SABIC Innovative Plastics LNP Thermocomp QF002 PA6.10
| Category | Polymer , Thermoplastic , Nylon , Nylon 610 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp QF002 PA6.10.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* QF002 is a compound based on Nylon 6/10 containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.16 g/cc | 1.16 g/cc | ASTM D 792 |
| Density | 1.15 g/cc | 0.0415 lb/in³ | ASTM D 792 |
| Moisture Absorption at Equilibrium | 0.35 % | 0.35 % | 23°C / 50% RH; ISO 62 |
| 0.26 % @Time 86400 sec |
0.26 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0060 cm/cm @Time 86400 sec |
0.0030 - 0.0060 in/in @Time 24.0 hour |
ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0090 cm/cm @Time 86400 sec |
0.0060 - 0.0090 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 73.0 MPa | 10600 psi | Type I, 5 mm/min; ASTM D 638 |
| 76.0 MPa | 11000 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 1.8 % | 1.8 % | Type I, 5 mm/min; ASTM D 638 |
| 2.3 % | 2.3 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 4.58 GPa | 664 ksi | 1 mm/min; ISO 527 |
| 4.60 GPa | 667 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 121 MPa | 17500 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 3.76 GPa | 545 ksi | 2 mm/min; ISO 178 |
| 3.96 GPa | 574 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 0.360 J/cm @Temperature 23.0 °C |
0.674 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 3.25 J/cm @Temperature 23.0 °C |
6.09 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² @Temperature 23.0 °C |
1.43 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 20.0 kJ/m² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| 4.00 J @Temperature 23.0 °C |
2.95 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 54.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
30.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| CTE, linear, Transverse to Flow | 96.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
53.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 217 °C @Thickness 3.20 mm |
423 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 183 °C | 361 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 196 °C @Thickness 3.20 mm |
385 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- NanoAmor 95%, OD/ID/L: 10-20/5-10 nm/0.5-2 um Short Multi-Walled Carbon Nanotubes
- Ovation Polymers OpteSTAT™ MB PK 8000 Polyetheretherketone based Carbon Nanotube Compound
- SABIC Innovative Plastics NORYL NC212 PPE+HIPS (Asia Pacific)
- ExxonMobil 50 Exxon XD-3
- Dow Corning BY 25-320
- Ensinger XP-132 Compression Molded PI Compound, 15% Graphite Filled
- Diamond Polymers ASA M-143
- Aclo Accutech Polypropylene Copolymer CP0437G10CL Glass Reinforced Coupled
- Aclo Accutech Polypropylene Homopolymer HP0339T20L Talc Reinforced
Copyright © lookpolymers.com All Rights Reserved