- Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded
- Chi Mei Polylac® PA-777E ABS - High Heat
Chi Mei Polylac® PA-777E ABS - High Heat
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded |
| Manufacturer | Chi Mei Corporation (ChiMei) |
| Trade Name | Polylac® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chi Mei Polylac® PA-777E ABS - High Heat.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultra High Heat
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0030 - 0.0070 cm/cm | 0.0030 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 5.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
5.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO-1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 115 | 115 | ASTM D785 |
| Ball Indentation Hardness | 99.0 MPa | 14400 psi | H358/30; ISO 2039-1 |
| Tensile Strength at Break | 37.0 MPa | 5370 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 44.0 MPa | 6380 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 13 % | 13 % | 50 mm/min; ISO 527 |
| Flexural Strength | 71.0 MPa | 10300 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.20 GPa | 319 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched | 1.11 J/cm @Thickness 6.35 mm |
2.08 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 1.22 J/cm @Thickness 3.17 mm |
2.29 ft-lb/in @Thickness 0.125 in |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 95.0 kJ/m² | 45.2 ft-lb/in² | ISO 180/1C |
| Charpy Impact Unnotched | NB | NB | ISO 179 |
| Charpy Impact, Notched | 1.10 J/cm² | 5.24 ft-lb/in² | ISO 179 |
| Impact | 9.00 | 9.00 | Impact Flexural Test Notched (KJ/m²) |
| NB | NB | Impact Flexural Test Unnotched (KJ/m²) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 106 °C | 223 °F | unannealed; ISO 75 |
| 118 °C | 244 °F | annealed; ISO 75 | |
| Vicat Softening Point | 119 °C @Load 5.00 kg |
246 °F @Load 11.0 lb |
50°C/hr; ISO 306 |
| 121 °C @Load 5.00 kg |
250 °F @Load 11.0 lb |
120°C/hr; ISO 306 | |
| 129 °C @Load 1.00 kg |
264 °F @Load 2.20 lb |
50°C/hr; ISO 306 | |
| 131 °C @Load 1.00 kg |
268 °F @Load 2.20 lb |
120°C/hr; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
UL 94 |
Users viewing this material also viewed the following:
- Osprey Metals 4140/MA Low Alloy Steel Master Alloy Powder (Grade 80% - 22)
- Humiseal 2A64 Urethane Conformal Coating
- Lanxess Durethan® BKV 40 H2.0 901510 Nylon 6, Glass Fiber Reinforced
- A. Schulman POLYPUR™ FPU 1109 Thermoplastic Polyurethane Compound
- A. Schulman FORMION™ FI 372 Ionomer
- Zig Sheng Industrial ZISAMIDE® HP3207 Nylon 6
- Diamond Polymers NPP 808 C3 TDS Polycarbonate Alloy
- ConocoPhillips ANDEROL® HTC PG 150 Chain & Way Fluid, Synthetic Polyglycol Food Grade Fluid ISO 150
- Plenco 50240 PET, Pellet, Injection Molded, Black (discontinued **)
- Solvay SIPOMER® PAM-100 Phosphate Esters of Polyethylene Glycol Monomethacrylate
Copyright © lookpolymers.com All Rights Reserved