SABIC Innovative Plastics LNP LUBRICOMP RFL34 PA 66 (Asia Pacific)

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP RFL34 PA 66 (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
LNP* Lubricomp* RFL34 is a compound based on Nylon 66 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
Physical Properties Metric English Comments
Density 1.42 g/cc
0.0513 lb/in³
ASTM D792
1.42 g/cc
0.0513 lb/in³
ISO 1183
Moisture Absorption 0.500 %
0.500 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.013 cm/cm

@Time 86400 sec
 0.013 in/in

@Time 24.0 hour
 ASTM D955
0.013 cm/cm

@Time 86400 sec
 0.013 in/in

@Time 24.0 hour
 ISO 294
Linear Mold Shrinkage, Transverse 0.019 cm/cm

@Time 86400 sec
 0.019 in/in

@Time 24.0 hour
 ASTM D955
0.019 cm/cm

@Time 86400 sec
 0.019 in/in

@Time 24.0 hour
 ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 155 MPa
22500 psi
ISO 527
157 MPa
22800 psi
ASTM D638
Tensile Strength, Yield 155 MPa
22500 psi
ISO 527
157 MPa
22800 psi
ASTM D638
Elongation at Break 3.2 %
3.2 %
ISO 527
3.3 %
3.3 %
ASTM D638
Elongation at Yield 3.2 %
3.2 %
ISO 527
3.3 %
3.3 %
ASTM D638
Tensile Modulus 8.06 GPa
1170 ksi
1 mm/min; ISO 527
8.27 GPa
1200 ksi
50 mm/min; ASTM D638
Flexural Strength 220 MPa
31900 psi
ASTM D790
223 MPa
32300 psi
ISO 178
Flexural Modulus 6.89 GPa
999 ksi
ASTM D790
7.00 GPa
1020 ksi
ISO 178
Izod Impact, Notched 1.06 J/cm
1.99 ft-lb/in
ASTM D256
Izod Impact, Unnotched 11.74 J/cm
21.99 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 11.0 kJ/m²
5.23 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 67.0 kJ/m²
31.9 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 10.0 J
7.38 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 4.00 J
2.95 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.60
0.60
ASTM D3702 Modified
Coefficient of Friction, Static 0.60
0.60
ASTM D3702 Modified
K (wear) Factor 20.1 x 10-8 mm³/N-M
10.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 71.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 39.4 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
72.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 40.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
CTE, linear, Transverse to Flow 36.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 20.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
36.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 20.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 262 °C
504 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
262 °C

@Thickness 3.20 mm
 504 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 250 °C
482 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
252 °C

@Thickness 3.20 mm
 486 °F

@Thickness 0.126 in
 unannealed; ASTM D648