3M Dyneon™ TFM™ 2001 PTFE (discontinued **)

Category	Polymer , Thermoplastic , Fluoropolymer , PTFE
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	3M Dyneon™ TFM™ 2001 PTFE (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Processable by standard paste extrusion methodRecommended for high performance applications with reduction ratios up to 1000:1Provides denser polymer structure with fewer micro voids and lower gas permeability than standard PTFE fine powder gradesProvides smooth surface, high transparency and weldability in the finished productImparts isotropic mechanical properties, high stress-crack resistance, improved flex life, and high pressure resistance under surge stressInformation provided by Dyneon, A 3M Company

Physical Properties	Metric	English	Comments
Bulk Density	0.450 g/cc	0.0163 lb/in³	ISO 12086
Density	2.15 g/cc	0.0777 lb/in³	Sintered Sheets; ISO 12086
Particle Size	500 µm	500 µm	average; ISO 12086
Thickness	63.0 microns	2.48 mil	ASTM D4895

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	34.0 MPa	4930 psi	Sintered Sheet; ISO 12086
Elongation at Break	400 %	400 %	ASTM D4895

Descriptive Properties	Value	Comments
Extrusion Pressure	26 MPa	reduction ratio 400, ASTM D4894
Reduction Ratio Range	20-1000:1	Dyneon Method