NOVA Chemicals Sclair® IG464-C Compression Molded HDPE Resin

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Injection Molded
Manufacturer NOVA Chemicals
Trade Name Sclair®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF NOVA Chemicals Sclair® IG464-C Compression Molded HDPE Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
IG464-C complies with the U.S. FDA specifications for olefin polymers and may thus be used in the United States as an article or component of an article intended for use in contact with food. IG464-C is subject to the specific limitation that it may contact food only at temperatures of 212°F and below.NOVA Chemicals' polyethylene resins are chemically and biologically inert.Features: Superior stiffness allows for part thinwalling and enhanced stacking strength, Low viscosity for exceptional processability yielding shorter cycle times and energy savings, Exceptional physical properties provide impact resistance for demanding applications, Low warpage for improved part quality and reliabilityAdditives: AntioxidantApplications: Crates, Pallets, Totes, Pails
Physical Properties Metric English Comments
Density 0.964 g/cc
0.0348 lb/in³
ASTM D 792
Melt Flow 10 g/10 min

@Load 2.16 kg,
Temperature 190 °C
10 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Hardness, Shore D 68
68
ASTM D 2240
Tensile Strength at Break 15.0 MPa
2180 psi
50 mm/min test speed; ASTM D 638
Tensile Strength, Yield 33.0 MPa
4790 psi
50 mm/min test speed; ASTM D 638
Elongation at Break 100 %
100 %
50 mm/min test speed; ASTM D 638
Elongation at Yield 7.0 %
7.0 %
50 mm/min test speed; ASTM D 638
Flexural Modulus, 1% Secant 1700 MPa
247000 psi
ASTM D 790
Thermal Properties Metric English Comments
Vicat Softening Point 131 °C
268 °F
ASTM D 1525