Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | <= 160 MPa | <= 23200 psi | ISO/R527 |
Polykemi AB SCANAMID 66 A12^ F25 FR6 Nylon 66, Glass Fiber Reinforced, Flame Retardant Information provided by Polykemi AB |
|||
Tensile Strength at Break | 160 MPa | 23200 psi | |
Radici Radilon® A RV250 (dry) Nylon 66 Radilon® A is a range of polyamide 66 (PA66) products obtained through the polymerization of hexamethylendiamine and adipic acid, and used for injection, extrusion and blow-molding.Information prov.. |
|||
Tensile Strength at Break | 160 MPa | 23200 psi | ISO 527 |
Nilit FRIANYL B63 GV25 Nylon 6 for injection molding, 25% glass fiber reinforced Nylon 6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Tensile Strength at Break | 160 MPa | 23200 psi | ISO 527-2 |
Pasargad Polymer Peyvand Pasamid 3P-H7130B Nylon 6/66, 30% Glass Fiber Reinforced Form: PelletsProcessing Method: Injection MoldingUses: Automotive Application Furniture Appliance Components Electrical PartsFastenerHousingInformation provided by Pasargad Polymer Peyvand Co |
|||
Tensile Strength at Break | 160 MPa | 23200 psi | ASTM D1708 |
GEHR Plastics Ultem 2300 PEI-30 GF 30% Glass Fiber Reinforced
(discontinued **) Polyetherimide has a high mechanical strength in connection with a good chemical and heat resistance, good dimensional stability and great resistance. It's unique torque strength permits the econom.. |
|||
Tensile Strength at Break | 160 MPa | 23200 psi | ASTM D638 |
LNP Thermocomp® EF-1004 BK8-115 Polyetherimide, Glass Fiber Reinforcement
(discontinued **) Forms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names.. |
|||
Tensile Strength at Break | 160 MPa | 23200 psi | ASTM D683 |
Loxim 330 01HB Nylon 6 Information provided by Loxim Industries |
|||
Tensile Strength at Break | 160 MPa | 23200 psi | ISO 527-1/-2 |
Lanxess Durethan® BKV 130 000000 Copolyamide, 30% Glass Fiber CoPA, injection molding grade, 30% glass fibers, elastomer modified, electroplateable, higher notched impact strength and also higher energy absorption under biaxial impact load than BKV 30, even in.. |
|||
Tensile Strength at Break | 160 MPa | 23200 psi | d.a.m.; ISO 527-1, -2; 5 mm/min |
Lanxess Durethan® BKV 130 GIT DUS008 900116 Nylon 6, Impact Modified PA 6, 30% glass fibers, injection molding, impact modified, GIT/WITInformation provided by LANXESS. |
|||
Tensile Strength at Break | 160 MPa | 23200 psi | ISO 527 Type 1A |
Solvay TECHNYLSTARâ„¢ S 216L2 V30 PA6, 30% glass filled, DRY Description: TECHNYLSTAR polyamide reinforced with 30% GF, UV stabilized, for Injection molding. Available in: Europe and North AmericaProduct Applications: TECHNYLSTAR TM S 216L2 V30 BLACK is chara.. |
|||
Tensile Strength at Break | 160 MPa | 23200 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP RFN16SXZ PA 66 LNP LUBRICOMP* RFN16SXZ is a compound based on Nylon 66 resin containing 30% Glass Fiber, 5% MOS2. Added features of this material include: Heat Stabilized, Wear Resistant. |
|||
Tensile Strength at Break | 160 MPa | 23200 psi | ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP OF008E PPS - LINEAR LNP* THERMOCOMP* OF008E is a compound based on PPS - Linear resin containing 40% Glass Fiber. Added features of this material include: Easy Molding. |
|||
Tensile Strength at Break | 160 MPa | 23200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP PF006S PA 6 (Europe-Africa-Middle East) Heat stabilized, 30% glass fibre reinforced Polyamide 6 injection moulding resin. |
|||
Tensile Strength at Break | 160 MPa | 23200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP PF006U PA 6 (Europe-Africa-Middle East) UV stabilized, 30% glass fibre reinforced Polyamide 6 injection moulding resin. |
