Eurostar Starpylen HU 30BF4 PP, 30% Bamboo Fiber Filled, Injection Molding
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Wood Filled |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Starpylen |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Starpylen HU 30BF4 PP, 30% Bamboo Fiber Filled, Injection Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Starpylen HU30BF4 is a 30% Bamboo Fiber Reinforced Polypropylene Injection Molding Resin (also known as HU30BF4) (PRELIMINARY DATASHEET)Information provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.00 g/cc | 0.0361 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.010 cm/cm @Thickness 4.00 mm |
0.0050 - 0.010 in/in @Thickness 0.157 in |
E2P method |
| Melt Flow | 6.7 g/10 min @Load 2.16 kg, Temperature 230 °C |
6.7 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | ISO 527 |
| Elongation at Yield | 2.6 % | 2.6 % | ISO 527 |
| Flexural Strength | 59.0 MPa | 8560 psi | ISO 178 |
| Flexural Modulus | 3.00 GPa | 435 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 3.60 kJ/m² | 1.71 ft-lb/in² | 80x10x4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 185 - 195 °C | 365 - 383 °F | |
| Zone 2 | 185 - 195 °C | 365 - 383 °F | |
| Zone 3 | 185 - 195 °C | 365 - 383 °F | |
| Melt Temperature | 185 - 195 °C | 365 - 383 °F | |
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |
| Drying Temperature | 70.0 °C @Time 10800 sec |
158 °F @Time 3.00 hour |
Users viewing this material also viewed the following:
- Polykemi AB POLYfill PPH B8065 Polypropylene Homopolymer, Mineral Reinforced
- DSM Akulon® Ultraflow™ K-FHGM24 Nylon 6-30% Glass and Mineral Reinforced (European Grade) (Cond) (discontinue
- Taiwan PU Corporation CPU-69-A/B Mixing Ratio 100/28 Polyurethane Casting Elastomer
- SSAB Tunnplat Aluzink F26A Metal-coated Mild Steel
- A. Schulman POLYAXIS® LP624 Stabilized High Density Polyethylene
- Williams Advanced Alloys C102 Solder
- Cytec Thornel® T-650/42 12K Carbon Fiber, Polyacrylonitrile (PAN) Precursor
- Entec Hyrene® PSCRY 2.5 General Purpose Polystyrene
- ExxonMobil 1 Mobiltemp Series
- Azdel SuperLite® SL551000-100 PP Resin Matrix / 55% Glass Fiber (2.5 mm Molded Thickness)
Copyright © lookpolymers.com All Rights Reserved