- HOME
- POLYMER SEARCH
- Thermoplastic
- Polystyrene (PS)
- Polystyrene, Impact Modified
- Americas Styrenics STYRON® 404 High Impact Polystyrene
Americas Styrenics STYRON® 404 High Impact Polystyrene
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified |
| Manufacturer | Americas Styrenics LLC |
| Trade Name | STYRON® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Americas Styrenics STYRON® 404 High Impact Polystyrene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product CharacteristicsAdditive FreeTypical ApplicationsCompounding and masterbatchesInformation provided by AmericasStyrenics LLC.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0080 cm/cm | 0.0040 - 0.0080 in/in | ASTM D955 |
| Melt Flow | 2.3 g/10 min @Load 5.00 kg, Temperature 200 °C |
2.3 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 33.1 MPa | 4800 psi | ASTM D638 |
| Tensile Strength | 33.1 MPa | 4800 psi | ASTM D638 |
| Elongation at Break | 60 % | 60 % | ASTM D638 |
| Tensile Modulus | 1.93 GPa | 280 ksi | ASTM D638 |
| Flexural Strength | 42.7 MPa | 6200 psi | ASTM D790 |
| Flexural Modulus | 2.00 GPa | 290 ksi | ASTM D790 |
| Izod Impact, Notched | 0.747 J/cm | 1.40 ft-lb/in | compression molded; ASTM D256 |
| 0.854 J/cm | 1.60 ft-lb/in | injection molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 90.0 µm/m-°C | 50.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 93.3 °C | 200 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.8 °C | 181 °F | ASTM D648 |
| Vicat Softening Point | 106 °C | 222 °F | ASTM D1525 |
Users viewing this material also viewed the following:
- North Wood Plastics 60 HDPE + UNIFILL (20% Wood Fiber)
- Huntsman IROGRAN® CA116-201 TPU-Polyester
- Greene Tweed Avalon® 69 PTFE, Thermoplastic and Carbon Filled
- Heatbath/Park #900 High Speed Hardening Salt
- Solvay ANTAROX® BL 214 Surfactant
- SABIC Innovative Plastics LNP THERMOCOMP MF004S PP
- Total Lumicene® mPE M 2310 EP Metallocene Polyethylene, Blown Film
- Dow Corning SILASTIC® T-4 RTV SILICONE RUBBER BASE & T-4 O CURING AGENT
- A. Schulman ComAlloy Voloy® 683 Nylon 6/6, Glass Fiber/Bead Reinforced, Nylon 6/6 Alloy, Flame Retardant, UL
Copyright © lookpolymers.com All Rights Reserved