Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Ball Indentation Hardness | 50.0 MPa | 7250 psi | ISO2039.1 DIN.53456 |
Omnia Plastica PE 500 - Polyethylene 500 Polyethylene with a molecular weight of ± 500,000. PE 500 is more rigid than the high molecular weight polyethylene and it is therefore more suitable for mechanical applications. The friction coeff.. |
|||
Ball Indentation Hardness | 50.0 - 160 MPa | 7250 - 23200 psi | Average value: 138 MPa Grade Count:13 |
Overview of materials for Polybutylene Terephthalate (PBT), Unreinforced, Molded This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Unreinforced, Molded". Each property range of values reported is minim.. |
|||
Ball Indentation Hardness | 50.0 MPa | 7250 psi | ISO 2039-1 |
Lanxess Durethan® B 31 FCS 000000 Nylon 6, Film Grade PA 6, non-reinforced, extrusion, low viscosity, slip agentInformation provided by LANXESS. |
|||
Ball Indentation Hardness | 50.0 MPa | 7250 psi | Conditioned; ISO 2039-1 |
Lanxess Durethan® B 40 SK 000000 Nylon 6 PA 6, non-reinforced, injection molding |
|||
Ball Indentation Hardness | 50.0 MPa | 7250 psi | Hc 30; ISO 2039; partially |
Schwartz Technical Plastics LAMIGAMID® 100 Polyamide 6, Extruded, Conditioned Application: machine parts under 80 mm diameter, hammer-heads, cup-shaped bearing shellsInformation provided by Schwartz Technical Plastics GmbH |
|||
Ball Indentation Hardness | 50.0 MPa | 7250 psi | 358 N/30s; ISO 2039 |
Borealis Daplen™ EE188AI Polypropylene TPO Compound Daplen™ EE188AI is a 15% mineral filled polypropylene compound intended for injection molding. This material has an excellent balance between impact strength and stiffness and is easy to process. .. |
|||
Ball Indentation Hardness | 50.0 MPa | 7250 psi | 358 N/30s; ISO 2039 |
Borealis Daplen™ EE189AI Polypropylene TPO Compound Daplen™ EE189AI is a 15% mineral filled polypropylene compound intended for injection molding. This material has an excellent balance between impact strength and stiffness and is easy to process. .. |
|||
Ball Indentation Hardness | 50.0 MPa | 7250 psi | dry; ISO 2039-1 |
EMS-Grivory Grivory® 2S 25 W 20 HL X black 9992 PA610 Product Description: Grilamid 2S 25 W 20 HL X black 9992 is a semi-flexible high viscosity heat stabilized, impact modified and plasticized Polyamide 610, especially suitable for extrusion applicati.. |
|||
Ball Indentation Hardness | 50.0 MPa | 7250 psi | dry; ISO 2039-1 |
EMS-Grivory Grivory® 2S 25 W 20 HL X nat PA610 Product Description: Grilamid 2S 25 W 20 HL X natural is a semi-flexible high viscosity heat and UV stabilized, impact modified and plasticized Polyamide 610, espcailly suitable for extrusion applic.. |
|||
Ball Indentation Hardness | 50.0 MPa | 7250 psi | dry; ISO 2039-1 |
EMS-Grivory Grivory® 2S 25 W 20 X black 9992 PA610-I Product Description: GRILAMID 2S 25 W 20 X black 9992 is a semi-flexible high viscosity heat and impact modified polyamide 610, especially suitable for extrusion applications. This PA610 product is .. |
|||
Ball Indentation Hardness | 50.0 MPa | 7250 psi | dry; ISO 2039-1 |
EMS-Grivory Grivory® 2S 25 W 20 X nat PA610-I Product Description: GRILAMID 2S 25 W 20 X natural is a semi-flexible high viscosity heat and UV stabilized, impact modified polyamide 610, especially suitable for extrusion applications. This PA610.. |
