Polymer Property : Flexural Strength = 59.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	59.0 MPa	8560 psi
Pyrotek F-51 Dense Machinable Board F-51 is a high temperature resin base, supplemented with fiberglass and graphite to provide extra strength and lubricity. F-51 is abrasion resistant and suitable for hot glass handling applications..
Flexural Strength	59.0 MPa	8560 psi	ISO 178
NOVA Chemicals DYLARK® 378 Impact Grade Engineering Resin Features:High heat resistance Good chemical resistance High impact strength Excellent flow characteristicsApplications:Automotive interior trim applications Automotive consoles Structural HousingsIn..
Flexural Strength	59.0 MPa	8560 psi	at 5% strain; ASTM D790
Shell Carilon® D26VM100 Polyketone, High-Flow Injection Molding Grade (discontinued **) Shell announced in Feb. 2000 that the Carilon product line is being discontinued. CARILON Polymer D26VM100 is a high-flow injection molding grade with mechanical properties which classify it as an ..
Flexural Strength	59.0 MPa	8560 psi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP ABL12 ABS LNP* Lubricomp* ABL12 is a compound based on Acrylonitrile Butadiene Styrene resin containing 10% Glass Bead and 5% PTFE. Added features of this material include: Internally Lubricated.
Flexural Strength	59.0 MPa	8560 psi	ASTM D790M
DSM Somos® 7110 Epoxy Photopolymer, Green Parts (discontinued **) DescriptionDSM Somos® 7110 Photopolymer is a humidity-tolerant, high heat-deflection-temperature, low-curl, high-speed liquid that produces rigid, highly accurate parts. It produces exceptional, u..
Flexural Strength	59.0 - 80.0 MPa	8560 - 11600 psi	ASTM D790
Huntsman RenShapeÂ® SL 7820 Stereolithography Plastic RenShapeÂ® SL 7820 stereolithography material is a white, low viscosity and stable liquid that produces strong black models and prototypes with good surface fi nish and detail, and ABS-like appear..
Flexural Strength	59.0 MPa	8560 psi	ASTM D790
Kolon KOCETALÂ® TF304 Wear Modified Acetal Resin PTFE powder added, improved wear property. Applications: High speed, high load and wear resistant products. Information provided by API-Kolon.
Flexural Strength	59.0 MPa	8560 psi	ISO 178
Lucite International DiakonÂ® Rapide CLG 356B Enhanced Molding Acrylic Polymer Specially designed to reduce injection molding cycle times and therefore provide production cost benefits.Information provided by Lucite International
Flexural Strength	59.0 MPa	8560 psi	ASTM D790
Kostat G148BK TAB Spacer Reels KOSTATs TAB Spacer Reels are ideal for shipment and storage of any components packaged in TAB spacer tapes. KOSTATSs TAB Spacer Reels, uniquely formulated and manufactured with the most advanced in..
Flexural Strength	59.0 MPa	8560 psi	ASTM D 790
MRC Polymers SATRANâ„¢ 805 ABS Terpolymer, Impact Modified Information provided by MRC Polymers Inc.
Flexural Strength	59.0 MPa	8560 psi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP KL004L Acetal Copoly (Asia Pacific) LNP* Lubricomp* KL004L is a compound based on Acetal Copolymer resin containing PTFE. Added features of this material include: Internally Lubricated, Low Extractible.
Flexural Strength	59.0 MPa	8560 psi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP KL004L Acetal Copolymer LNP* LUBRICOMP* KL004L is a compound based on Acetal Copolymer resin containing 20% PTFE. Added features of this material include: Wear Resistant, Low Extractible.
Flexural Strength	59.0 MPa	8560 psi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP MX06404 PP LNP LUBRICOMP* MX06404 is a compound based on Polypropylene resin containing 20% Glass Fiber and 15% PTFE. Added features of this material include: Heat Stabilized, Low Extractable, Wear Resistant...
Flexural Strength	59.0 MPa	8560 psi	ISO 178
SABIC Innovative Plastics LNP STAT-LOY A3000 ABS LNP STAT-LOY* A3000 is a compound based on ABS resin. Added feature of this material is: Antistatic.
