Polymer Property : Tensile Strength at Break = 76.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	76.0 MPa	11000 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® FST9705 PC Copolymer High viscosity Proprietary Polycarbonate Ester, OSU 55/55 compliant, low smoke, flame retardant resin
Tensile Strength at Break	76.0 MPa	11000 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® FST9705 PC Copolymer (Asia Pacific) High visocisty PC Copolymer, OSU 55/55 compliant, low smoke, flame retardant resin
Tensile Strength at Break	76.0 MPa	11000 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® FST9705 PC Copolymer (Europe-Africa-Middle East) High viscosity PC Copolymer, OSU 55/55 compliant, low smoke, flame retardant resin
Tensile Strength at Break	76.0 MPa	11000 psi	Type I, 50 mm/min; ASTM D 638
SABIC Innovative Plastics Lexan® ML6031 PC Copolymer (Asia Pacific) High viscosity PC copolymer blend with enhanced UV stabilization and added release agent. V2 rated. Available in transparent and tinted colorsThis data was supplied by SABIC-IP for the Asia Pacific ..
Tensile Strength at Break	76.0 MPa	11000 psi	Type I, 50 mm/min; ASTM D 638
SABIC Innovative Plastics Lexan® ML6031 PC Copolymer (Europe-Africa-Middle East) High viscosity PC copolymer blend with enhanced UV stabilization and added release agent. V2 rated. Available in transparent and tinted colorsThis data was supplied by SABIC-IP for the Europe-Africa..
Tensile Strength at Break	76.0 MPa	11000 psi	ASTM D638
SABIC Innovative Plastics LNP COLORCOMP PX99848 PA 6 LNP* COLORCOMP* PX99848 is an unfilled Nylon 6 resin.
Tensile Strength at Break	76.0 MPa	11000 psi	ISO 527-1/-2
DSM Akulon® K224-PG6U (Cond.) 33% Glass Reinforced, Impact Modified Nylon 6 (North America) (discontinued **) Description: The Akulon portfolio is engineered for optimum performance to suit different processing techniques and end use markets.Unfilled Extrusion ResinsAkulon resins are available with melt vis..
Tensile Strength at Break	76.0 MPa	11000 psi	10mm/min; ASTM D638
Kingfa JH720 G10 10% Glass Fiber Reinforced PC Features:High mechanical strengthGood size stabilityGood surfaceSuitable for exact moldingApplications:Exact mechanism partsPrinter, photocopies, scanner cabinetComputer plug partsCD-ROM, DVDElectri..
Tensile Strength at Break	76.0 MPa	11000 psi	10mm/min; ASTM D638
Kingfa JH-R2G10 P60 10% Glass Fiber Reinforced PC/ABS Alloy Features:UL HB @ 1.6-3.2mmExcellent balance propertiesHigh stiffnessGood size stabilityGood surface adhesionExcellent processing properties, large partsApplications:Injection moldingAutomobile instr..
Tensile Strength at Break	76.0 MPa	11000 psi	ASTM D638
LG Chemical IH830H PMMA, General Purpose Grade for Injection Molding Highest of all grades in heat resistanceMechanical strength and surface hardnessParticularly recommended for tail lamp, reflectors, and general lighting fixturesFeatures: Excellent transparency and ..
Tensile Strength at Break	76.0 MPa	11000 psi	ISO 527
SABIC Innovative Plastics LNP LUBRICOMP HFG25Z PA 11 (Asia Pacific) LNP* Lubricomp* HFG25Z is a compound based on Nylon 11 resin containing Glass Fiber, Graphite Powder. Added features of this material include: Internally Lubricated.
Tensile Strength at Break	76.0 MPa	11000 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP HFG25Z PA 11 (Asia Pacific) LNP* Lubricomp* HFG25Z is a compound based on Nylon 11 resin containing Glass Fiber, Graphite Powder. Added features of this material include: Internally Lubricated.
Tensile Strength at Break	76.0 MPa	11000 psi	ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP KFL32L Acetal Copolymer LNP* LUBRICOMP* KFL32L is a compound based on Acetal Copolymer resin containing 10% Glass Fiber, 15% PTFE. Added feature of this material is: Wear Resistant.
Tensile Strength at Break	76.0 MPa	11000 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP LX00430 PEEK LNP* LUBRICOMP* LX00430 is a compound based on Pelyetheretherketone containing Proprietary Fillers. Added feature of this grade is: Wear Resistant.
