Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 165 MPa | 23900 psi | 5.1 mm/min; ASTM D638 |
PolyOne Edgetek® PS-30CF/000 HF UV BLACK Polybutylene Terephthalate (PBT) Information provided by PolyOne |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | d.a.m.; ISO 527-1, -2; 5 mm/min |
Lanxess Durethan® ECO BV 35 H2 900500 Nylon 6, 35% Glass Fiber PA 6, 35% glass fibers, injection molding, heat-ageing stabilized, contains 30% pre-consumer recycled materialInformation provided by LANXESS. |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | ISO 527 Type 1A |
Solvay TECHNYL® A 218 V40 PA66, 40% glass fiber, Conditioned Description: Polyamide PA66, reinforced with 40% of glass fiber, heat stabilized for injection molding.Available in: Asia Pacific, Europe and North AmericaProduct Applications: TECHNYL A 218 V40 is .. |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP OX97635 PPS LNP LUBRICOMP* OX97635 is a compound based on Polyphenylene Sulfide resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive, Wear Resistant. |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | ISO 527 Type 1A |
Solvay TECHNYLSTARâ„¢ SX 216 V60 PA6, 60% glass filled, Conditioned Description: TECHNYL STAR TM Polyamide reinforced with 60% of glass fiber, for injection molding. Characterized by a high fluidity of the melt.Available in: Europe and North America Product Applicat.. |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | ISO 527 Type 1A |
Solvay TECHNYLSTARâ„¢ SX 218 L2 V60 Black JA6A PA6, 60% glass filled, Conditioned Description: TECHNYLSTAR polyamide reinforced with 60% of glass fiber, heat and UV stabilized, characterized by a high fluidity of the melt, for injection molding.Available in: Europe Product Applic.. |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | ISO 527 Type 1A |
Solvay TECHNYLSTARâ„¢ SX 218 V60 Black Z PA6, 60% glass filled, Conditioned Description: TECHNYLSTAR Polyamide reinforced with 60% of glass fiber, heat stabilized, for injection molding. Characterized by a high fluidity of the melt. Available in: Asia Pacific, Europe and No.. |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics ULTEM 2310R PEI (Europe-Africa-Middle East) 30% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C) with internal mold release. Resin is RoHS compliant. UL94 V0 and 5VA listing. |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM 2410EPR PEI 40% Glass fiber filled, high flow Polyetherimide (Tg 217C) with internal mold release for enhanced electroplatability. ECO Conforming, UL94 V0 listing. |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM 2410EPR PEI (Europe-Africa-Middle East) 40% Glass fiber filled, high flow Polyetherimide (Tg 217C) with internal mold release for enhanced electroplatability. Resin is RoHS compliant. UL94 V0 listing. |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics ULTEM AR9300 PEI (Europe-Africa-Middle East) 30% Glass fiber filled, standard flow Polyetherimide (Tg 217C). Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution. |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics ULTEM HU2310 PEI 30% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP.. |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON EE003XXC PEI LNP STAT-KON* EE003XXC is a compound based on Polyetherimide resin containing 15% Carbon Fiber. Added features of this material include: Clean Compound System, Electrically Conductive. |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP RF0069S PA 66 LNP THERMOCOMP* RF0069S is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added features of this material include: Flame Retardant, Heat Stabilized. |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP RF006H PA 66 LNP THERMOCOMP* RF006H is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added feature of this grade is: Healthcare. |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | ISO 527-1/-2 |
Unitika B2040G50 PA66, 50% Glass Fiber Reinforced, Conditioned Information provided by Unitika Ltd. |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | ISO 527-93 |
Wellman Wellamid® GF33-66 22LH-NBK1 Nylon 66, 33% Glass Fiber Reinforced, General Purpose Grade All information provided by Wellman Engineered Resins. |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | ISO 527-93 |
Wellman Wellamid® MRGF1647-BK1 Nylon 66, 40% Mineral/Glass Fiber Reinforced All information provided by Wellman Engineered Resins. |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | 5 mm/min; ISO 527 |
CP-Polymer-Technik Wellamid® 6000 GV 30 HW 30% Glass Fiber Nylon 6, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | conditioned; ISO 527-1/-2 |
EMS-Grivory Grivory® HT2V-3H PA6T/66-GF30 Product description: Grivory HT2V-3H is a 30 % glass fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamde. Polymer designation acc. to ISO: .. |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | 5 mm/min; ISO 527 |
Eurostar Starflam AFR460B PA66, Glass Fiber Reinforced, Flame Retardant, Injection Molding Starflam AFR460B is a Flame Retardant, Glass Fiber Reinforced Polyamide 66, Injection Molding ResinInformation provided by Eurostar. |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | ISO 527 |
Eurotec® Tecomid® NB40 GR25 NL PA 6 25% glass fiber reinforced Excellent stiffness/toughness balanceHigh mechanical strengthVery good thermal stabilityExcellent flammability characteristicsGood electrical propertiesHigh wear resistance and low frictionVery good.. |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | ISO 527-1 |
Barlog Plastics KEBATER A9045 PBT, 45% glass fiber reinforced, improved surface quality, reduced warpage, food grade (PBT+X)-GF45Information provided by BARLOG plastics GmbH. |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | 5 [mm/min]; ISO 527-2/5 |
Akro-Plastic Akromid® B3 GF 30 RM-M (3016) PA 6 Dry, 30% Glass Filled In all, the construction relevant features show that the significantly reduced moisture absorption of AKROMID B3 GF 30 RM leads to increasing rigidities and strengths as already expected. Neverthele.. |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | DIN 53 455 |
Albis Plastics Tedur® P 9519 PPS, ~45% Glass Fiber (black only) Compounded Regrind and/or Production Scrap, Excellent Cost-Performance Ratio. Incandescent wire resistance (2 mm) is 960°C per VDE 0471 T1.2.Applications: Handles, Fixing ElementsProcessing: Injec.. |