DuPont Performance Polymers Zytel® 70G43L NC010 Nylon 66  (Unverified Data**)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled
Manufacturer DuPont Performance Polymers
Trade Name Zytel®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® 70G43L NC010 Nylon 66  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
43% Glass Reinforced Polyamide 66Zytel 70G43L NC010 is a 43% glass fiber reinforced polyamide 66 resin for injection molding.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.29 g/cc
0.0466 lb/in³
1.49 g/cc
0.0538 lb/in³
DAM; ISO 1183
Water Absorption 4.7 %

@Thickness 2.00 mm
4.7 %

@Thickness 0.0787 in
DAM; Sim. to ISO 62
Moisture Absorption 1.50 %

@Thickness 2.00 mm
1.50 %

@Thickness 0.0787 in
DAM; Sim. to ISO 62
Water Absorption at Saturation 0.90 %
0.90 %
DAM; Immersion 24h; ASTM D570
Viscosity 56420 cP

@Shear Rate 5000 1/s,
Temperature 305 °C
56420 cP

@Shear Rate 5000 1/s,
Temperature 581 °F
ISO 11403-1 -2
69100 cP

@Shear Rate 5000 1/s,
Temperature 295 °C
69100 cP

@Shear Rate 5000 1/s,
Temperature 563 °F
ISO 11403-1 -2
86190 cP

@Shear Rate 5000 1/s,
Temperature 285 °C
86190 cP

@Shear Rate 5000 1/s,
Temperature 545 °F
ISO 11403-1 -2
164800 cP

@Shear Rate 500 1/s,
Temperature 305 °C
164800 cP

@Shear Rate 500 1/s,
Temperature 581 °F
ISO 11403-1 -2
204400 cP

@Shear Rate 500 1/s,
Temperature 295 °C
204400 cP

@Shear Rate 500 1/s,
Temperature 563 °F
ISO 11403-1 -2
257400 cP

@Shear Rate 500 1/s,
Temperature 285 °C
257400 cP

@Shear Rate 500 1/s,
Temperature 545 °F
ISO 11403-1 -2
Viscosity Test 130 cm³/g
130 cm³/g
DAM; ISO 307 1157 1628
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.010 cm/cm
0.010 in/in
DAM; ISO 294-4 2577
Mechanical Properties Metric English Comments
Hardness, Rockwell M 90
90
50%RH; ISO 2039-2
105
105
DAM; ISO 2039-2
Hardness, Rockwell R 118
118
50%RH; ISO 2039-2
125
125
DAM; ISO 2039-2
Tensile Strength at Break 160 MPa
23200 psi
50%RH; ISO 527-1/-2
225 MPa
32600 psi
DAM; ISO 527-1/-2
Tensile Stress 10.33 MPa