|||
Ball Indentation Hardness | 50.0 MPa | 7250 psi | conditioned; ISO 2039-1 |
EMS-Grivory Grivory® XE 4129 black 9020 PA610 Product description: Grilamid XE 4129 black 9020 is a high viscosity Polyamide 610 especially suitable for extrusion applications. A characteristic of tubes made out of this material is the high res.. |
|||
Ball Indentation Hardness | 50.0 MPa | 7250 psi | ISO 2039-1 |
Azoty Tarnow™ TARFLEN SM-K25 PTFE Based on Tarflen SM1 reinforced with 25% coke for standard compression molding.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A. |
|||
Ball Indentation Hardness | 50.0 - 55.0 MPa | 7250 - 7980 psi | ISO 2032-N132 |
Adamas Adalon® 237 PTFE, 25% Glass Fiber Information provided by Adamas, HPM |
|||
Ball Indentation Hardness | 50.0 - 55.0 MPa | 7250 - 7980 psi | ISO 2032-N132 |
Adamas Adalon® 252 PTFE, 28% Glass Fiber Information provided by Adamas, HPM |
|||
Ball Indentation Hardness | 50.0 - 55.0 MPa | 7250 - 7980 psi | ISO 2032-N132 |
Adamas Adalon® 406 PTFE, 15% PEEK Information provided by Adamas, HPM |
|||
Ball Indentation Hardness | 50.0 - 55.0 MPa | 7250 - 7980 psi | ISO 2032 |
Adamas Adalon® 509 PTFE, 3% MoS2 Information provided by Adamas, HPM |
|||
Ball Indentation Hardness | 50.0 MPa | 7250 psi | value at 30 sec.; ISO 2039-1 |
CENTROPLAST CENTROLEN PE-HD Polyethylene high density This material is a low density, easily machined plastic that can be welded and has good chemical resistance. Applications include apparatus engineering, and machines in the foodstuff industry.Infor.. |
|||
Ball Indentation Hardness | 50.0 MPa | 7250 psi | ISO 2039 |
Orbilan ORBILAN® PE 500 HMW-PE Orbilan PE 500 plastic is used as cutting boards for the food industry and gastronomy, in refrigeration chambers as ram protection and for swing doors as well as at sports grounds for sheets or hand.. |
|||
Ball Indentation Hardness | 50.0 - 160 MPa | 7250 - 23200 psi | Average value: 132 MPa Grade Count:5 |
Overview of materials for Nylon 6, Extruded This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Extruded". Each property range of values reported is minimum and maximum values of appropriate .. |
|||
Ball Indentation Hardness | 50.0 - 190 MPa | 7250 - 27600 psi | Average value: 119 MPa Grade Count:32 |
Overview of materials for Nylon 6, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Unreinforced". Each property range of values reported is minimum and maximum values of appropri.. |
|||
Ball Indentation Hardness | 50.0 - 60.0 MPa | 7250 - 8700 psi | ISO 2032-N132 |
Adamas Adalon® 266 PTFE, Mineral/Glass Bubbles Filler Information provided by Adamas, HPM |
|||
Ball Indentation Hardness | 50.0 - 52.0 MPa | 7250 - 7540 psi | ISO 2032 |
Adamas Adalon® 600 PTFE, Boro Nitruro Information provided by Adamas, HPM |
|||
Ball Indentation Hardness | 50.0 MPa | 7250 psi | conditioned; ISO 2039-1 |
EMS-Grivory Grivory® BZ 1 PA6 Information provided by EMS Grivory |
|||
Ball Indentation Hardness | 50.0 MPa | 7250 psi | H385/30; ISO 2039 |
Borealis Daplen™ KSX65T20 Polypropylene Compound 20% Mineral Filled Daplen KSX65T20 is a 20% mineral filled grade intended for injection molding. Daplen KSX65T20 has been developed especially for the car industry, to be used in interior parts. Daplen KSX65T20 offe.. |