- HOME
- POLYMER SEARCH
- Polymer Property : Flexural Strength = 40.0 MPa
Polymer Property : Flexural Strength = 40.0 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Strength | 40.0 MPa | 5800 psi | |
| Plastcom SLOVALEN PH 91 N PP, basic type FeaturesCompounded homopolymer PP. General use in all industry branches. Packing material, garden flower-pots, toys, furniture industry, guides, dowels, clamps, office chairs, holders etc. Delivered.. |
|||
| Flexural Strength | <= 40.0 MPa | <= 5800 psi | ISO 178 |
| Polykemi AB POLYfill PP CMX8030 VT Polypropylene, Mineral Reinforced Information provided by Polykemi AB |
|||
| Flexural Strength | 40.0 MPa | 5800 psi | STN EN ISO 178 |
| Plastcom SLOVALEN PH 91 T 20 Polypropylene Homopolymer, 20% Micronized Talc FeaturesModified homopolymer PP for injection moulding with the content of 20% micronized, floated, chemically modified talc. General application in all industry branches - packing material, garden.. |
|||
| Flexural Strength | <= 40.0 MPa | <= 5800 psi | ISO 178 |
| Polykemi AB POLYfill PPC 05ENH Polypropylene Copolymer, Flame Retardant, Halogen Free Information provided by Polykemi AB |
|||
| Flexural Strength | 40.0 MPa | 5800 psi | ASTM D790 |
| Ineos Nova Zyntar® F7120 Developmental Flame Retardant Polystyrene
(discontinued **) Features: High flow for thin wall partsGood balance of physical propertiesUL94 V-0 @ 1.5 mm for black color Good aesthetics for injection molding Applications:Large television cabinetsConsumer elect.. |
|||
| Flexural Strength | 40.0 - 65.0 MPa | 5800 - 9430 psi | |
| MarkeTech MC-LD and MC-MD Ultra High Temperature Machinable Ceramics For very high temperatures or where thermal conductivity or thermal shock is important, these machinable alkaline/alkaline earth zirconium phosphate ceramics (NaZr2P3O12 or BaZr4P6O24) are recommend.. |
|||
| Flexural Strength | 40.0 MPa | 5800 psi | ASTM D790 |
| LG Chemical LUPOL HF-3202D High Flow Polypropylene, 20% Mineral Fillers, High Impact LUPOL resins, based on polyolefin with a wide range of characteristics, are a family of low cost engineering plastics.Applications: Automotive: Bumper cover, instrument panel, glove box, air cleaner.. |
|||
| Flexural Strength | 40.0 MPa | 5800 psi | ISO 178 |
| Solvay TECHNYL® C 216 PA6, Conditioned Description: Unreinforced polyamide PA6, standard nucleation for fast cycling, for injection molding.Available in: Asia PacificProduct Applications: This grade has a high fluidity and good mould rel.. |
|||
| Flexural Strength | 40.0 MPa | 5800 psi | ISO 178 |
| SABIC Innovative Plastics LNP STAT-KON MX01739C PP LNP* SAT-KON* MX01739C is a compound based on Polypropylene containing Proprietary Filler(s). Added features of this grade include: Electrically Conductive, Clean Compounding System. |
|||
| Flexural Strength | 40.0 MPa | 5800 psi | ISO 178 |
| Techmer ES Plaslube® NY-6/MS/M PA12 |
|||
| Flexural Strength | 40.0 MPa | 5800 psi | ISO Data |
| Styrolution Styrolux 684D SBC Styrolux 684D is a thermoplastic styrene-butadiene block copolymer which is suitable for injection molding, extrusion, and thermoforming. It offers an outstanding combination of crystal clarity and.. |
|||
| Flexural Strength | 40.0 MPa | 5800 psi | ISO 178 |
| SABIC Innovative Plastics LNP STAT-LOY K3000SZ Acetal Copoly (Asia Pacific) LNP* Stat-loy* K3000SZ is a compound based on Acetal Copolymer resin containing Anti-Static. Added features of this material include: Antistat. |
|||
| Flexural Strength | 40.0 MPa | 5800 psi | ISO 178 |
| SABIC Innovative Plastics LNP STAT-LOY K3000Z Acetal LNP* STAT-LOY* K3000Z is a compound based on unfilled Acetal resin. Added feature of this material is: Antistat. |
|||
| Flexural Strength | 40.0 MPa | 5800 psi | ASTM D790 |
| SABIC Innovative Plastics LNP STAT-LOY M3000 PP LNP STAT-LOY* M3000 is a compound based on unfilled Polypropylene resin. Added feature of this material is: Antistat. |