@Strain 0.190 %,
Temperature 150 °C
1498 psi

@Strain 0.190 %,
Temperature 302 °F
50%RH; ISO 11403-1 -2
16.73 MPa

@Strain 0.260 %,
Temperature 90.0 °C
2426 psi

@Strain 0.260 %,
Temperature 194 °F
50%RH; ISO 11403-1 -2
18.05 MPa

@Strain 0.310 %,
Temperature 150 °C
2618 psi

@Strain 0.310 %,
Temperature 302 °F
DAM; ISO 11403-1 -2
23.95 MPa

@Strain 0.290 %,
Temperature 40.0 °C
3474 psi

@Strain 0.290 %,
Temperature 104 °F
50%RH; ISO 11403-1 -2
25.74 MPa

@Strain 0.470 %,
Temperature 180 °C
3733 psi

@Strain 0.470 %,
Temperature 356 °F
DAM; ISO 11403-1 -2
31.39 MPa

@Strain 0.710 %,
Temperature 150 °C
4553 psi

@Strain 0.710 %,
Temperature 302 °F
50%RH; ISO 11403-1 -2
41.26 MPa

@Strain 0.610 %,
Temperature 90.0 °C
5984 psi

@Strain 0.610 %,
Temperature 194 °F
DAM; ISO 11403-1 -2
45.36 MPa

@Strain 1.07 %,
Temperature 180 °C
6579 psi

@Strain 1.07 %,
Temperature 356 °F
DAM; ISO 11403-1 -2
46.1 MPa

@Strain 0.360 %,
Temperature 0.000 °C
6690 psi

@Strain 0.360 %,
Temperature 32.0 °F
50%RH; ISO 11403-1 -2
47.64 MPa

@Strain 1.06 %,
Temperature 150 °C
6910 psi

@Strain 1.06 %,
Temperature 302 °F
DAM; ISO 11403-1 -2
48.52 MPa

@Strain 1.43 %,
Temperature 150 °C
7037 psi

@Strain 1.43 %,
Temperature 302 °F
50%RH; ISO 11403-1 -2
49.92 MPa

@Strain 0.930 %,
Temperature 90.0 °C
7240 psi

@Strain 0.930 %,
Temperature 194 °F
50%RH; ISO 11403-1 -2
51.87 MPa

@Strain 0.610 %,
Temperature 23.0 °C
7523 psi

@Strain 0.610 %,
Temperature 73.4 °F
50%RH; ISO 11403-1 -2
57.13 MPa

@Strain 1.69 %,
Temperature 180 °C
8286 psi

@Strain 1.69 %,
Temperature 356 °F
DAM; ISO 11403-1 -2
59.91 MPa

@Strain 2.20 %,
Temperature 150 °C
8689 psi

@Strain 2.20 %,
Temperature 302 °F
50%RH; ISO 11403-1 -2
60.83 MPa

@Strain 0.570 %,
Temperature 40.0 °C
8823 psi

@Strain 0.570 %,
Temperature 104 °F
DAM; ISO 11403-1 -2
61.87 MPa

@Strain 0.880 %,
Temperature 40.0 °C
8974 psi

@Strain 0.880 %,
Temperature 104 °F
50%RH; ISO 11403-1 -2
64.48 MPa

@Strain 0.400 %,
Temperature -40.0 °C
9352 psi

@Strain 0.400 %,
Temperature -40.0 °F
50%RH; ISO 11403-1 -2
64.59 MPa

@Strain 2.30 %,
Temperature 180 °C
9368 psi

@Strain 2.30 %,
Temperature 356 °F
DAM; ISO 11403-1 -2
64.59 MPa

@Strain 1.82 %,
Temperature 150 °C
9368 psi

@Strain 1.82 %,
Temperature 302 °F
DAM; ISO 11403-1 -2
68.6 MPa

@Strain 1.56 %,
Temperature 90.0 °C
9950 psi

@Strain 1.56 %,
Temperature 194 °F
50%RH; ISO 11403-1 -2
69.27 MPa

@Strain 1.23 %,
Temperature 90.0 °C
10050 psi

@Strain 1.23 %,
Temperature 194 °F
DAM; ISO 11403-1 -2
77.02 MPa

@Strain 2.67 %,
Temperature 150 °C
11170 psi

@Strain 2.67 %,
Temperature 302 °F
DAM; ISO 11403-1 -2
78.19 MPa

@Strain 5.31 %,
Temperature 150 °C
11340 psi

@Strain 5.31 %,
Temperature 302 °F
50%RH; ISO 11403-1 -2
