Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 34.0 MPa | 4930 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Cycolac® MG38 ABS (Europe-Africa-Middle East) Very high impact ABS. Toughness/rigidity. Good fatigue resistance. |
|||
Tensile Strength at Break | 34.0 MPa | 4930 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Cycolac® MG38N ABS (Asia Pacific) Very high impact ABS. Toughness/rigidity. Good fatigue resistance. NSF Standard 61 certified in limited colors (restrictions may apply)> |
|||
Tensile Strength at Break | 34.0 MPa | 4930 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Geloy XTWM200 ASA (Asia Pacific) ASA resin for injection molding. Excellent flow, colorability and outdoor weathering capability.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Tensile Strength at Break | 34.0 MPa | 4930 psi | |
Plastcom SLOVALEN PH 92 T 30 PP, 30% mineral filling FeaturesModified PP for injection moulding with the content of 30% mineral filling. Increased rigidity, strength and thermal. Decreased shrinkage. General application in all industry branches.Packag.. |
|||
Tensile Strength at Break | <= 34.0 MPa | <= 4930 psi | ISO/R527 |
Polykemi AB POLYfill PPH T15020 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | 34.0 MPa @Temperature 23.0 °C |
4930 psi @Temperature 73.4 °F |
50 mm/min; ASTM D638 |
Solvay Specialty Polymers Halar® 1450LC Polyethylene, Chlorotrifluoroethylene (ECTFE)
(Unverified Data**) Information provided by Solvay Specialty Polymers. |
|||
Tensile Strength at Break | 34.0 MPa | 4930 psi | Sintered Sheet; ISO 12086 |
3M Dyneon™ TFM™ 2001 PTFE
(discontinued **) Processable by standard paste extrusion methodRecommended for high performance applications with reduction ratios up to 1000:1Provides denser polymer structure with fewer micro voids and lower gas p.. |
|||
Tensile Strength at Break | 34.0 MPa | 4930 psi | ISO 37 |
Huntsman AVALON® 98 AE Thermoplastic Polyurethane Introduction: AVALON 98 AE is a general purpose polyester based thermoplastic polyurethane for injection molding. AVALON 98 AE is part of the AVALON Perform Range and offers a premium soiling materi.. |
|||
Tensile Strength at Break | 34.0 MPa | 4930 psi | ISO 527 |
FKuR Kunststoff Fibrolon® F 8530 Biodegradable Wood-Plastic Compound, Fiber Reinforced FIBROLON® are fiber reinforced compounds. Depending on specific customer requirements either a biodegradable polymer or a polyolefin can be used as the polymeric matrix. With the brand name of F.. |
|||
Tensile Strength at Break | 34.0 MPa | 4930 psi | ISO 37 |
Huntsman AVALON® 92 AB Thermoplastic Polyurethane Introduction: AVALON 92 AB is a high performance polyester based thermoplastic polyurethane for injection molding. AVALON 92 AB is part of the AVALON Performance Range and offers a premium soling ma.. |
|||
Tensile Strength at Break | 34.0 MPa | 4930 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP AX08306 ABS LNP* THERMOCOMP* AX08306 is a compound based on ABS resin containing Proprietary Filler(s). Added feature of this grade is: Platable. |
|||
Tensile Strength at Break | 34.0 MPa | 4930 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP HX03408 PA11 LNP* Thermocomp* HX03408 is a compound based on Nylon 11 containing Proprietary Fillers. Added feature includes: Clean Compound System |
|||
Tensile Strength at Break | 34.0 MPa | 4930 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP MX06402H PP LNP* THERMOCOMP* MX06402H is a compound based on Polypropylene resin containing 20% Glass Fiber. Added features of this material include: Heat Stabilized, Low Extractable. |
|||
Tensile Strength at Break | 34.0 MPa | 4930 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP MF002AS PP LNP THERMOCOMP* MF002AS is a compound based on Polypropylene resin containing 10% Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
Tensile Strength at Break | 34.0 MPa | 4930 psi | Crosshead speed 100 mm/min; ISO 527 |
SCG Chemicals EL-Leneâ„¢ H5211P High Density Polyethylene Pipe Resin Key Characteristics: Good processing, high thermal stabilityRecommended Applications: Water pipes, conduit, sewage drainage pipesInformation provided by SCG Chemicals |
