Techmer ES Plastiblend® ABS CR X BK
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | Techmer ES |
| Trade Name | Plastiblend® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Plastiblend® ABS CR X BK.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFeatures: Good Chemical ResistanceUses: Electrical PartsAppearance: BlackInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm @Thickness 3.17 mm |
0.0050 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 102 | 102 | ASTM D785 |
| Tensile Strength at Break | 33.1 MPa | 4800 psi | ASTM D638 |
| Elongation at Break | 2.4 % | 2.4 % | ASTM D638 |
| Flexural Strength | 64.8 MPa | 9400 psi | ASTM D790 |
| Flexural Modulus | 2.34 GPa | 340 ksi | ASTM D790 |
| Izod Impact, Notched | 2.40 J/cm @Thickness 3.17 mm |
4.50 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 90.0 µm/m-°C | 50.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 101 °C | 214 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 96.7 °C | 206 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® FXM141R PC
- DuPont Nucrel® 2906 Ethylene-Methacrylic Acid Copolymer Resin (discontinued **)
- Honeywell Capran® K Coated Nylon Film (discontinued **)
- ICO Polymers ICORENEâ„¢ 150-1501 HDPE Rotational Molding Resin
- LATI Latamid 66 H2E21 G/13 PA 66, 13% Glass Fiber Reinforced
- Haysite SDL® H261 Polyester, Static Dissipative
- Taiwan PU Corporation CPU-69-A/B Mixing Ratio 100/40 Polyurethane Casting Elastomer
- Tipco Tipcolite® TG 211 Phenolic Compound, Mineral & Wood Flour, Soft Flow & High Electrical Properties
- Polyram Polytron P30N01 Homopolymer Polypropylene, Chemically Coupled 30% Long Fiber
- SABIC Innovative Plastics LNP Thermocomp TX88477 PU
Copyright © lookpolymers.com All Rights Reserved