3M Dyneon™ TFM™ 1630 PTFE (discontinued **)

Category	Polymer , Thermoplastic , Fluoropolymer , PTFE
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	3M Dyneon™ TFM™ 1630 PTFE (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Semi-free-flowing resin for convenient handlingHigh bulk density leading to more economical processingVery dense polymer structure; low permeabilityGood electrical and mechanical propertiesSmoother surfacesSubstantially lower deformation under loadImproved weldabilityInformation provided by Dyneon, A 3M Company

Physical Properties	Metric	English	Comments
Specific Gravity	2.16 g/cc	2.16 g/cc	@ 23°C, Sintering Molding; ASTM D4894-98a
Bulk Density	0.840 g/cc	0.0303 lb/in³	ASTM D4894-98a
Particle Size	200 µm	200 µm	average; ASTM D4894-98a
Deformation	4.0 %	4.0 %	2175 psi - permanent, 23°C, Sintering Molding; ASTM D621
	8.0 %	8.0 %	2175 psi - 24 hrs, 23°C, Sintering Molding; ASTM D621
	9.0 %	9.0 %	2175 psi - 100 hrs, 23°C, Sintering Molding; ASTM D621

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	29.0 MPa	4210 psi	Sintered Molding; ASTM D4894-98a
	34.0 MPa	4930 psi	Sintered Molding; DIN 53455 (film, 0.2mm)
Elongation at Break	400 %	400 %	Sintered Molding; ASTM D4894-98a
	620 %	620 %	Sintered Molding; DIN 53455 (film, 0.2mm)
Tensile Modulus	0.648 GPa	94.0 ksi	Sintered Molding; ASTM D638

Thermal Properties	Metric	English	Comments
Melting Point	317 - 337 °C	603 - 639 °F	second; ASTM D4894-98a
	332 - 352 °C	630 - 666 °F	initial; ASTM D4894-98a
Maximum Service Temperature, Air	260 °C	500 °F
Minimum Service Temperature, Air	-200 °C	-330 °F
Flammability, UL94	V-0	V-0
Shrinkage	4.00 % @Temperature 23.0 °C	4.00 % @Temperature 73.4 °F	Sintering Moldings; ASTM D4894-98a

Electrical Properties	Metric	English	Comments
Dielectric Strength	106.3 kV/mm	2700 kV/in	ASTM D149-95a