Flexural Strength	59.0 MPa	8560 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP STAT-LOY AF3009 ABS (Asia Pacific) LNP* Stat-loy* AF3009 is a compound based on Acrylonitrile Butadiene Styrene resin containing Glass Fiber, Flame Retardant. Added features of this material include: Antistat, Flame Retardant.
Flexural Strength	59.0 MPa	8560 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP STAT-KON AD000 ABS LNP* STAT-KON* AD000 is a compound based on ABS containing Carbon. Added feature of this grade is: Electrically Conductive.
Flexural Strength	59.0 MPa	8560 psi	ASTM D 790
SABIC Innovative Plastics LNP Stat-loy W3000 PBT LNP STAT-LOY* W3000 is a compound based on Polybutylene Terephalate resin containing Anti-Static. Added features of this material include: Antistat.This data was supplied by SABIC-IP for the Americ..
Flexural Strength	59.0 MPa	8560 psi	ISO 178
SABIC Innovative Plastics LNP THERMOCOMP MF006AL PP LNP* THERMOCOMP* MF006AL is a compound based on Polypropylene resin containing 30% Glass Fiber. Characteristics of this grade are: Low Extractable.
Flexural Strength	59.0 MPa	8560 psi	1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics Noryl BN30 PPE+PS Blowmoldable. DTUL 180F. UL rated.This data was supplied by SABIC-IP for the Americas region.
Flexural Strength	59.0 MPa	8560 psi	ASTM D790
UBE UBESTA® 3030LUX Rigid Automotive Grade Nylon 12 Description: UBE UBESTA® Automotive grade Nylon 12Comments: UV resistance, heat resistanceInformation provided by UBE.
Flexural Strength	59.0 MPa	8560 psi	ISO 178
Polyplastics Duracon® TD-10 Acetal Co-polymer (POM), High impact, Flexible DURACON® is a crystalline thermoplastic acetal copolymer. The primary raw material trioxane, a trimer of formaldehyde.The thermoplastic adopts a copolymer structure in which polyoxymethylene (-C-O)..
Flexural Strength	59.0 MPa	8560 psi	ISO 178
Eurostar Starpylen HU 30BF4 PP, 30% Bamboo Fiber Filled, Injection Molding Starpylen HU30BF4 is a 30% Bamboo Fiber Reinforced Polypropylene Injection Molding Resin (also known as HU30BF4) (PRELIMINARY DATASHEET)Information provided by Eurostar.
Flexural Strength	59.0 MPa	8560 psi	2 mm/min; ISO 178
Chi Mei Polylac® PA-763 ABS - Flame Retardant F.R. High Heat Weather Resistant
Flexural Strength	59.0 MPa	8560 psi	JIS-K-6740
Denka VINYKON R5205 PVC, R grade for hard extrusion A PVC resin compound offering excellent physical properties and workability. A broad product lineup is available, including hard and soft grades, as well as those for extrusion and injection molding..
Flexural Strength	59.0 MPa	8560 psi	ASTM D790
A. Schulman ComAlloy Comtuf® 618 Nylon 6, Mineral Reinforced, Impact Modified Data provided by the manufacturer, ComAlloy International Company.15% Mineral Reinforced. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been i..
Flexural Strength	59.0 MPa	8560 psi
Poco Graphite TM Industrial Grade Graphite POCO’s specialty graphite materials are used in a wide range of highly technical and industrial applications. Each grade has characteristics and properties that allow the user to match the ideal gr..
Flexural Strength	59.0 MPa	8560 psi	0.1 in/min; ASTM D790
Ineos Nova 8048 High Performance Styrenic Enhanced Polystyrene (discontinued **) Improved toughness, Custom colorsApplications: Designed for injection molding applications requiring clarity and toughnessPerformance grades of polystyrene are engineered to have specific properties..
Flexural Strength	59.0 MPa	8560 psi	23°C, 50% RH; ASTM D790
Asahi Kasei Xyron® 100Z Modified Polyphenylene Ether Flame RetardantInformation provided by Asahi Kasei