|||
| Flexural Strength | 40.0 MPa | 5800 psi | 5% strain; ISO 178 |
| Borealis MB250WG Polypropylene Compound, Mineral Filled MB250WG is a 20 % mineral filled polypropylene compound intended for injection molding. Applications: MB250WG has been developed especially for the white goods industry. Washing machine parts, and .. |
|||
| Flexural Strength | 40.0 MPa | 5800 psi | ASTM D790 |
| A. Schulman POLYFORT™ FXP 2779U UV Stabilized Copolymer Polypropylene DescriptionPolyfort® FXP 2779U is a 20% talc-filled, UV stabilized copolymer polypropylene.Information provided by A. Schulman. |
|||
| Flexural Strength | 40.0 MPa | 5800 psi | ASTM D790 |
| A. Schulman POLYFORT™ FPP 1245 CaCO3 Filled Copolymer Polypropylene DescriptionPolyfort® FPP 1245 is a 20% CAC03 filled copolymer polypropylene product. Information provided by A. Schulman. |
|||
| Flexural Strength | 40.0 MPa | 5800 psi | ASTM D790 |
| A. Schulman POLYFORT™ FPP 1245U CaCO3 Filled UV Stable Copolymer Polypropylene DescriptionPolyfort® FPP 1245U is a 20% CAC03 filled UV stable copolymer polypropylene product. Information provided by A. Schulman. |
|||
| Flexural Strength | 40.0 MPa | 5800 psi | ASTM D790 |
| A. Schulman POLYFORT™ FPP 1245 CaCO3 Filled Copolymer Polypropylene DescriptionPolyfort® FPP 1245 is a 20% CAC03 filled copolymer polypropylene product. Information provided by A. Schulman. |
|||
| Flexural Strength | 40.0 MPa | 5800 psi | ASTM D790 |
| A. Schulman POLYFORT™ FPP 1245U CaCO3 Filled UV Stable Copolymer Polypropylene DescriptionPolyfort® FPP 1245U is a 20% CAC03 filled UV stable copolymer polypropylene product. Information provided by A. Schulman. |
|||
| Flexural Strength | 40.0 MPa | 5800 psi | ASTM-D790 |
| Polyram RamShine PV102 ABS, General Purpose General purpose ABS for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
| Flexural Strength | 40.0 MPa | 5800 psi | cond; ISO 178 |
| DSM EcoPaXX® Q-X07207 PA410-I Impact Modified |
|||
| Flexural Strength | 40.0 MPa | 5800 psi | ASTM D790 |
| Entec Hypro™ PPH-T10 Homopolymer Polypropylene, 10% Talc Reinforced Information provided by Entec |
|||
| Flexural Strength | 40.0 MPa | 5800 psi | After conditioning at 23°C and 50% RH; ISO 178 |
| Arkema Group Orgalloy® LE 60 ES Polyamide Alloy Polyamide Alloy, Blow Molding of Technical PartsInformation provided by Arkema Group |
|||
| Flexural Strength | 40.0 MPa | 5800 psi | at max force; ISO 178 |
| BASF Ultramid® C3U10 PA6/66 FR (Conditioned) Description: Flame-retardant injection-molding grade; light colorable. Burning behavior optimized for glow-wire requirements of IEC 60335. Typical applications are switches, housings, plug connector.. |
|||
| Flexural Strength | 40.0 MPa | 5800 psi | ASTM D790 |
| Aclo Accuguard Polypropylene HPN469V2CSL Homopolymer Non-Halogenated Copper Stabilized |
|||
| Flexural Strength | 40.0 MPa | 5800 psi | ASTM D790 |
| Aclo Accutech Polypropylene HP0315V Homopolymer High Heat Approved to GMP.PP.013 |
|||
| Flexural Strength | 40.0 MPa | 5800 psi | ISO 178 |
| Azoty Tarnow™ TARNOFORM 300 CI4 POM Impact modified injection molding grade based on Tarnoform 300 reinforced with 20% MBS rubber yielding good cold impact strength and good strength of weld lines combined with good weatherability.Inf.. |
|||
| Flexural Strength | 40.0 MPa | 5800 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP LUBRICOMP CL002 PS (Europe-Africa-Middle East) LNP* LUBRICOMP* CL002 is a compound based on Polystyrene resin containing PTFE. Added features include: Internally Lubricated. |
|||
| Flexural Strength | 40.0 MPa | 5800 psi | 2 mm/min; ISO 178 |
| Sax Polymers SAXALEN PPH329B20 Polypropylene Homopolymer, 20% Glass Filled SAXALEN PPH329B20 is a 20% glass beads filled Polypropylene - Homopolymer intended for injection molding. Low shrinkage, low warpage gradeInformation provided by SAX Polymers |
|||
Copyright © lookpolymers.com All Rights Reserved