notch Edgew 80104 sp=62mm; ISO 179/1eA
Impact Test	10.0 J	7.38 ft-lb	Multiaxial Impact; ISO 6603
	25.0 J @Temperature 23.0 °C	18.4 ft-lb @Temperature 73.4 °F	Instrumented Impact Total Energy; ASTM D 3763

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	87.0 µm/m-°C @Temperature -40.0 - 40.0 °C	48.3 µin/in-°F @Temperature -40.0 - 104 °F	ASTM E 831
	87.0 µm/m-°C @Temperature -40.0 - 40.0 °C	48.3 µin/in-°F @Temperature -40.0 - 104 °F	ISO 11359-2
CTE, linear, Transverse to Flow	85.0 µm/m-°C @Temperature -40.0 - 40.0 °C	47.2 µin/in-°F @Temperature -40.0 - 104 °F	ASTM E 831
	85.0 µm/m-°C @Temperature -40.0 - 40.0 °C	47.2 µin/in-°F @Temperature -40.0 - 104 °F	ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi)	87.0 °C	189 °F	Flatw 80104 sp=64mm; ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi)	77.0 °C	171 °F	Flatw 80104 sp=64mm; ISO 75/Af
	83.0 °C @Thickness 3.20 mm	181 °F @Thickness 0.126 in	unannealed; ASTM D 648
Vicat Softening Point	89.0 °C	192 °F	Rate B/50; ASTM D 1525
	91.0 °C	196 °F	Rate B/50; ISO 306
	92.0 °C	198 °F	Rate B/120; ISO 306
	98.0 °C	208 °F	Rate A/50; ISO 306
Flammability, UL94	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in	UL 94 by SABIC-IP

Descriptive Properties	Value	Comments
Pencil Hardness test, 1kgf	HB	ASTM D 3363