Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 95.0 MPa | 13800 psi | STN EN ISO 527-2 |
Plastcom SLOVAMID 6 GF 15 LS Polyamide 6, 15% Glass Fiber, UV Stabilization FeaturesPA 6 for injection moulding, chemically reinforced with 15% glass fiber, stabilized against UV-radiation. Used for the grips of electric tools, hobby tools, gears, covers of electric tools... |
|||
Tensile Strength at Break | 95.0 MPa | 13800 psi | ISO.527 DIN.53455 |
Omnia Plastica PEI Polyetherimide This high performance engineering plastic is a non-reinforced self-extinguishing amorphous polymer with high thermal, electrical and mechanical properties which are typical of a crystalline polymer... |
|||
Tensile Strength at Break | 95.0 MPa | 13800 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Cycoloy® C4215HF PC+ABS (Europe-Africa-Middle East) Cycoloy C4215HF is a 15% glass reinforced, non-FR PC+ABS grade with high heat resistance, excellent strength and rigidity with good cosmetic apprearance. It combines good processability with a low s.. |
|||
Tensile Strength at Break | 95.0 MPa | 13800 psi | ISO 527 |
Nilit RECONYL A H Recycled nylon 6.6 for injection molding Recycled nylon 6.6 for injection molding, heat stabilized (available only in black).Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Tensile Strength at Break | <= 95.0 MPa | <= 13800 psi | ISO/R527 |
Polykemi AB SCANAMID 66 A12^FC Nylon 66 Information provided by Polykemi AB |
|||
Tensile Strength at Break | 95.0 MPa @Temperature 23.0 °C |
13800 psi @Temperature 73.4 °F |
ISO 527-2/5 |
PolyOne Bergamid™ B700 G20 H UF Polyamide 6 (Nylon 6) Information provided by PolyOne |
|||
Tensile Strength at Break | 95.0 MPa | 13800 psi | ISO 527 |
SABIC Innovative Plastics LNP KONDUIT RTF2B PA 66 (Europe-Africa-Middle East) LNP* Konduit* RTF2B is a compound based on Nylon 66 resin containing Glass Fiber, Proprietary Thermal Filler. Added features of this material include: Thermally Conductive. |
|||
Tensile Strength at Break | 95.0 MPa | 13800 psi | STN EN ISO 527-2 |
Plastcom SLOVALEN PH 49 GF 30 003/3M Polypropylene reinforced with glass fiber, heat stabilized Modified homopolymer PP for injection molding, reinforced with 30% glass fiber, heat stabilized. Delivered in black color.Information Provided by Plastcom spol. s r.o. |
|||
Tensile Strength at Break | 95.0 MPa | 13800 psi | ISO 527 |
Gharda Chemicals GATONE™ 5400 PEEK, Medium Viscosity Grade
(discontinued **) Medium viscosity grade for extrusion and injection moldingCHARACTERISTICS: Outstanding chemical resistance.Outstanding wear resistance.Outstanding resistance to hydrolysis.Excellent mechanical prope.. |
|||
Tensile Strength at Break | 95.0 MPa | 13800 psi | ISO 527 |
Gharda Chemicals GATONE™ 5600 PEEK, Low Viscosity Grade
(discontinued **) Low viscosity. grade for injection molding of thin sections & complex partsCHARACTERISTICS: Outstanding chemical resistance.Outstanding wear resistance.Outstanding resistance to hydrolysis.Excellen.. |
|||
Tensile Strength at Break | 95.0 MPa | 13800 psi | ISO 527-1/-2 |
DSM Akulon® K224-TPG3 Impact Modified Nylon 6-15% Glass Reinforced (European Grade) (Dry)
(discontinued **)&l The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier .. |
|||
Tensile Strength at Break | 95.0 MPa | 13800 psi | ISO 527-1/-2 |
Mitsubishi Xantar® G4F 23 R Polycarbonate-20% Glass Reinforced Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
Tensile Strength at Break | 95.0 MPa | 13800 psi | cond.; ISO 527-1, -2; 5 mm/min |
Lanxess Durethan® BKV 130 GIT DUS008 900116 Nylon 6, Impact Modified PA 6, 30% glass fibers, injection molding, impact modified, GIT/WITInformation provided by LANXESS. |
|||
Tensile Strength at Break | 95.0 MPa | 13800 psi | 10mm/min; ASTM D638 |
Kingfa PBT-RG151 Flame Retardant, 15% Glass Fiber Reinforced PBT Features:Flame retardantHigh strengthHigh temperature propertiesGood electric propertiesExcellent size stabilityNo bloomingApplications:Injection moldingConnectorsRelayBobbinsPlugsE & E partsInforma.. |
