LTL Color Compounds ColorFast® PBA1000 PBT/ABS Alloy
| Category | Polymer , Thermoplastic , ABS Polymer , ABS/Polyester Alloy , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | LTL Color Compounds |
| Trade Name | ColorFast® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LTL Color Compounds ColorFast® PBA1000 PBT/ABS Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PBT/ABS alloy with excellent physical properties and chemical resistanceAll information provided by LTL Color Compounders, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 33.1 MPa | 4800 psi | 2.0 in/min; ASTM D638 |
| Tensile Strength, Yield | 46.9 MPa | 6800 psi | 2.0 in/min; ASTM D638 |
| Elongation at Break | 35 % | 35 % | 2.0 in/min; ASTM D638 |
| Elongation at Yield | 7.0 % | 7.0 % | 2.0 in/min; ASTM D638 |
| Flexural Modulus | 2.07 GPa | 300 ksi | 2.0 in/min; ASTM D790 |
| Izod Impact, Notched | 0.854 J/cm @Temperature 22.8 °C |
1.60 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 204 - 238 °C | 400 - 460 °F | |
| Middle Barrel Temperature | 210 - 232 °C | 410 - 450 °F | |
| Front Barrel Temperature | 221 - 254 °C | 430 - 490 °F | |
| Nozzle Temperature | 216 - 249 °C | 420 - 480 °F | |
| Melt Temperature | 221 - 254 °C | 430 - 490 °F | |
| Mold Temperature | 10.0 - 71.1 °C | 50.0 - 160 °F | |
| Drying Temperature | 85.0 °C | 185 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour | nominal; maximum drying time of 8 hours |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | |
| Shot Size | 40 - 60 % | 40 - 60 % | |
| Vent Depth | 0.00254 - 0.00762 cm | 0.00100 - 0.00300 in | |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm |
Users viewing this material also viewed the following:
- Premix Premi-Glas® 2550® CR-SX Fiberglass Reinforced Thermoset SMC
- Quadrant EPP Fluorosint® HPV PTFE + additives, bearing grade, compression moulded (ISO Data)
- MarkeTech Strontium Titanate (SrTiO3) Single Crystal Substrate
- Mitsubishi Xantar® C CF 107 Polycarbonate/ABS Blend
- Taiwan PU Corporation PTMG CPU-167L Polyurethane Casting Elastomer
- SABIC Innovative Plastics ULTEM Foam XP080 PEI
- DSM Stanyl® TW200F3 Nylon 46-15% Glass Reinforced (European Grade) (Dry)
- Eurostar Starflam BFR552Y3 PA6, Mineral/Glass Fiber Filled, Flame Retardant, Injection Molded
- LNP Lubricomp® PDX-J-91198 Polyethersulfone, Proprietary Filler (discontinued **)
- LATI Lastane 50 G/25 PUR, 25% Glass Fiber Reinforced
Copyright © lookpolymers.com All Rights Reserved