SABIC Innovative Plastics LNP THERMOCOMP RF0069XZ PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP RF0069XZ PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* RF0069XZ is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added features of this material include: Flame Retardant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.69 g/cc | 1.69 g/cc | ASTM D792 |
| Density | 1.68 g/cc | 0.0607 lb/in³ | ISO 1183 |
| 1.69 g/cc | 0.0611 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.360 % | 0.360 % | 50% RH, 24 hrs; ASTM D570 |
| 0.540 % | 0.540 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0050 cm/cm @Time 86400 sec |
0.0020 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.040 cm/cm @Time 86400 sec |
0.010 - 0.040 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 155 MPa | 22500 psi | 5 mm/min; ISO 527 |
| 160 MPa | 23200 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.9 % | 1.9 % | 5 mm/min; ISO 527 |
| 2.1 % | 2.1 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 13.09 GPa | 1899 ksi | 1 mm/min; ISO 527 |
| 13.36 GPa | 1938 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 237 MPa | 34400 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 11.5 GPa | 1670 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 11.95 GPa | 1733 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.730 J/cm | 1.37 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.29 J/cm | 13.7 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 45.0 kJ/m² | 21.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 8.00 J @Temperature 23.0 °C |
5.90 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 25.4 µm/m-°C @Temperature -30.0 - 30.0 °C |
14.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 49.7 µm/m-°C @Temperature -30.0 - 30.0 °C |
27.6 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 255 °C | 491 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 254 °C @Thickness 3.20 mm |
489 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 241 °C @Thickness 3.20 mm |
466 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Flammability, UL94 | V-0 @Thickness 1.00 mm |
V-0 @Thickness 0.0394 in |
UL 94 |
Users viewing this material also viewed the following:
- Haysite H258 Polyester Laminate
- Indium Corp. CU 12 Copper Cleaner
- LATI Laticonther 83 CP/85 PA12, Impact Modified
- SABIC Innovative Plastics LNP Lubricomp QP003 PA 6/10 (Asia Pacific)
- Solvay Specialty Polymers Kalix® 2930 HFFR Polyamide, High Performance (HPPA), Glass Fiber
- Saint-Gobain CHR® 2275-2 Extruded PTFE Film Backing Silicone Adhesive Pressure Sensitive Tape
- American Elements Z-MITE™ Zinc Oxide Nanopowder
- Colorite Polymers 9812 Clear Injection Molding Vinyl Compound
- 3M 8426-11 Cold Shrink Connector Insulators
- ATI Allegheny Ludlum Stainless Steel Chromium-Nickel Type 304, 60% Cold Rolled (UNS S30400)
Copyright © lookpolymers.com All Rights Reserved