Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 33.1 MPa | 4800 psi | 2 in/min; ASTM D638 |
RheTech Products M12P100-01 12% Mica Reinforced Polypropylene, Black Applications: Fan shroudsAir ductsFiller panelsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 33.1 MPa | 4800 psi | 2 in/min; ASTM D638 |
RheTech Products T10P100-00 10% Talc Reinforced Polypropylene, Natural Applications: Consumer goodsIP structural componentsInterior trimInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 33.1 MPa | 4800 psi | 2 in/min; ASTM D638 |
RheTech Products T10P100-01 10% Talc Reinforced Polypropylene, Black Applications: Consumer goodsAir ductsUnderhood componentsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 33.1 MPa | 4800 psi | 2 in/min; ASTM D638 |
RheTech Products T10UP100-01 10% Talc Reinforced Polypropylene Copolymer, General Purpose Black, UL94 HB Rated Applications: Wire troughElectrical componentsConsumer goodsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 33.1 MPa | 4800 psi | TM R050-36 |
Resinlab® EP1325 Thixotropic, Heat Curing Epoxy Adhesive Resinlab™ EP1325 and EP1325LV are one part thixotropic, heat curing epoxy adhesives. They can also be used as a small mass potting compounds, staking or damming adhesives, or polymer systems where .. |
|||
Tensile Strength at Break | 33.1 MPa | 4800 psi | 2 in/min; ASTM D638 |
RheTech Products HP506-01A 21% Talc Reinforced High Performance Polypropylene, UV Stabilized, Black Applications: Automotive interior applicationsHVAC ductsTail lamp housingsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 33.1 MPa | 4800 psi | ASTM D638 |
Albis Plastics Cellulose Acetate CA700 , Unreinforced, 29% Plasticizer
(discontinued **) Amorphous Cellulose Acetate (CA)Characteristics: Chemical Resistance, Toughness, Strength, Hardness, Gloss, Clarity and "Feel"Applications: Tool Handles, Optical Products, Toys and Sheet ProductsPro.. |
|||
Tensile Strength at Break | 33.1 MPa | 4800 psi | |
Indium Corp. Indalloy 149 Tin-Lead Solder Alloy Information Provided by Indium Corporation |
|||
Tensile Strength at Break | 33.1 MPa | 4800 psi | |
Green Dot Terratek® SC 50 Polypropylene - Wheat Starch Biocomposite Terratek® SC 50 is a proprietary blend of wheat starch and polypropylene for injection molding applications. SC 50 contains 50% wheat starch by weight, however, a range of properties can be achie.. |
|||
Tensile Strength at Break | 33.1 MPa | 4800 psi | 2.0 in/min; ASTM D638 |
LTL Color Compounds ColorFast® PBA1000 PBT/ABS Alloy PBT/ABS alloy with excellent physical properties and chemical resistanceAll information provided by LTL Color Compounders, Inc. |
|||
Tensile Strength at Break | 33.1 MPa | 4800 psi | Type I, 51 mm/min; ASTM D638 |
Styron MAGNUMâ„¢ 357 HP Acrylonitrile Butadiene Styrene (ABS) Resin Overview: MAGNUMâ„¢ ABS resins are thermoplastic materials which provide an excellent balance of processability, impact resistance and heat resistance as imparted by the various polymer compositi.. |
|||
Tensile Strength at Break | 33.1 MPa | 4800 psi | ASTM D638 |
Techmer ES Plastiblend® ABS CR X BK Availability: North AmericaForms: PelletsFeatures: Good Chemical ResistanceUses: Electrical PartsAppearance: BlackInformation provided by TP Composites, Inc. |
|||
Tensile Strength at Break | 33.1 MPa | 4800 psi | transverse direction; ASTM D882 |
A. Schulman CP842-01 Hexene Copolymer LLDPE Resin DescriptionCP 842-01 is a Hexene copolymer LLDPE resin designed for use in blown film applications. Blow up ratios of2:1 or higher are recommended. ApplicationTypical applications of CP 842-01 incl.. |
|||
Tensile Strength at Break | 33.1 MPa | 4800 psi | transverse direction; ASTM D882 |