|||
Tensile Strength at Break | 160 MPa | 23200 psi | conditioned; ISO 527-1/-2 |
EMS-Grivory Grivory® BG-60 FC PA6-GF60 Product description: Grilon BG-60 FC is a heat stabilized PA6 injection molding grade with 60% glass fibers. Grilon BG-60 FC has the following important properties: Short cycle timesExcellent surfac.. |
|||
Tensile Strength at Break | 160 MPa | 23200 psi | conditioned; ISO 527-1/-2 |
EMS-Grivory Grivory® TSGL-40/4 FA black 9840 PA666-GF40 Product description: Grilon TSGL-40/4 FA black 9840 is based on a heat stabilized semi-crystalline Polyamide PA66+PA6 and 40% long glass fibers. Grilon TSGL-40/4 FA black 9840 is characterized by th.. |
|||
Tensile Strength at Break | 160 MPa | 23200 psi | conditioned; ISO 527-1/-2 |
EMS-Grivory Grivory® XE 4105 black 9992 PA610-GF50 Product description: Grilamid XE 4105 black 9992 is a 50% glass fiber reinforced, heat stabilized and UV resistant polyamide 610 (PA610) injection molding grade. This product is to a large extent ba.. |
|||
Tensile Strength at Break | 160 MPa | 23200 psi | 50%RH; ISO 527-1/-2 |
DuPont Performance Polymers Zytel® 70G43HSLA BK099 Nylon 66
(Unverified Data**) 43% Glass Reinforced Heat Stabilized Polyamide 66 Zytel 70G43HSLA BK099 is a 43% glass fiber reinforced heat stabilized black polyamide 66 resin for injection molding.Information provided by DuPont .. |
|||
Tensile Strength at Break | 160 MPa | 23200 psi | 50%RH; ISO 527-1/-2 |
DuPont Performance Polymers Zytel® 70G43L NC010 Nylon 66
(Unverified Data**) 43% Glass Reinforced Polyamide 66Zytel 70G43L NC010 is a 43% glass fiber reinforced polyamide 66 resin for injection molding.Information provided by DuPont Performance Polymers |
|||
Tensile Strength at Break | 160 MPa | 23200 psi | DAM; ISO 527-1/-2 |
DuPont Performance Polymers Zytel® FE270050 BK099 Nylon 66
(Unverified Data**) 30% Glass/Mineral Reinforced Polyamide 66Information provided by DuPont Performance Polymers |
|||
Tensile Strength at Break | 160 MPa | 23200 psi | DAM; ISO 527-1/-2 |
DuPont Performance Polymers Minlon® EFE6053 BK413 Nylon 66
(Unverified Data**) 40% Mineral/Glass Reinforced Polyamide 66 Minlon EFE6053 BK413 is a 40% mineral/glass reinforced heat stabilized polyamide 66 resin for injection molding.Information provided by DuPont Performance P.. |
|||
Tensile Strength at Break | 160 MPa | 23200 psi | 5 mm/min; ISO 527 |
Eurostar Staramide BG6 PA6, 30% Glass Filled, Injection Molded BG6 is a 30% Glass Fiber Reinforced Polyamide 6 Injection Molding ResinInformation provided by Polymer Technology & Services, the North American exclusive supplier. |
|||
Tensile Strength at Break | 160 MPa | 23200 psi | Conditioned; ISO R 527 |
Addiplast Addinyl A2 V40 Nylon 66, 40% Glass Filled Glass fiber reinforced, high strengthInformation provided by Addiplast. |
|||
Tensile Strength at Break | 160 MPa @Temperature -40.0 °C |
23200 psi @Temperature -40.0 °F |
ASTM Test |
BASF Ultramid® 8231G HS 14% Glass Filled PA6 (Dry) Ultramid 8231G HS is a heat stabilized, 14% glass fiber reinforced nylon 6 injection molding compound. It is also available in non-heat stabilized (Ultramid 8231) and/or pigmented versions. The gla.. |
|||
Tensile Strength at Break | 160 MPa | 23200 psi | 5 [mm/min]; ISO 527-1/2 |
Akro-Plastic Akromid® B3 GF 25 (2471) PA 6 Dry, 25% Glass Filled AKROMID® B (Polyamide 6) is an engineering compound, characterized by high mechanical strength, stiffness and thermal resistance. Furthermore, this polyamide offers high toughness at low temperatur.. |