|||
Tensile Strength at Break | 34.0 MPa | 4930 psi | ISO 527 |
Total HP 401 MDPE, pipe, cable, sheet FINATHENE® HP 401 is a polyethylene copolymer based on C6 hexene as co-monomer and is produced by a continuous low-pressure slurry polymerization process. FINATHENE® HP 401 is a black high densit.. |
|||
Tensile Strength at Break | 34.0 MPa | 4930 psi | ISO 527-1/-2 |
DuPont Performance Polymers Hytrel® 4556 Polyester Elastomer TPC-ET
(Unverified Data**) 45 Shore D High Performance Polyester ElastomerInformation provided by DuPont Performance Polymers |
|||
Tensile Strength at Break | 34.0 MPa | 4930 psi | ISO R 527 |
Fainplast Compounds RE 116 Rigid PVC, Extrusion Small tubes for shoes |
|||
Tensile Strength at Break | 34.0 MPa | 4930 psi | 50 mm/min; ISO 527 |
Chi Mei Polylac® PA-756H ABS - High Flow Super high flow |
|||
Tensile Strength at Break | 34.0 MPa | 4930 psi | 50 mm/min; ISO 527 |
Chi Mei Polylac® PA-777B ABS - High Heat High Heat Impact |
|||
Tensile Strength at Break | 34.0 MPa | 4930 psi | ASTM D638 |
Azdel SuperLite® SL551800-100 PP Resin Matrix / 55% Glass Fiber (4 mm Molded Thickness) AZDEL SuperLite® SL551800-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |
|||
Tensile Strength at Break | 34.0 MPa | 4930 psi | |
AorTech Biomaterials ECSil™ 90A Biomedical Carbonate Silicone Pellets Elast-Eon™ Carbonate Silicone (ECSil™) is a family of next generation biomedical polymers. ECSil™ is finding strong interest in cardiac pacing leads, orthopaedics, spinal discs, and generally an.. |
|||
Tensile Strength at Break | 34.0 MPa | 4930 psi | ASTM D638 |
3M Dyneon™ PFA FLEX 8515 UHPZ Perfluoroalkoxy Fluorothermoplastic Granules Dyneon™ PFA-FLEX UHP family exhibits improved environmental stress crack resistance to stress cracking agents such as fluorsurfactants and fluorosurfactant-containing chemicals. In addition, this f.. |
|||
Tensile Strength at Break | 34.0 - 40.0 MPa | 4930 - 5800 psi | ASTM D638 |
Arkema Group KYNAR FLEX® 3120-15 Polyvinylidene Fluoride Copolymer - Extrusion & Molding Characteristics: Natural resin - translucent, off-white hemispheres. Flexible, flame and smoke suppressant. High stability in harsh thermal, chemical and ultraviolet environments. High toughness.. |
|||
Tensile Strength at Break | 34.0 - 55.0 MPa | 4930 - 7980 psi | ASTM D638 |
Arkema Group KYNAR® 740 Black/Red Polyvinylidene Fluoride Homopolymer - Injection Molding and Extrusion Characteristics: Pigmented. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechanical strength, low permeability, abrasion resistance; high purityAppli.. |
|||
Tensile Strength at Break | 34.0 - 55.0 MPa | 4930 - 7980 psi | ASTM D638 |
Arkema Group KYNAR® 740 Polyvinylidene Fluoride Homopolymer - Injection Molding and Extrusion Characteristics: Natural resin - translucent, off-white hemispheres. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechanical strength, low permeabili.. |
|||
Tensile Strength at Break | 34.0 MPa | 4930 psi | |
AorTech Biomaterials Elast-Eon™ E2-862 Biomedical Polyurethane Pellets Elast-Eon™ polymers are used in biomedical applications. They have high biostability so they can be used for long term implantation. |
|||
Tensile Strength at Break | 34.0 MPa | 4930 psi | DIN EN ISO 527-3 |
3M Dyneon™ TF 2025Z PTFE Fine Powder Dyneon™ TF 2025 Z PTFE is an ideal grade for pipe liner applications in chemical plant construction due to high green strength.Product Features:High molecular weightFine powder grade for low to med.. |
|||
Tensile Strength at Break | 34.0 MPa | 4930 psi | Sintered Molding; DIN 53455 (film, 0.2mm) |
3M Dyneon™ TFM™ 1630 PTFE
(discontinued **) Semi-free-flowing resin for convenient handlingHigh bulk density leading to more economical processingVery dense polymer structure; low permeabilityGood electrical and mechanical propertiesSmoother .. |
|||
Tensile Strength at Break | 34.0 MPa | 4930 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics GELOY CR7520 ASA (Asia Pacific) ASA copolymer. Automotive grilles and exteriors. Excellent weatherability, good flow/aesthetics and high impact. Rated f2 by UL. |