Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 15.0 MPa | 2180 psi | ASTM D638 |
SABIC Innovative Plastics LNP FARADEX MS003 PP LNP* FARADEX* MS003 is a compound based on Polypropylene resin containing 15% Stainless Steel. Added features of this material include: Electrically Conductive, EMI/RFI Shielding. |
|||
Tensile Strength at Break | 15.0 MPa | 2180 psi | 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible 90031 Polyvinyl Chloride, Flexible (PVC, Flexible) Automotive OEM approval(s).Information provided by PolyOne |
|||
Tensile Strength at Break | 15.0 MPa | 2180 psi | 50 mm/min test speed; ASTM D 638 |
NOVA Chemicals Sclair® IG464-C Compression Molded HDPE Resin IG464-C complies with the U.S. FDA specifications for olefin polymers and may thus be used in the United States as an article or component of an article intended for use in contact with food. IG464.. |
|||
Tensile Strength at Break | 15.0 MPa | 2180 psi | |
LATI Latene® 7H2W-V0 PP Homopolymer, Heat Stabilized, Flame Retardant Polypropylene homopolymer (PPh) based compound. Heat stabilized. Metal stabilized. UL94 V-0 classified, halogens-based flame retardants and red phosphorous free. Low smoke density and low toxicity i.. |
|||
Tensile Strength at Break | 15.0 MPa | 2180 psi | after 7days @80°C; UL 1581 |
SABIC Innovative Plastics NORYL WCD933 PPE-TPE Flexible and non-halogenated flame retardant extrusion grade intended for evaluation in applications such as insulation of HD 21.14 flexible cables. Flame retardant performance capable of meeting EN.. |
|||
Tensile Strength at Break | 15.0 MPa | 2180 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL WCP921 PPE-TPE Flexible Noryl* injection molding grade. Low specific gravity with good non-halogenated flame retardant performance. Developed for evaluation in overmolding applications such as plugs, strain relief.. |
|||
Tensile Strength at Break | 15.0 MPa | 2180 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL WCP921 PPE-TPE (Asia Pacific) Flexible Noryl* injection molding grade. Low specific gravity with good non-halogenated flame retardant performance. Developed for evaluation in overmolding applications such as plugs, strain relief.. |
|||
Tensile Strength at Break | 15.0 MPa | 2180 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL WCP921 PPE-TPE (Europe-Africa-Middle East) Flexible Noryl* injection molding grade. Low specific gravity with good non-halogenated flame retardant performance. Developed for evaluation in overmolding applications such as plugs, strain relief.. |
|||
Tensile Strength at Break | 15.0 MPa | 2180 psi | ISO 527 |
SABIC Innovative Plastics LNP STAT-KON MD000 PP (Asia Pacific) LNP STAT-KON* MD000 is a compound based on Polypropylene resin containing Carbon Powder. Added features of this material include: Electrically Conductive. |
|||
Tensile Strength at Break | 15.0 MPa | 2180 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP AH0230A ABS LNP THERMOCOMP* AH0230A is a compound based on ABS resin. Added feature of this material is: High Specific Gravity. |
|||
Tensile Strength at Break | 15.0 MPa | 2180 psi | ISO R 527 |
Stir SpA PVGUM 11 ATC (PVC) Application: Tread with Nitrile rubberInformation provided by STIR SpA |
|||
Tensile Strength at Break | 15.0 MPa | 2180 psi | ISO R 527 |
Fainplast Compounds FAINGUM 6510 Flexible PVC, Injection Molding for Footwear Soles with rubber |
|||
Tensile Strength at Break | >= 15.0 MPa | >= 2180 psi | ISO R 527 |
Fainplast Compounds FK 91 Flexible PVC, Insulation Lead Free Power cables |
|||
Tensile Strength at Break | >= 15.0 MPa | >= 2180 psi | ISO R 527 |
Fainplast Compounds GA 88 Flexible PVC, Flame Retardant Sheathing Operating temperature 105°C |
|||
Tensile Strength at Break | >= 15.0 MPa | >= 2180 psi | ISO R 527 |
Fainplast Compounds GA 90/R Flexible PVC, Flame Retardant Sheathing Hydrocarbon resistant |
|||
Tensile Strength at Break | 15.0 MPa | 2180 psi | ISO R 527 |
Fainplast Compounds GS 7410 Flexible PVC, Injection Molding for Footwear Sandals |
|||
Tensile Strength at Break | 15.0 MPa | 2180 psi | ISO R 527 |
Fainplast Compounds GS 7716 Flexible PVC, Injection Molding for Footwear Soles for mild climates |
|||
Tensile Strength at Break | >= 15.0 MPa | >= 2180 psi | ISO R 527 |
Fainplast Compounds HG 84 Flexible PVC, Sheathing for High Temperatures Operating temperature 90°C |
|||
Tensile Strength at Break | >= 15.0 MPa | >= 2180 psi | ISO R 527 |
Fainplast Compounds FR 86/2 Flexible PVC, Insulation Power cables |
|||
Tensile Strength at Break | 15.0 MPa | 2180 psi | ISO R 527 |
Fainplast Compounds MPH 73/T Medical Flexible PVC, Extrusion Technical tubes no DOP |
|||
Tensile Strength at Break | 15.0 MPa | 2180 psi | ISO R 527 |
Fainplast Compounds PK 0111 Flexible PVC, Lead Free Gas pipe according to DIN 4815 |
|||
Tensile Strength at Break | 15.0 MPa | 2180 psi | ISO R 527 |
Fainplast Compounds PK 88/2-UV Flexible PVC, Lead Free Outdoor profiles anti-UV |
|||
Tensile Strength at Break | 15.0 MPa | 2180 psi | ASTM D638 |
Aclo Accutech Polypropylene Copolymer CP0436W10L Wollastonite Reinforced |
|||
Tensile Strength at Break | 15.0 MPa | 2180 psi | ASTM D638 |
Aclo Accutech Polypropylene Copolymer CP0437T30L1 Talc Reinforced |
|||
Tensile Strength at Break | 15.0 MPa | 2180 psi | Conditioned; ISO R 527 |
Addiplast Addilene PMD 50218 Flame Retardant Polypropylene Flame retardant, unreinforced, with halogensInformation provided by Addiplast. |
|||
Tensile Strength at Break | 15.0 MPa | 2180 psi | ASTM D257 |
3M BBI-A Shrinkable Tubing for Bus Bar 3M Heat Shrinkable Tubing for Bus Bar BBI-A Series is designed for insulating rectangular, square and round bus bar rated from 5 kV through 35 kV. It will also cover and insulate inline bolted conne.. |
|||
Tensile Strength at Break | 15.0 MPa | 2180 psi | ISO R 527 |
Fainplast Compounds PH 7020 Flexible PVC, Transparent Extrusion Transparent garden hoses |