PolyOne Geon™ Vinyl Rigid Molding M3500 Polyvinyl Chloride, Rigid (PVC, Rigid)

Category Polymer , Thermoplastic , Vinyl (PVC) , PVC, Rigid Grade
Manufacturer PolyOne Corporation
Trade Name Geon™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Geon™ Vinyl Rigid Molding M3500 Polyvinyl Chloride, Rigid (PVC, Rigid).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by PolyOne
Physical Properties Metric English Comments
Specific Gravity 1.36 g/cc
1.36 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0020 - 0.0050 cm/cm
0.0020 - 0.0050 in/in
ASTM D955
Spiral Flow 71.1 cm
28.0 in
Mechanical Properties Metric English Comments
Hardness, Shore D 80
80
ASTM D2240
Tensile Strength, Yield 46.2 MPa
6700 psi
Type I, 51 mm/min; ASTM D638
Elongation at Break 50 %
50 %
Type I, 51 mm/min; ASTM D638
Tensile Modulus 2.55 GPa
370 ksi
Type I, 51 mm/min; ASTM D638
Flexural Strength 71.0 MPa
10300 psi
ASTM D790
Flexural Modulus 2.48 GPa
360 ksi
ASTM D790
Izod Impact, Notched 0.530 J/cm

@Thickness 3.18 mm,
Temperature 0.000 °C
0.993 ft-lb/in

@Thickness 0.125 in,
Temperature 32.0 °F
Injection Molded; ASTM D256A
6.40 J/cm

@Thickness 3.18 mm,
Temperature 23.0 °C
12.0 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
Injection Molded; ASTM D256A
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 72.8 °C

@Thickness 6.35 mm
163 °F

@Thickness 0.250 in
Unannealed; ASTM D648
77.2 °C

@Thickness 6.35 mm
171 °F

@Thickness 0.250 in
Annealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 71.1 °C

@Thickness 6.35 mm
160 °F

@Thickness 0.250 in
Unannealed; ASTM D648
75.0 °C

@Thickness 6.35 mm
167 °F

@Thickness 0.250 in
Annealed; ASTM D648
UL RTI, Electrical 85.0 °C
185 °F
UL 746
UL RTI, Mechanical with Impact 85.0 °C
185 °F
UL 746
UL RTI, Mechanical without Impact 85.0 °C
185 °F
UL 746
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
ALL; UL 94
5VA

@Thickness 1.60 mm
5VA

@Thickness 0.0630 in
ALL; UL 94
Processing Properties Metric English Comments
Melt Temperature 199 - 210 °C
390 - 410 °F
Descriptive Properties Value Comments
Appearance Opaque
Features General Purpose
High Impact Resistance
Medium Flow
Forms Pellets
Generic Material PVC, Rigid
Generic Name Polyvinyl Chloride, Rigid (PVC, Rigid)
Processing Method Injection Molding
Regional Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Uses Appliances
Business Equipment
Construction Applications
Electrical/Electronic Applications
General Purpose
Telecommunications