81.6 MPa

@Strain 1.11 %,
Temperature 23.0 °C
11800 psi

@Strain 1.11 %,
Temperature 73.4 °F
50%RH; ISO 11403-1 -2
82.52 MPa

@Strain 2.24 %,
Temperature 90.0 °C
11970 psi

@Strain 2.24 %,
Temperature 194 °F
50%RH; ISO 11403-1 -2
87.13 MPa

@Strain 1.49 %,
Temperature 40.0 °C
12640 psi

@Strain 1.49 %,
Temperature 104 °F
50%RH; ISO 11403-1 -2
87.46 MPa

@Strain 0.700 %,
Temperature 23.0 °C
12690 psi

@Strain 0.700 %,
Temperature 73.4 °F
DAM; ISO 11403-1 -2
90.23 MPa

@Strain 1.92 %,
Temperature 90.0 °C
13090 psi

@Strain 1.92 %,
Temperature 194 °F
DAM; ISO 11403-1 -2
94.64 MPa

@Strain 5.84 %,
Temperature 150 °C
13730 psi

@Strain 5.84 %,
Temperature 302 °F
DAM; ISO 11403-1 -2
97.13 MPa

@Strain 1.01 %,
Temperature 40.0 °C
14090 psi

@Strain 1.01 %,
Temperature 104 °F
DAM; ISO 11403-1 -2
103.93 MPa

@Strain 0.930 %,
Temperature 0.000 °C
15074 psi

@Strain 0.930 %,
Temperature 32.0 °F
50%RH; ISO 11403-1 -2
104.43 MPa

@Strain 1.62 %,
Temperature 23.0 °C
15146 psi

@Strain 1.62 %,
Temperature 73.4 °F
50%RH; ISO 11403-1 -2
105.23 MPa

@Strain 2.08 %,
Temperature 40.0 °C
15262 psi

@Strain 2.08 %,
Temperature 104 °F
50%RH; ISO 11403-1 -2
106.17 MPa

@Strain 2.66 %,
Temperature 90.0 °C
15399 psi

@Strain 2.66 %,
Temperature 194 °F
DAM; ISO 11403-1 -2
123.84 MPa

@Strain 2.19 %,
Temperature 23.0 °C
17962 psi

@Strain 2.19 %,
Temperature 73.4 °F
50%RH; ISO 11403-1 -2
124 MPa

@Strain 0.910 %,
Temperature 0.000 °C
18000 psi

@Strain 0.910 %,
Temperature 32.0 °F
DAM; ISO 11403-1 -2
124.08 MPa

@Strain 1.48 %,
Temperature 40.0 °C
17996 psi

@Strain 1.48 %,
Temperature 104 °F
DAM; ISO 11403-1 -2
130.71 MPa

@Strain 1.12 %,
Temperature 23.0 °C
18958 psi

@Strain 1.12 %,
Temperature 73.4 °F
DAM; ISO 11403-1 -2
132.75 MPa

@Strain 1.01 %,
Temperature -20.0 °C
19254 psi

@Strain 1.01 %,
Temperature -4.00 °F
50%RH; ISO 11403-1 -2
134.98 MPa

@Strain 1.36 %,
Temperature 0.000 °C
19577 psi

@Strain 1.36 %,
Temperature 32.0 °F
50%RH; ISO 11403-1 -2
145.96 MPa

@Strain 2.01 %,
Temperature 40.0 °C
21170 psi

@Strain 2.01 %,
Temperature 104 °F
DAM; ISO 11403-1 -2
146 MPa

@Strain 1.06 %,
Temperature -20.0 °C
21200 psi

@Strain 1.06 %,
Temperature -4.00 °F
DAM; ISO 11403-1 -2
148.08 MPa

@Strain 1.00 %,
Temperature -40.0 °C
21477 psi

@Strain 1.00 %,
Temperature -40.0 °F
50%RH; ISO 11403-1 -2
161.41 MPa

@Strain 1.86 %,
Temperature 0.000 °C
23411 psi

@Strain 1.86 %,
Temperature 32.0 °F
50%RH; ISO 11403-1 -2
161.78 MPa

@Strain 1.51 %,
Temperature 23.0 °C
23464 psi

@Strain 1.51 %,
Temperature 73.4 °F
DAM; ISO 11403-1 -2
168.1 MPa

@Strain 1.39 %,
Temperature -20.0 °C
24380 psi

@Strain 1.39 %,
Temperature -4.00 °F
50%RH; ISO 11403-1 -2
Copyright © lookpolymers.com All Rights Reserved