Tensile Strength at Break	76.0 MPa	11000 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP AF004XXY ABS LNP* Thermocomp* AF004XXY is a compound based on ABS containing 20% glass fiber.
Tensile Strength at Break	76.0 MPa	11000 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP Thermocomp QF002 PA6.10 LNP* Thermocomp* QF002 is a compound based on Nylon 6/10 containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region.
Tensile Strength at Break	76.0 MPa	11000 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP WFB62 PBT LNP* THERMOCOMP* WFB62 is a compound based on PBT resin containing 10% Glass Fiber, 10% Glass Bead. Added feature of this grade is: Low Warpage.
Tensile Strength at Break	76.0 MPa	11000 psi	ASTM D638
Sumitomo Bakelite North America E 8398 Hardware Grade Epoxy Fiberglass and mineral reinforced epoxy molding compound with excellent dimensional stability, good electrical insulation properties, and good strength.Information provided by Vyncolit, a Sumitomo B..
Tensile Strength at Break	76.0 MPa	11000 psi	ASTM D638
Sumitomo Bakelite North America EM 7302LD-2 Long Glass Fiber Reinforced Epoxy EM 7302LD-2 is a long fiberglass reinforced epoxy molding compound with a low density inert filler. This compound is designed for applications where moderate strength and weight savings are desirabl..
Tensile Strength at Break	76.0 MPa	11000 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP EP003 PEI LNP* Lubricomp EP003 is a Polyetherimide containing 15% PTFE/Silicone. Added features include: Internally Lubricated.
Tensile Strength at Break	76.0 MPa	11000 psi	ASTM D638
Sumitomo Bakelite North America EpiallÂ® 1908B-1 Short Glass Fiber Reinforced Epoxy Epiall 1908B-1 is a short fiberglass reinforced epoxy molding compound, with excellent dimensional stability, good strength properties and good electrical insulation properties.Information provided ..
Tensile Strength at Break	76.0 MPa	11000 psi	Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics Noryl CRX2201 PPE+HIPS (Asia Pacific) Noryl* CRX2201 resin is a 25% mineral reinforced, injection moldable modified polyphenylene ether resin designed for improved chemical resistance when compared with standard Noryl resins. Noryl CRX..
Tensile Strength at Break	76.0 MPa	11000 psi	Type I, 50 mm/min; ASTM D 638
SABIC Innovative Plastics Noryl PX0346 PPE+PS This data was supplied by SABIC-IP for the Americas region.
Tensile Strength at Break	76.0 MPa	11000 psi	5 mm/min; ISO 527
Eurostar Starflam AFR560B5 PA66, Mineral/Glass Fiber Reinforced, Flame Retardant, Injection Molding Starflam AFR560B5 is a Flame Retardant, Mineral Filled and Glass Fiber Reinforced Polyamide 66, Injection Molding ResinInformation provided by Eurostar.
Tensile Strength at Break	76.0 MPa	11000 psi	v = 5 mm/min; ISO 527-2
CENTROPLAST CENTROLYTE ZX Polyethylene terephthalate with lubricant This material's solid lubricant additive has good sliding properties, and is well suited for high load, dry running situations. Possible uses include precision plain bearings, plug connectors, r..
Tensile Strength at Break	76.0 MPa	11000 psi	DAM; ISO 527-1/-2
DuPont Performance Polymers Minlon® 12T BKB100 Nylon 66 (Unverified Data**) 36% Mineral Reinforced Toughened Polyamide 66 Minlon 12T BKB100 is a 36% mineral reinforced toughened heat stabilized black polyamide 66 resin for injection molding.Information provided by DuPont Pe..
Tensile Strength at Break	76.0 MPa	11000 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® SLX2071T PC Copolymer (Europe-Africa-Middle East) High viscosity PC copolymer blend with enhanced UV stabilization and added release agent. V2 rated. Available in transparent and tinted colors
Tensile Strength at Break	76.0 MPa	11000 psi	Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics LNP Thermocomp MF0069S PP LNP* Thermocomp* MF0069S is a compound based on Polypropylene resin containing Glass Fiber, Flame Retardant. Added features of this material include: Chemically Coupled, Flame Retardant, Heat Stabi..
Tensile Strength at Break	76.0 MPa	11000 psi	ISO 527
SABIC Innovative Plastics LNP THERMOTUF WF003I Polyester, TP LNP THERMOTUF* WF003I is a compound based on Polyester, TP resin containing Glass Fiber. Added features of this material include: High Impact.