Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | <= 155 MPa | <= 22500 psi | ISO/R527 |
Polykemi AB SCANMID 6 B12^ F25 Nylon 6, Glass Fiber Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | 155 MPa | 22500 psi | |
Radici Radilon® S RV250 (dry) Nylon 6 Radilon® S is a range of polyamide 6 (PA6) products obtained through the polymerization of caprolactam and used for injection, extrusion and blow-molding.Information provided by Radici group. |
|||
Tensile Strength at Break | 155 MPa | 22500 psi | |
Radici Radilon® S RV500 (cond.) Nylon 6 Radilon® S is a range of polyamide 6 (PA6) products obtained through the polymerization of caprolactam and used for injection, extrusion and blow-molding.Information provided by Radici group. |
|||
Tensile Strength at Break | 155 MPa | 22500 psi | |
Plastcom SLOVAMID 6 NG GF 20 HLS PA6, 20% glass fibre, combined stability FeaturesPA 6 for injection moulding, chemically reinforced with 20% glass fibre, heat stabilized and weather stabilized. Stabilized against hydrolysis. Good surface finisch.Packaging, transport, sto.. |
|||
Tensile Strength at Break | <= 155 MPa | <= 22500 psi | ISO/R527 |
Polykemi AB SCANMID 6 B22^ E F40 Nylon 6, Glass Fiber Reinforced, Modified Information provided by Polykemi AB |
|||
Tensile Strength at Break | 155 MPa | 22500 psi | 10mm/min; ASTM D638 |
Kingfa PA66-RG301 Flame Retardant, 30% Glass Fiber Reinforced PA66 Features:Flame retardantHigh strengthHigh temperature propertiesGood electric propertiesNo bloomingApplications:Injection moldingConnectorsRelayBobbinsPlugsInformation Provided by Kingfa Sci. & Tech.. |
|||
Tensile Strength at Break | 155 MPa | 22500 psi | d.a.m.; ISO 527-1, -2; 5 mm/min |
Lanxess Durethan® BKV 130 DUS008 901510 Nylon 6, Glass Fiber Reinforced, Impact Modified PA 6, 30% glass fibers, injection molding, impact modifiedInformation provided by LANXESS. |
|||
Tensile Strength at Break | 155 MPa | 22500 psi | d.a.m.; ISO 527-1, -2; 5 mm/min |
Lanxess Durethan® BKV 30 H2.0 EF DUS029 901510 Nylon 6, Glass Fiber Reinforced PA 6, 30% glass fibers, injection molding, improved flowability, heat-aging stabilizedInformation provided by LANXESS. |
|||
Tensile Strength at Break | 155 MPa | 22500 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP RFL34 PA 66 (Asia Pacific) LNP* Lubricomp* RFL34 is a compound based on Nylon 66 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength at Break | 155 MPa | 22500 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP RFN16 PA 6 LNP* LUBRICOMP* RFN16 is a compound based on Nylon 66 resin containing 30% Glass Fiber, 5% MOS2. Added features of this material include: Wear Resistant. |
|||
Tensile Strength at Break | 155 MPa | 22500 psi | ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP EF004 PEI LNP* Thermocomp* EF004 is a compound based on Polyetherimide resin containing 20% Glass Fiber. |
|||
Tensile Strength at Break | 155 MPa | 22500 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP RF006LXP PA 66 (Asia Pacific) LNP* Thermocomp* RF006LXP is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: Low Extractible. |
|||
Tensile Strength at Break | 155 MPa | 22500 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL GFN1740V PPE+PS (Asia Pacific) Noryl* GFN1740V Polyphenylene Oxide (PPO) + Polystyrene (PS) resin is a 40 % Glass Reinforced, injection moldable grade with improved hydrolytic stability and with a Tensile Modulus > 11000 MPa; thi.. |
|||
Tensile Strength at Break | 155 MPa | 22500 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL EXNL1285 PPE+PS (Europe-Africa-Middle East) Noryl* EXNL1285 Polyphenylene Oxide (PPO) + Polystyrene (PS) resin is a 40 % Glass Reinforced, injection moldable grade with improved hydrolytic stability and with a Tensile Modulus > 11000 MPa; thi.. |
|||
Tensile Strength at Break | 155 MPa | 22500 psi | dry; ISO 527-1/-2 |
EMS-Grivory Grivory® 2SV-30H nat PA610-GF30 Product Description: GRILAMID XE3976 natural 9992 is a 30% glass fiber reinforced, heat stabilized polyamide 610 injection molding grade. This product is to a large extent based on renewable raw mat.. |
|||
Tensile Strength at Break | 155 MPa | 22500 psi | dry; ISO 527-1/-2 |
EMS-Grivory Grivory® LV-50H FWA black 9225 PA12-GF50 Product description: Grilamid LV-50H FWA black 9225 is a 50 % glass fiber reinforced, heat stabilized polyamide 12 injection molding grade with the following special features: High stiffness combine.. |
|||
Tensile Strength at Break | 155 MPa | 22500 psi | conditioned; ISO 527-1/-2 |
EMS-Grivory Grivory® TSG-60 PA666-GF60 Product description: Grilon TSG-60 is a heat stabilized, normal viscosity PA66 + PA6 injection molding grade with 60% glass fibers. Grilon TSG-60 has the following important properties: Very high st.. |
|||
Tensile Strength at Break | 155 MPa @Temperature 23.0 °C |
22500 psi @Temperature 73.4 °F |
ISO 527 |
DuPont Performance Polymers Crastin® SK609 NC010 PBT
(Unverified Data**) Crastin® SK609 NC010 is a 50% glass fiber reinforced, lubricated polybutylene terephthalate resin for injection molding.Information provided by DuPont Performance Polymers |
|||
Tensile Strength at Break | 155 MPa | 22500 psi | ISO 527 |
Eurotec® Tecodur® PB70 GR50 NL PBT 50% glass fiber reinforced Excellent stiffness and hardnessGood mechanical strengthGood creep and fatigue behaviorVery good thermal stabilityExcellent flammability characteristicsGood electrical propertiesHigh wear resistance.. |
|||
Tensile Strength at Break | 155 MPa | 22500 psi | ISO 527-93 |
Wellman Wellamid® GF33-66/6 XE-WBK 33% Glass Fiber Reinforced, Weatherable Black Nylon 66/6 Description: Glass Fiber Reinforced, Weatherable Black Nylon 66/6Information provided by Wellman. |
|||
Tensile Strength at Break | 155 MPa | 22500 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP RF0069XZ PA 66 LNP THERMOCOMP* RF0069XZ is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added features of this material include: Flame Retardant. |
|||
Tensile Strength at Break | 155 MPa | 22500 psi | conditioned; ISO 527-1/-2 |
EMS-Grivory Grivory® BG-50 FC PA6-GF50 Product description: Grilon BG-50 FC is a heat stabilized PA6 injection molding grade with 50% glass fibers. Grilon BG-50 FC has the following important properties: Short cycle timesExcellent surfac.. |
|||
Tensile Strength at Break | 155 MPa | 22500 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON LX00797C PEEK LNP* STAT-KON* LX00797C is a compound based on Polyetheretherketone containing Proprietary Filler(s). Added features of this material include: ristics of this grade are: Clean Compounding System, .. |
|||
Tensile Strength at Break | 155 MPa | 22500 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL FE1740PW PPE+PS (Europe-Africa-Middle East) Noryl* FE1740PW Polyphenylene Oxide (PPO) + Polystyrene (PS) resin is a 40 % Glass Reinforced, injection moldable grade with improved hydrolytic stability and with a Tensile Modulus > 11000 MPa; thi.. |