- Entec Hypro™ PPH-T10 Homopolymer Polypropylene, 10% Talc Reinforced
Entec Hypro™ PPH-T10 Homopolymer Polypropylene, 10% Talc Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 10% Talc Filler |
| Manufacturer | Entec Engineered Resins |
| Trade Name | Hypro™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Entec Hypro™ PPH-T10 Homopolymer Polypropylene, 10% Talc Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Entec
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.980 g/cc | 0.0354 lb/in³ | ASTM D792 |
| Melt Flow | 10.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
10.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | ASTM D638 |
| Elongation at Break | 20.0 % | 20.0 % | ASTM D638 |
| Elongation at Yield | 7.00 % | 7.00 % | ASTM D638 |
| Flexural Strength | 40.0 MPa | 5800 psi | ASTM D790 |
| Flexural Modulus | 1.862 GPa | 270.1 ksi | tangent; ASTM D790 |
| Izod Impact, Notched | 0.320 J/cm @Thickness 3.17 mm |
0.599 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 113 °C | 235 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPE A 8205 BLK
- SABIC Innovative Plastics ULTEM 1000P PEI
- Eagle Brass 260 Cartridge Brass, 3/4 Hard
- CoorsTek Nitrogen Bonded Silicon Carbide, SCNB
- Ecomass® 4703TU95 Tungsten Filled Polyurethane
- DuPont Teijin Films Mylar® RL42 Polyester Packaging Film, 75 Gauge
- 3M 25A29 Co-Extruded Polyethylene Protective Tapes
- Abatron MasterMold 12-3 Flexible Mold Making Compound
- BASF Elastollan 890 AN TPUR
Copyright © lookpolymers.com All Rights Reserved