A. Schulman CP842-01 Hexene Copolymer LLDPE Resin DescriptionCP 842-01 is a Hexene copolymer LLDPE resin designed for use in blown film applications. Blow up ratios of2:1 or higher are recommended. ApplicationTypical applications of CP 842-01 incl.. |
|||
Tensile Strength at Break | 33.1 MPa | 4800 psi | transverse direction; ASTM D882 |
A. Schulman CP842-01 Hexene Copolymer LLDPE Resin DescriptionCP 842-01 is a Hexene copolymer LLDPE resin designed for use in blown film applications. Blow up ratios of2:1 or higher are recommended. ApplicationTypical applications of CP 842-01 incl.. |
|||
Tensile Strength at Break | 33.1 MPa | 4800 psi | ASTM D638 |
Chesterton ARC 897 Fine Grade Sliding Wear Compound Description: ARC 897 is an advanced ceramic reinforced composite for the repair and protection of all metal surfaces subjected to severe erosion, corrosion, and chemical attack. It is applied at a t.. |
|||
Tensile Strength at Break | 33.1 MPa | 4800 psi | ASTM D638 |
Eastman Tenite 360A4000012 Propionate Clear, Trsp Tenite cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gloss, clarity, and a warm feel. The mechanical properties if Tenite cellulosi.. |
|||
Tensile Strength at Break | 33.1 MPa | 4800 psi | ASTM D638 |
Eastman Tenite 360E3V45512 Propionate Water Clear, Trsp Tenite cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gloss, clarity, and a warm feel. The mechanical properties of Tenite cellulosi.. |
|||
Tensile Strength at Break | 33.1 MPa | 4800 psi | ASTM D638 |
ExxonMobil HDPE HPA 020 Wire & Cable High Density Polyethylene Resin Product Description: HPA 020 is a HDPE grade for Medium/High Voltage power cable jacketing. The grade should be used in blends with LLDPE to improve ESCR. Sufficient Carbon Black or UV stabilizer sh.. |
|||
Tensile Strength at Break | 33.1 MPa | 4800 psi | ASTM D638 |
Americas Styrenics STYRON® 404 High Impact Polystyrene Product CharacteristicsAdditive FreeTypical ApplicationsCompounding and masterbatchesInformation provided by AmericasStyrenics LLC. |
|||
Tensile Strength at Break | 33.1 MPa | 4800 psi | cured, grit-blasted steel; ASTM D2095 |
3M Scotch-Weld™ MG20 SF Medical Grade Instant Adhesive 3M™ Scotch-Weld™ Medical Grade Instant Adhesive are intended for use on a wide variety of materials used in the construction of disposable medical assemblies. They will quickly bond metals, plasti.. |
|||
Tensile Strength at Break | 33.1 MPa | 4800 psi | ASTM D4894 |
3M Dyneon™ TFM™ 1700 Modified PTFE Powder Type III, gr. 1 PTFE. Dyneon™ TFM™ 1700 PTFE is a second-generation modified polytetrafluoro-ethylene (PTFE) that maintains the exceptional chemical and heat resistance properties of first-genera.. |
|||
Tensile Strength at Break | 33.1 MPa | 4800 psi | ASTM D3574 |
3M Scotch® 3311 Foil Tape Scotch® Foil Tape 3311 is an aluminum alloy foil with a pressure-sensitive adhesive and paper liner. The aggressive rubber adhesive sticks well to most surfaces and the paper liner makes for conven.. |
|||
Tensile Strength at Break | 33.1 MPa | 4800 psi | TM R050-36 |
Resinlab® EP1285HD-10 Highly Filled, Medium Viscosity Casting Resin Resinlab™ EP1285 (Formerly Lab Product W021901 series) is a highly filled, medium viscosity black casting resin designed for applications requiring a high degree of thermal conductivity and a low C.. |
|||
Tensile Strength at Break | 33.1 MPa | 4800 psi | 2" (50mm) per min.; ASTM D638 Type IV |
Formosa Plastics Formolene® HP3902 Pipe HDPE Natural Medium Density Hexene CopolymerApplications: Pipe for gas distribution, oilfield and other industrial pipe, telecommunications conduit.Formolene HP3902 is a high performance copolymer that i.. |