SABIC Innovative Plastics LNP THERMOCOMP ZF406XXX PPO Blend
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP ZF406XXX PPO Blend.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* ZF406XXX is a compound based on PPO Blend resin containing Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.53 g/cc | 0.0553 lb/in³ | ISO 1183 |
| 1.54 g/cc | 0.0556 lb/in³ | ASTM D792 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm @Time 86400 sec |
0.0050 - 0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0050 - 0.0070 cm/cm @Time 86400 sec |
0.0050 - 0.0070 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 95.0 MPa | 13800 psi | ASTM D638 |
| 119 MPa | 17300 psi | ISO 527 | |
| Elongation at Break | 0.90 % | 0.90 % | ASTM D638 |
| 1.2 % | 1.2 % | ISO 527 | |
| Tensile Modulus | 11.53 GPa | 1672 ksi | 50 mm/min; ASTM D638 |
| 11.69 GPa | 1695 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 192 MPa | 27800 psi | ISO 178 |
| 199 MPa | 28900 psi | ASTM D790 | |
| Flexural Modulus | 9.90 GPa | 1440 ksi | ISO 178 |
| 11.45 GPa | 1661 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.800 J/cm | 1.50 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.23 J/cm | 9.80 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 29.0 kJ/m² | 13.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 19.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
11.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 57.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
32.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 262 °C | 504 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 263 °C @Thickness 3.20 mm |
505 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Flammability, UL94 | V-0 @Thickness 1.55 mm |
V-0 @Thickness 0.0610 in |
UL 94 by SABIC-IP |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPO D-6208
- Prodways PLASTCure Flex 100 3D Printing Polymer
- Resinlab® EP1112NC Black Electronic Grade Epoxy Encapsulant
- SK Chemicals SKYTHANE® 185A S series Polyurethane
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 60 PHR N550 (FEF) Filler
- TSE Industries Millathane® 97 Millable Polyester Polyurethane Rubber, 30.0 PHR Wacker HDK N20 Filler
- 3M Dyneon™ FX 11818 Fluoroelastomer
- 3M 4411G Extreme Sealing Tape
- Braskem LF218/21 LLDPE Cast and Blown Film Extrusion Polyethylene Copolymer
- Karina 06/30-FC-LMP Blue Color Concentrate for PVC
Copyright © lookpolymers.com All Rights Reserved