SABIC Innovative Plastics LNP THERMOCOMP AF004XXY ABS
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port, China |
| Download PDF |
SABIC Innovative Plastics LNP THERMOCOMP AF004XXY ABS.pdf
|
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* AF004XXY is a compound based on ABS containing 20% glass fiber.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Density | 1.19 g/cc | 0.0430 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.250 % | 0.250 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow |
0.0020
cm/cm <br>@Time 86400 sec
|
0.0020
in/in <br>@Time 24.0 hour
|
ASTM D955 |
|
0.0020
cm/cm <br>@Time 86400 sec
|
0.0020
in/in <br>@Time 24.0 hour
|
ISO 294 | |
| Linear Mold Shrinkage, Transverse |
0.0040
cm/cm <br>@Time 86400 sec
|
0.0040
in/in <br>@Time 24.0 hour
|
ASTM D955 |
|
0.0040
cm/cm <br>@Time 86400 sec
|
0.0040
in/in <br>@Time 24.0 hour
|
ISO 294 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 76.0 MPa | 11000 psi | Type I, 5 mm/min; ASTM D638 |
| 77.0 MPa | 11200 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 1.8 % | 1.8 % | 5 mm/min; ISO 527 |
| 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 6.04 GPa | 876 ksi | 1 mm/min; ISO 527 |
| 6.08 GPa | 882 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 119 MPa | 17300 psi | ISO 178 |
| 122 MPa | 17700 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 5.97 GPa | 866 ksi | 2 mm/min; ISO 178 |
| 6.08 GPa | 882 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.800 J/cm | 1.50 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.74 J/cm | 7.01 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 23.0 kJ/m² | 10.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy |
13.0
J <br>@Temperature 23.0 °C
|
9.59
ft-lb <br>@Temperature 73.4 °F
|
ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow |
56.0
µm/m-°C <br>@Temperature -30.0 - 30.0 °C
|
31.1
µin/in-°F <br>@Temperature -22.0 - 86.0 °F
|
ASTM D696 |
| CTE, linear, Transverse to Flow |
52.0
µm/m-°C <br>@Temperature -30.0 - 30.0 °C
|
28.9
µin/in-°F <br>@Temperature -22.0 - 86.0 °F
|
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
100
°C <br>@Thickness 3.20 mm
|
212
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
Users viewing this material also viewed:
- Polimeri Europa Europrene® NEOCIS BR 60 Butadiene Rubber
- Precision Polymer Engineering Kemex™ V76W
- Proto3000 Objet Digital Materials™ DM_9840/9740 Rubber-like Prototyping Polymer
- PolyOne Geon™ Vinyl Flexible R7545H Polyvinyl Chloride, Flexible (PVC, Flexible)
- SABIC Innovative Plastics Lexan® HP3NREU PC (Europe-Africa-Middle East)
- Teijin Multilon T-3713 Standard PC/ABS Polymer Alloy
- Solvay MIRACARE® LSC-217 Surfactant
- Solvay TECHNYL® A 218 S40 Black 21 N PA66, 40% glass spheres, Conditioned
- A. Schulman POLYTROPE™ TPP 524 Injection Molding Grade Olefinic Thermoplastic Elastomer
- ATI Allvac® Nickelvac® L-605 Cobalt-Nickel Superalloy, Heat Treatment: 1204°C (2200°F) Anneal
Copyright © lookpolymers.com All Rights Reserved