SABIC Innovative Plastics LNP THERMOCOMP MF006AL PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP MF006AL PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* MF006AL is a compound based on Polypropylene resin containing 30% Glass Fiber. Characteristics of this grade are: Low Extractable.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ASTM D792 |
| 1.14 g/cc | 0.0412 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.0300 % | 0.0300 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0400 % | 0.0400 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 35.0 MPa | 5080 psi | Type I, 5 mm/min; ASTM D638 |
| 43.0 MPa | 6240 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 46.0 MPa | 6670 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 0.90 % | 0.90 % | Type I, 5 mm/min; ASTM D638 |
| 0.90 % | 0.90 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 0.90 % | 0.90 % | Type I, 5 mm/min; ASTM D638 |
| 0.90 % | 0.90 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 7.04 GPa | 1020 ksi | 1 mm/min; ISO 527 |
| 8.24 GPa | 1200 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 59.0 MPa | 8560 psi | ISO 178 |
| Flexural Yield Strength | 62.0 MPa | 8990 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 6.19 GPa | 898 ksi | 2 mm/min; ISO 178 |
| 6.29 GPa | 912 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.390 J/cm | 0.731 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 1.39 J/cm | 2.60 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 9.00 J @Temperature 23.0 °C |
6.64 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 33.5 µm/m-°C @Temperature -30.0 - 30.0 °C |
18.6 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 97.7 µm/m-°C @Temperature -30.0 - 30.0 °C |
54.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 134 °C | 273 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 141 °C @Thickness 3.20 mm |
286 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 106 °C @Thickness 3.20 mm |
223 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- NanoAmor 95%, OD/ID: 20-30/5-10 nm Aligned Multi-Walled Carbon Nanotubes
- SABIC Innovative Plastics Lexan® 143 PC (Europe-Africa-Middle East)
- Indium Corp. Indalloy 35 Bismuth Solder Alloy
- LG Chemical TR300 MABS, Flame Retardant, Transparency
- Schwartz Technical Plastics LAMIGAMID® 320 Cast Polyamide 6, Conditioned
- Solvay Specialty Polymers AvaSpire® AV-722 CF30 Polyaryletherketone (PAEK), 30% Carbon Fiber
- A. Schulman POLYFLAM™ RPP 1058 General Purpose Homopolymer Polypropylene (30% Fiberglass)
- Dow Corning SM 8715 EX
- Esstech X-166-0098 Poly Methyl Methacrylate/Methacrylic Acid
- Plansee MoCu15 Molybdenum-Copper
Copyright © lookpolymers.com All Rights Reserved