|||
Tensile Strength at Break | 95.0 MPa | 13800 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Lubricomp GFL14 PSU LNP* Lubricomp* GFL14 is a compound based on Polysulfone containing Glass Fiber and PTFE Lubricant.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 95.0 MPa | 13800 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics ULTEM CRS5001 PEI (Europe-Africa-Middle East) Transparent, Standard flow Polyetherimide copolymer (Tg 225C) with enhanced chemical resistance to strong acids, bases, aromatics, and ketones.Resin is RoHS compliant. UL94 V0 listing. |
|||
Tensile Strength at Break | 95.0 MPa | 13800 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON EX01696C PEI LNP* STAT-KON* EX01696C is a compound based on Polyetherimide resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive, Clean Compounding System. |
|||
Tensile Strength at Break | 95.0 MPa | 13800 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Thermocomp PFB42U PA 6 (Europe-Africa-Middle East) LNP STARAMIDE PFB42U is a compound based on Nylon 6 resin containing Glassfiber and Glass Beads Additional features include Heat Stabilized.This data was supplied by SABIC-IP for the Europe-Africa-M.. |
|||
Tensile Strength at Break | 95.0 MPa | 13800 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP ZF406XXX PPO Blend LNP THERMOCOMP* ZF406XXX is a compound based on PPO Blend resin containing Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant. |
|||
Tensile Strength at Break | 95.0 MPa | 13800 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP ZF406XXX PPO Blend (Asia Pacific) LNP THERMOCOMP* ZF406XXX is a compound based on PPO Blend resin containing Flame Retardant, Glass Fiber. Added features of this material include: Flame Retardant. |
|||
Tensile Strength at Break | 95.0 MPa | 13800 psi | Vertical; ASTM D570 |
Unitika UNILATE® 1 SC PET Antistatic gradeUNILATE® products are plate materials prepared by using a polyethylene terephthalate (PET resin) as the main component, blending it with glass staple fiber, inorganic filler, and ot.. |
|||
Tensile Strength at Break | 95.0 MPa | 13800 psi | ISO 527-1/-2 |
Covestro Bayblend® T88 GF-10* Polycarbonate + SAN Glass Filled Impact Grade Developmental productInjection molding grade10 % GFoptimized heat ageing- and UV-stabilityvery good flowtensile modulus = 5100 MPaVicat/B 120 = 134 °CPreprocessingMax. Water content |
|||
Tensile Strength at Break | 95.0 MPa | 13800 psi | ISO 527-1/-2 |
DuPont Performance Polymers Delrin® 510GR NC000 Acetal (POM)
(Unverified Data**) 10% Glass Reinforced Medium Viscosity Acetal Homopolymer Delrin 510GR is a 10% glass reinforced acetal homopolymer for injection molding. It has high strength stiffness and high deflection temperatu.. |
|||
Tensile Strength at Break | 95.0 MPa | 13800 psi | 50%RH; ISO 527-1/-2 |
DuPont Performance Polymers Zytel® 80G33L NC010 Nylon 66
(Unverified Data**) 33% Glass Reinforced Toughened Polyamide 66 Zytel 80G33L NC010 is a 33% glass fiber reinforced polyamide 66 resin with outstanding impact resistance developed using DuPont Super Tough technology.Inf.. |
|||
Tensile Strength at Break | 95.0 MPa | 13800 psi | 5 mm/min; ISO 527 |
Eurostar Staramide PFB42U PA6, Glass Fiber/Bead Filled, Injection Molded Starflam PFB42U is an UV Stabilized, Glass Bead and Glass Fiber Reinforced Polyamide 6 Injection Molding ResinInformation provided by Eurostar. |
|||
Tensile Strength at Break | 95.0 MPa | 13800 psi | ISO 527 |
Eurotec® Tecotek® PC30 GR20 GR003 ZG20 PC, 20% glass fiber reinforced, flame retardant - halogen (RoHS compliant), grey RAL 7035 Information provided by Eurotec® |
|||
Tensile Strength at Break | 95.0 MPa | 13800 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON OE002 PPS - LINEAR LNP* STAT-KON* OE002 is a compound based on PPS - Linear resin containing 10% Carbon Fiber. Added feature of this material is: Electrically Conductive. |